提高自蔓延高温合成陶瓷内衬钢管性能的研究

在概括了自蔓延高温合成陶瓷内衬钢管的制备原理基础上，从降低陶瓷层孔隙率，减少陶瓷层裂纹和提高陶瓷层结合强度等方面，论述了提高自蔓延高温合成陶瓷内衬钢管性能的措施，对自蔓延高温合成陶瓷内衬钢管的应用现状及展望进行了评述。     

Measurement of Thermal Diffusivity at Low Temperatures Using an Optical Reflectivity Technique

An experimental arrangement has been developed for measuring the transient temperature responses and the thermal diffusivities of foil materials in the range of 10 to 300K by using the optical reflectivity technique. The cryogenic system with optical windows is designed to provide temperatures from 10 to 300 K. The front surface of a foil specimen is heated by a pulsed Nd:YAG laser. In situ measurement of the reflectivity of a continuous-wave He–Ne laser at the rear surface is conducted on the microsecond time scale. Using the temperature dependence of reflectivity, the transient temperature response is deduced. The thermal diffusivity is obtained by fitting Parker's formulae to the experimental data on temperature rise. Stainless-steel foils are chosen as samples and are studied in the region from 10 to 300 K. The accuracy is examined by comparing the present results with the theoretical temperature responses and thermal diffusivity data from the literature. Good agreement is observed.     

碳/碳复合材料CVI工艺中热解碳形成机理的研究

对碳碳复合材料CVI或（CVD）工艺中热碳组织的类型，沉积机理等研究情况进行了简要的综述，并对其进一步研究提出了相应观点。     

测定钠中杂质的手动阻塞计的研究

文章介绍了测定钠中杂质浓度的手动阻塞计的原理、装置和实验结果。为了减少测量误差,我们研究了影响准确测定阻塞温度的因素,并且找到了减少测量误差的办法。在同样的杂质饱和温度下,该阻塞计测得的高、低阻塞温度所对应的杂质浓度差是很接近的。对氧其差值为1.03ppm;对氢为0.0763ppm。     

SO2转化温度异常情况分析

结合凤山实业总公司硫酸车间 SO2 转化系统的具体工艺流程 ,分析近几年转化系统出现温度不正常的原因 ,提出解决方法     

High temperature controlled atmosphere experiments for catalysts in a transmission electron microscope

A new transmission electron microscopy (TEM) specimen preparation procedure for high temperature experiments using a controlled atmosphere specimen holder (HTCASH) has been developed. It is designed for studying the microstructure of catalyst specimens before and after treatments in various gases. The procedure involved (1) finding a new formula for the embedding material, (2) devising a new method of making specimen supports, and (3) developing a method for removing the embedding material after the specimen has been microtomed. These techniques were then brought together to produce the ideal specimens for the HTCASH experiments. As an extra benefit, this procedure is also suitable for preparing specimens for ultrahigh resolution imaging experiments. The application of the new procedure in HTCASH experiments is illustrated through a high temperature reduction of a Co/SiO₂-923 catalyst.     

白钨矿浮选731捕收剂低温乳化试验研究

介绍了731捕收剂在低温条件下试验的情况。试验研究结果表明，采用A和B药剂以5：6的比例混合组成的复合乳化剂对731进行乳化，低温时乳化体系稳定性好，浮选过程中降低乳化731的用量，同时提高了选择性，降低了浮选成本，实现了低温环境下白钨矿正常浮选作业，达到选矿技术攻关指标。     

Corrosion behaviour of low-Si alloyed steels in neutral reducing conditions at 90 °C

Electrochemical investigations on low-Si alloyed steels with Si content ranging from 0.25 to 3.2 wt.% were carried out in a 0.1 M NaCl borate-buffered solution (pH 8.4) in reducing conditions at 90 °C. Silicon as an alloying element was proved to degrade at first the steel ability to passivate. For longer immersion times, protective effects developed more efficiently on the steel containing 3.2 wt.% silicon. Passive layers electrochemically formed in the transpassive domain on the steel containing 3.2% Si were shown to be significantly different from those grown at rest potential.     

含氯取代基的聚间苯二甲酰间苯二胺的合成与表征

以 2 ,5 -二氯对苯二甲酰氯作为第三单体 ,将其与间苯二甲酰氯、间苯二胺在N ,N -二甲基乙酰胺中进行低温溶液共缩聚反应 ,合成了含氯取代基的聚间苯二甲酰间苯二胺。研究了单体摩尔浓度、反应初始温度、叔胺添加剂种类、第三单体用量等对共聚物相对分子质量的影响 ,并用红外光谱、热重分析等方法对共聚物进行了表征。     

提高自蔓延陶瓷内衬钢管耐蚀性研究的进展

广泛应用于石油，化工，能源等领域的钢管，除了要有高强度外，还要有良好的耐蚀性。自蔓延高温合成技术是制备耐蚀钢管的新技术，具有工艺简单，成本低和产品耐蚀性能好等特点。介绍了自蔓延高温合成陶瓷内衬钢管的原理和提高陶瓷内衬钢管耐蚀性的措施，展望了耐蚀陶瓷内衬钢管在工业生产上的应用前景。