Characterization of nanostructured Cr2Nx/Cu multilayers deposited by reactive DC magnetron sputtering

Nitride/metal nanostructured multilayers of Cr₂N_x/Cu were deposited by reactive DC magnetron sputtering with various bilayer periods (2.5-30 nm) and substrate temperatures (25-400 °C). All films had a total thickness of about 470 nm and the overall chemical composition of the chromium nitride layers was close to Cr₂N_0.8. The deposited films were characterized by Rutherford Backscattering (RBS), low-angle X-ray reflectivity (XRR), high-angle X-ray diffraction (XRD) and transmission electron microscopy (TEM). The hardness and elastic modulus were measured by nanoindentation. The films deposited at 25 °C had a well-defined multilayer structure and the chromium nitride layers were found to crystallize into N-deficient fcc CrN_0.4 with traces of hexagonal Cr₂N_0.8. The layers were strongly textured with fcc CrN_0.4[002] and Cu[002] oriented along the growth direction — the fcc CrN_0.4 and Cu grains growing with a cube-on-cube relationship. The measured hardness values were about 8 GPa, and showed no dependence on the bilayer period. Higher deposition temperatures caused the multilayer structure to degrade, and at 400 °C the films were better described as non-textured nanocomposites with the chromium nitride crystallized entirely into the equilibrium hexagonal Cr₂N_0.8 structure. Hardness values of the high-temperature films in the range of 4-8 GPa were measured. Multilayer films deposited at 25 °C were found to be thermally stable against post-deposition annealing at temperatures up to about 400 °C. Annealing at 500 °C caused severe structural changes — the fcc CrN_0.4 phase transformed into hexagonal Cr₂N_0.8 accompanied by degradation of the periodic multilayer structure. The hardness decreased from the originally 8 GPa to about 5 GPa upon annealing.     

天然核桃壳对废水中Cd~(2+)和Pb~(2+)的吸附热力学研究

采用批处理技术研究了天然核桃壳吸附废水中Cd2+和Pb2+的主要影响因素,如p H值、核桃壳用量和离子初始浓度等因素,并探讨了吸附等温线及吸附热力学。研究表明,天然核桃壳对Cd2+和Pb2+的最大吸附量分别为12.5mg/g和38.02mg/g。天然核桃壳吸附Cd2+的过程对Freundlich方程和Langmuir方程的拟合效果都较好;吸附Pb2+的过程则对Freundlich方程的拟合效果要好于Langmuir方程。热力学分析表明,天然核桃壳对Cd2+和Pb2+的吸附属自发吸热过程,且较易发生。     

Determination of lysozyme at the nanogram level in chicken egg white using Resonance Rayleigh-scattering method with Cd-doped ZnSe quantum dots as probe

A new method for the determination of lysozyme with high sensitivity based on Resonance Rayleigh scattering (RRS) by using Cd doped ZnSe quantum dots (QDs) as a probe was proposed in this experiment. Cd doped ZnSe QDs capped with glutathione were prepared in the water phase. Further, the RRS spectrum, transmission electron microscope, and absorption spectrum of the QDs-lysozyme system have been characterized. In addition, the effects of several factors on scattering intensities were investigated, including pH value of solution, amount of QDs, mixing sequence of each reagent and the coexisting substances. Moreover, the possible mechanism for the RRS enhancement of Cd doped ZnSe QDs-lysozyme system was preliminary discussed. The RRS method for the determination of lysozyme has good sensitivity with the detection limits 6.5 × 10⁻¹⁰ g mL⁻¹. The contents of lysozyme were determined with recoveries of 97.1-101.6% and relativity standard deviation of 2.5-3.1%, respectively. It proved that the method established in our study is very sensitive, rapid, convenient and tolerant for the determination of lysozyme in synthetically and chicken egg white.     

