Processing study of a high temperature adhesive

An adhesive-bonding process cycle study was performed for a polyimidesulphone. The high molecular weight, linear aromatic system possesses properties which make it attractive as a processable, low-cost material for elevated temperature applications. The results of a study to better understand the parameters that affect the adhesive properties of the polymer for titanium alloy adherends are presented. These include the tape preparation, the use of a primer and press and simulated autoclave processing conditions. The polymer was characterized using Fourier transform infrared spectroscopy, glass transition temperature determination, flow measurements, and weight loss measurements. The lap shear strength of the adhesive was used to evaluate the effects of the bonding process variations.     

Selective O-methylation of phenol with dimethyl carbonate over X-zeolites

The O-methylation of phenol with dimethyl carbonate proceeds selectively in the vapor phase over alkali ion exchanged X-zeolites. Thus, a 76% yield of anisole was obtained with a 93% selectivity over NaX at 553 K. The participation of basic sites in the O-methylation is suggested.     

One-step formation of ethyl methyl ketone from 1-butene and water on ultrastable Y-type zeolite catalyst

Proton exchanged ultrastable Y-type zeolite with silica/alumina = 40 showed a pronounced catalytic activity for the formation of ethyl methyl ketone directly from 1-butene and water. The formation rate of ethyl methyl ketone was much higher than those on MoO₃-based catalysts in the oxidation of 1-butene by oxygen. It was suggested that the basic site necessary for the formation of ethyl ketone directly from 1-butene and water would be the pentacoordinated Al.     

钛纳米改性聚合物防腐涂料的研究

为保护大庆油田三元复合液中油管,以钛纳米改性聚合物为主要原料,研制了钛纳米改性聚合物重防腐涂料.采用透射电子显微镜(TEM)研究了钛纳米改性聚合物平均粒径.采用正交试验法,确定最佳原料配比.采用扫描电子显微镜(SEM)研究了漆膜腐蚀.采用金相显微镜研究了钛纳米改性聚合物在漆膜中的分布.探讨了油管的腐蚀机理和钛纳米涂料的防护机理.实验结果表明:钛纳米含量为6%时,涂料具有最佳的防腐蚀效果,能很好的保护大庆油田三元复合液中的油管,并具有优异的抗化学药品介质的腐蚀性能.     

Effects of main factors on remedying northern landscaping water by hybrid ecological filter

Natural zeolite and coal cinder were layered as main packing medium of the ecological filter instead of traditional filling to remedy the static lake water in Northern China.The ecological filter was running in a combined upward and downward flow mode.Dynamic experiments were carried out to study the effects of retention time and ambient temperature on pollutants’ removal efficiency of the hybrid ecological filter.The function of plant was also studied by contrast test.It is showed that the removal efficiencies of NH4+-N and TP are increased when the retention time is changed from 1 h to 2 h and 4 h,but the removal efficiency of TN is decreased,the removal efficiency of NH4+-N is increased from 91.5% to 98% and that of TP is increased from 31.8% to 52.5%.When the temperature declines,the temporal removal efficiency of NH4+-N is reduced,but the removal efficiency of 24 h and 48 h is remained.The removal efficiency of TP after 24 h and 48 h is decreased when the temperature declines evidently.The retention time plays an important role in NH4+-N and TP removal,and the ambient temperature is significant for TP removal.The plant favors for TP and organic matter removal but has little effect on TN removal.     

频率响应法研究噻吩在CeY分子筛上的吸附行为

以NaY、液相Ce离子交换改性的Y型分子筛(L-CeY)为研究对象,运用N2吸附、XRD、NH3-TPD和Py-FTIR等实验方法表征两种Y型分子筛的物化性能。采用频率响应技术(FR)和智能重量分析仪(IGA)研究噻吩在两种分子筛上的吸附行为,并考察噻吩在稀土离子改性Y型分子筛上的不同吸附作用模式。结果表明,频率响应技术能够有效识别分子筛孔道内发生的不同传质过程。噻吩在NaY分子筛上的吸附行为较为简单,存在孔道吸附和π电子相互作用两种吸附过程;而在L-CeY分子筛上吸附行为较为复杂,同时存在孔道吸附和"S-M"吸附等多种吸附过程,另外,在高温条件下,还存在复杂的催化反应过程。     

High-temperature oxidation of pure titanium in CO2 and Ar-10%CO2 atmospheres

The oxidation behavior of pure titanium has been investigated in the temperature range of 1000 K to 1300 K in CO₂ or Ar-10%CO₂. Optical microscopy, electron probe microanalyses, and X-ray measurements on the oxide scales formed during oxidation indicate that their structures are nearly independent of temperature and the corrosion atmosphere. The scales consisted of two layers, an external one and an internal one, having a rutile (TiO₂) structure. The parabolic rate law was confirmed for growth of the external scale and the permeation depth of oxygen in titanium with apparent activation energies of 266 and 226 kJ/mol, respectively. The rate-determining diffusion species in the oxidation processes are discussed.     

用双层辉光等离子法在钛表面制备的Ti-Pd合金层性能研究

采用双层辉光等离子冶金技术在纯钛表面制备了Ti—Pd合金层。其深度大约为90μm，Pd含量呈梯度变化，并出现了TiPd3，TiPd2，Ti2Pd3，Ti3Pd5，TiPd，Ti4Pd等6种化合物相和Pd相。合金层在100℃的NaCl饱和溶液＋HCl溶液以及40℃的8．6％H2SO4溶液中的耐缝隙腐蚀性能优于Ti0．2Pd合金；在室温80％H2SO4的溶液中，腐蚀速率仅为0．682mm／a，是Ti0．2Pd合金的18．2％：在室温30％HCl的溶液中，表面Ti—Pd的腐蚀速率仅为0．004mm／a，是Ti0．2Pd合金的12．5％。     

Synthesis mechanism of titanium carbide nano-fiber during self-propagating high temperature synthesis

Titanium carbide nano-fiber was synthesized by self-propagating high temperature synthesis (SHS) method. The final products after the SHS reaction were titanium carbide containing excess carbon and metallic titanium, which were removed by additional leaching process. TEM observation revealed that the average diameter is about 20 nm. Neutron diffraction analysis was carried out to study non-stoichiometric number of the titanium carbide. The non-stoichiometric numbers of the titanium carbide were 0.89–0.94. The Rietveld refinement of each patterns converged to good agreement (÷2=0.49–1.34). The formation mechanism of the carbide is related to a liquid-solid reaction including the preferential diffusion process of carbon atom into liquid titanium. This article is based on a presentation made in the 2002 Korea-US symposium on the “Phase Transformations of Nano-Materials,” organized as a special program of the 2002 Annual Meeting of the Korean Institute of Metals and Materials, held at Yonsei University, Seoul, Korea on October 25–26, 2002.     

Comparison between Ni-Cr-40vol%TiC wear-resistant plasma sprayed coatings produced from self-propagating high-temperature synthesis and plasma densified powders

Plasma sprayed Ni-Cr-40vol%TiC coatings produced from powders obtained by self-propagating hightemperature synthesis (SHS) and plasma densification (PD) processes are characterized. Chemical composition, microstructure, and mechanical properties, such as microhardness and wear resistance, are evaluated and compared. SHS coatings exhibit good sliding wear performance. The exact stoichiometry of titanium carbide inclusions in the metallic matrix affects the dimension of the crystal lattice parameter and was investigated by examining the shift of x-ray diffraction (XRD) peaks of the TiC. A value of the combined carbon/titanium ratio of about 0.6 was calculated for both powders, thus excluding the influence of the stoichiometry of the carbide inclusions on the wear properties of the coatings.