Photocatalytic behavior of TiO_2 and ZnO prepared with different methods under ultraviolet and visible light irradiation

IntroductionIn recent years photocatalytic oxidation hasreceived considerable attention as an alternativeremediation technology since the method offers anumber of advantages over conventionaltechnologies [1,2] Elimination o…     

高铝锌基合金粉末冶金材料及其摩擦学特性初探

初步研究了高铝锌基合金的粉末冶金工艺及其材料的摩擦磨损性能。通过气喷气冷法制取合金粉末，用压制后真空烧结的方法制备高铝锌基合金粉末冶金材料。实验结果表明，高铝锌基合金的粉末冶金试样在干摩擦和油润滑条件下的磨损率及摩擦系数均小于同一合金的铸造试样，但其压溃强度有待提高。在实验的基础上还探讨了该材料的耐磨减摩机理     

Dissolution mechanism of solid nickel in liquid zinc saturated with Fe

The dissolution behavior of solid nickel in static liquid zinc saturated with Fe at 723 K was studied. The results show that when immersing solid Ni in liquid Zn saturated with Fe, the intermetallic compound layers consisted of γ and δ phases are formed on nickel substrate, which is the same as that in liquid pure zinc. However, some F2 particles are formed in the liquid near the solid/liquid interface. These Г2 particles can easily heterogeneously nucleate on （particles and grow fast. The dissolution process is governed by diffusion of nickel atom across a concentration boundary layer in liquid Zn saturated with Fe, and is different from a mixed control mechanism of nickel in liquid pure zinc. The participation of Г2 particles makes the dissolution of solid Ni in the liquid accelerated.     

纯Ar气氛中退火对Al掺杂ZnO薄膜性能的影响

用射频磁控溅射技术制备了高度择优取向的Al掺杂ZnO(ZAO)薄膜,并对薄膜在纯氩气中进行了400～600℃的退火处理.利用X射线衍射(XRD)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)、光谱仪和四探针测试仪等对退火前后薄膜进行了表征和光学、电学性能研究.研究表明,纯氩气中退火处理对ZAO薄膜的晶体、光学和电学性能有影响.原位沉积的薄膜电阻率2.59Ωcm,可见光区透过率约70%.500℃纯Ar气氛中退火1h后,ZAO薄膜的平均晶粒有所长大,薄膜内应力达到最小,接近于松弛状态;薄膜可见光区平均透过率从70%提高到80%左右;而薄膜的电阻率变化不明显,从2.59Ωcm降低到1.13Ωcm.     

锌粉颗粒形状对机械沉积无结晶镀层结构的影响

以球状锌粉和片状锌粉为原始锌粉借助于机械镀工艺制备了无结晶锌防护层，运用光学显微镜（OM）、扫描电子显微镜（SEM）观察了镀层的结构形貌；采用XRD技术分析了镀层的物相组成；采用贴滤纸法进行了镀层的孔隙率测试。研究结果表明，片状锌粉制备的镀层比球状锌粉制备的镀层表面要平滑、光亮。球状锌粉制备的镀层中锌粉颗粒呈紧密堆积，部分锌粉颗粒发生塑性变形；片状锌粉制备的镀层中的锌粉颗粒呈层片状叠加，镀层中锌粉颗粒没有发生明显塑性变形。两种形状锌粉制备的镀层均为锌基多相混合体系，镀层中没有固溶体、化合物等合金相产生，属于锌基复合镀层。锌粉颗粒形状对镀层中颗粒之间的结合机理没有显著影响，两种镀层中锌粉颗粒间均以机械咬合为主。     

电镀锌层的大气腐蚀行为研究

研究了传统的氰化物镀锌层和无氟镀锌层在７个大气站９年的大气暴露腐蚀的试验结果，讨论了镀锌层的耐蚀性及４种钝化工艺的防护效果     

稀土元素提高渗硼层抗熔锌腐蚀性能的研究

采用固体法硼稀土共渗,研究了加稀土对渗层抗熔锌腐蚀性能的影响.结果表明,加入稀土后渗层抗熔锌腐蚀能力比不加稀土的提高3倍.主要原因是加入稀土后渗层致密、成分均匀、缺陷少、组织韧性好、裂纹扩展阻力大,致使裂纹不易扩展,难以形成锌蚀通道,从而材料的抗熔锌腐蚀能力增强.     

Composite corrosion inhibitors for secondary alkaline zinc anodes

The corrosion inhibition property of PEG600 and In(OH)3 as composite corrosion inhibitors for secondary alkaline zinc electrodes was studied, and the inhibition efficiency was determined as 81.9%. The research focused on the mechanism by the methods of electrochemical impedance spectroscopy, polarization curves and IR spectroscopy. The results indicate that the corrosion inhibition effectiveness is attributed to the joint inhibition of anodic zinc dissolution and cathodic hydrogen evolution. And the anodic process is depressed to a greater extent than the cathodic process. The synergistic mechanism of the composite inhinbitors proves to be the enhancement of adsorption of PEG600 by In(OH)3. Potentiostatic experiment results and SEM images verify the inhibition of dendritic growth by the composite inhibitors.     

硫酸盐还原菌对海底土中锌腐蚀的影响

利用微生物分析、交流阻抗测试技术、扫描电镜及表面能谱等方法，在室内模拟条件下研究了海底土中硫酸盐还原菌对锌腐蚀的影响，以及在以接菌及灭菌的海底土构成的宏电池腐蚀中锌的腐蚀行为。180d的试验结果表明：海底土中硫酸盐还原菌增强锌的腐蚀，锌在接菌泥中的平均腐蚀速率及点蚀深度均大于在灭菌泥中的平均腐蚀速率及点饰深度，平均腐蚀速率相差7．0倍，点蚀速率相差15．0倍以上。在接菌和灭菌海底土构成宏电池时，接菌海底土中锌作为阳极，腐蚀速率比自然腐蚀状态下有所增大，加速率为12．7％，而在灭菌海底土中锌作为阴极，腐蚀速率比自然腐蚀状态下有所减小。     

SiC颗粒增强锌基复合材料硬度的研究

本文研究了热处理条件对ＳｉＣ／Ｚｎ基复合材料硬度的影响，分析了循环等温处理过程中复合材料硬度的变化规律，并讨论了复合材料组分、温度以及热处理条件与该复合材料硬度特性的关系，提出了改善这类复合材料硬度的途径。