Bulk and Interphase Effects in Aged Structural Joints

Although structural adhesives are becoming widespread in numerous applications, one important limitation at present is the long term behaviour of bonded assemblies under conditions of high humidity, especially at elevated temperatures. This study presents a comparison between bulk properties of a structural epoxy resin and its behaviour in a torsional joint consisting of a hollowed-out cylinder bonded to a plate—both substrates being in stainless steel. Exposure to ca. 100% relative humidity at 70°C leads to modification of the bulk properties of the polymer, notably reduction of its elastic modulus. Although this may explain some differences in behaviour of the torsional joint, premature failure is attributed to weaknesses in the interphase zone.

Auger Electron Spectroscopy (AES) has been employed to investigate both unbonded steel surfaces and fracture zones. Although prolonged exposure to water leads to a more extensive degree of (apparently) adhesive failure at the interface polymer/metal, AES has shown the presence of non-negligible quantities of carbon, attributed to residual polymer. Failure would seem to occur, at least partly, in a weak interphase of the polymer, near, but not at, the interface.

Various possible causes are evoked. For dry failure, residual polymer may be due to the topography of the metal surface and/or local modification of the adhesive during cure. In the case of aged joints, in addition there are potential effects due to swelling and differential stresses, secondary bond failure and molecular chain scission within the polymer, all provoked by the presence of water.     

Effects of apitong (Dipterocarpus spp.) extractives on bond strength development and curing rate of adhesives

Emulsion polymer isocyanate ( ), polyvinyl acetate ( ) and resorcinol-formaldehyde ( ) adhesives were used to produce single lap shear specimens using resinous and non-resinous apitong (Dipterocarpus spp.) timbers. Tests showed that joints made with highly resinous apitong were about 40% weaker than similar joints made with non-resinous apitong. The resinous apitong was treated with different solvents to yield five different extractives which were characterized by infra-red analysis. Apitong extractives were then added to and adhesives and joints made with buna (Fagus crenata), a timber known to be low in extractives and easy to bond. Joints prepared using extractive-containing adhesives were generally weaker than those made with the unmodified adhesives. RF adhesives containing extractives cured more slowly than unmodified . It is thought that the acidic nature of the extractives changes the pH of the system sufficiently to affect the curing mechanism     

多羟甲基酚多丙烯酸酯的合成及其耐温性能研究

本文合成了新型耐温活性预聚体多羟甲基酚多丙烯酸酯,并考察了pH值,丙烯酸量,反应时间、反应温度、催化剂用量等因素对反应产率的影响。测试了固化物的TCA和DTA及力学性能,并用红外光谱确认主产物。     

A Thermo-Mechanical Study of Some Epoxy Adhesives Subjected to Combined Dynamic and Static Stresses

The object of the present study was to investigate the effect of superimposed dynamic and static stresses on mechanical and thermal properties of some epoxy adhesives. It was found that combinations of shear creep and torsional oscillations, applied simultaneously to adhesive joints at temperatures within the glassy range of the adhesive, led to strengthening of the joints in shear and to an increase in the glass transition temperature of the adhesive. Similar loading stresses applied at temperatures close to the T_g of the adhesive, led to opposite effects on the above mentioned properties of the joints. The width of the glassy-rubbery transition of the adhesives increased, in the whole range of temperatures used in this study and for all epoxy compositions, as a result of subjecting the joints to superimposed dynamic and static stresses. The broadening of the glass transition was interpreted as a result of the stiffening of polymer network during the combined stressing experiments. A linear relationship was found between the area of endothermal peaks in the first DSC scan of specimens subjected prior to test to superimposed dynamic and static stresses at temperatures below T_g, and the shear strength of the joints. In agreement with this observation and with literature data, a linear relationship was revealed also between the glass transition temperature of the resins (measured in the first DSC scan) and the shear strength of the joints. Based on experimental observations and on some literature information, it was suggested that the strengthening of the joint, as well as the changes in thermal properties of the adhesives, are mainly due to physical processes, such as short-range orientation of network chains and an increase in intermolecular interaction between highly polar sites of the network. The possibility that superimposed stressing led to changes in chemical crosslinking was discussed but it seems that no such reactions occurred.     

CJ91胶粘剂在螺旋振动光整机中的应用

螺旋振动光整机槽内壁的橡皮保护层由于老化及磨损等原因出现裂口甚至脱落现象，严重影响设备的使用寿命和闸把壳体的外观质量。通过分析和试验筛选出螺旋振动光整机的理想胶粘荆——CJ91胶粘剂并介绍了粘接修补工艺。     

混炼硅橡胶的配合技术(八)

介绍了2种汽车部件（密封图、汽车挡风玻璃刮片）装配用混炼硅橡胶的配制，以及硫化过程中能与接触基材粘接的混炼硅橡胶（通过添加各种增粘剂如含乙烯烃碳酸酯基或巯基乙酸酯基化合物、烷氧基硅烷、含乙烯基硅官能基过氧化物为硫化剂）的配制。     

Dynamic buffering performance of the honeycomb paperboard filled with polyurethane

A new kind of composite buffering material was made by filling the voids of honeycomb paperboard with polyurethane. Drop tests were performed to evaluate the dynamic energy absorption capacity of the material. Based on the tests results, we analyzed the mechanical behaviors of the material under different conditions and obtained the inherent influencing laws of some factors on the material＇s dynamic buffering performance. It was shown that the dynamic buffering performance varied directly with impact velocity, and inversely with the void diameter, thickness and buffeting area of the composite material.     

泡沫塑料表面的磁控溅射镀膜技术研究

对硬质聚氨酯泡沫塑料进行适当的前处理(涂刮不饱和聚酯腻子和喷涂双组份聚氨酯清漆),再采用磁控溅射镀膜技术对其进行紫铜T2镀膜,能够有效地降低泡沫塑料的吸水率,提高尺寸稳定性.     

聚氨酯涂料的技术动向

叙述聚氨脂涂料的类型,各类聚氨脂涂料的特性、聚氨脂涂料的合成及目前聚氨脂涂料的技术进步动向。     

HClO对贻贝粘附单元DOPA氧化的理论研究

采用量子化学密度泛函理论(DFT)研究贻贝粘附单元DOPA(3,4-二羟基苯丙氨酸)的结构与性质,得分子的几何构型、原子电荷分布、反应活性及热力学等参数,表明:DOPA苯环易与HClO(次氯酸)发生亲电取代反应(1),生成3-氯4,5-二羟基苯丙氨酸,阻碍生成贻贝内超强粘附单元DOPA二联体,降低粘附蛋白间粘性;DOPA侧链易与HClO发生亲电亲核反应(2),促使DOPA侧链的断裂,降低粘附蛋白内粘性;在相同温度下,反应(1)和反应(2)的△G<0,且△G(1)<△G(2),反应(1)较易发生.