氢氧化钠改性粉煤灰制吸附材料研究

以粉煤灰为原料制取水处理吸附材料。研究氢氧化钠浓度、回流时间、液固比、热处理时间和热处理温度对Cd2＋吸收率的影响。结果表明：氢氧化钠处理能显著提高粉煤灰的吸收能力;与未处理的粉煤灰相比,吸收率可由40．1％提高到80％以上：通过实验和分析得出氢氧化钠改性粉煤灰的较佳工艺条件：氢氧化钠浓度为3mol／L,回流时间为10h,氢氧化钠溶液与粉煤灰的液固比为6,热处理时间6h,热处理温度为90℃。     

High conductivity and transparent ZnO:Al films prepared at low temperature by DC and MF magnetron sputtering

Aluminum-doped zinc oxide thin films have been deposited by DC and MF magnetron sputtering from a ceramic oxide target in argon atmosphere without direct heating of the substrates. The samples were prepared at different predetermined conditions of input power or discharge voltage and the influence upon electronic, optical, and microstructural properties has been investigated. The as-deposited layers show low resistivity, such as 9 × 10^− 4 Ω cm minimum for DC excitation and 1.2 × 10^− 3 Ω cm for MF mode, with growth rates up to 130 nm/min, and resulting substrate temperatures always below 200 °C. Low resistivity of the films is combined with high transmission, 85-90% in the visible wavelength range (400-800 nm). A strong (002) texture perpendicular to the substrate has been found, with lower strain for DC than for MF sputtering.     

Comparison of Bi3Fe5O12 film giant Faraday rotators grown on (111) and (001) Gd3Ga5O12 single crystals

Bismuth iron garnet (Bi₃Fe₅O₁₂, BIG) epitaxial thin films were grown on single crystal (Gd₃Ga₅O₁₂, GGG) (111) and (001) substrates by rf-magnetron sputtering technique. Processing parameters have been optimized to obtain high deposition rate (2.74 μm/h) and the surface rms roughness less than 10 nm. X-ray diffraction reveals films epitaxial quality: exclusive (111) or (001) orientation with narrow rocking curves and strong in-plane texture. Films possess low optical loss and magneto-optical Faraday rotation (FR) as high as 5 deg/μm at 677 nm wavelength. Comparative analysis of films grown on (111) and (001) substrates clearly shows significant superiority of BIG/GGG(001) film. For this film, the coercive field ∼100 Oe appears to be 2.5 times lower while the optical transmission to be 10% higher than that for BIG/GGG(111) film. Enhanced magneto-optical performance of BIG/GGG(001) films relies upon better accommodation of the film-to-substrate mismatch strain through the tetragonal BIG lattice distortions compared to the rhombohedral one in BIG/GGG(111) films.     

示波极谱法测定糖尿病人头发中的铜、铅、镉、锌、铬的含量

采用HNO3-HClO4消化、HCl溶解头发样品,应用单扫描示波极谱法测定了糖尿病人头发中的Cu、Pb、Cd、Zn、Cr的含量,并把结果与健康人的含量进行了对比分析.     

Local structural characterization of Zn:Cd:Se ternary semiconductors

We have studied the local atomic structure around Zn and Cd, in CdSe, ZnSe, and ordered and disordered Zn_0.5Cd_0.5Se thin films, grown by molecular beam epitaxy (MBE) and atomic layer epitaxy (ALE) using X-ray absorption spectroscopy (XAS). Zn K-shell X-ray absorption fine structure (XAFS) shows that the Zn–Se pair nearest neighbor distance is the same in both ordered and disordered ternary samples. This result shows that the ordered (or disordered growth) does not have a significant effect in the nearest neighbor Zn environment. However, results from K-shell Cd XAFS show that the Cd–Se pair nearest neighbor distance in the Zn_0.5Cd_0.5Se ordered film exhibits a contraction compared to the same pair distance in the disordered Zn_0.5Cd_0.5Se sample and the binary CdSe compound. This suggests that the shortest Zn–Se nearest neighbor distance regulates the Cd–Se nearest neighbor distance in the ternary compounds, when these are grown in an ordered, layer by layer, fashion.     

丝缎中重金属总量测定方法的研究

利用3种消解方法将丝缎中铜、镉、铅溶解出来，消解液用火焰原子吸收分光光度法测定微量的铜、镉和铅。通过加标回收率实验，确定方法三准确度较高，其测定的加标平均回收率为98.3％～103．5％。