在KCl、NaCl熔剂的保护下,液态Mg能够还原K2ZrF6.通过控制炉料配比、还原温度、还原时间,并用机械正反向交替搅拌,成功地解决了传统生产工艺中渣相与Mg-Zr中间合金难以分离、合金杂质含量偏高、合金成分偏析的难题,获得了高质量的Mg-Zr中间合金.     

Preparation and Compressive Stress Effect of Polymer Matrix RE-Fe Giant Magnetostrictive Composite

Polymer matrix RE-Fe giant magnetostrictire composite （GMPC） was prepared using bonding and magnetic field forming technique, and magnetostriction of samples was measured for different compressive stress. The experimental results show thai there is certain compressive effect in GMPC. And the influence of compressive stress on magnetostriction of sample was investigated. It offers essential reference for application and device design of GMPC.     

用于模具制造的表面工程技术的进展

可用于模具制造的表面工程技术十分广泛，而稀土表面工程技术和纳米表面工程技术的进展必将进一步推动模具制造的表面工程技术的发展。     

聚酯薄膜砂带研制成功

湖北玉立砂带集团股份有限公司继锆刚玉涂层砂带、软基涂层砂带研制成功后，今年又推出砂带新品——聚酯薄膜砂带系列产品。该产品经市场试用后，深受用户喜爱，发展前景广阔。     

Synthesis, Characterization and Crystal Structure of Quaternary Complex of Gadolinium （Ⅲ）

Ａｎｕｍｂｅｒｏｆｌａｎｔｈａｎｉｄｅｔｅｒｎａｒｙｃｏｍｐｌｅｘｅｓｃｏｎ ｔａｉｎｉｎｇｈｅｔｅｒｏｃｙｃｌｉｃａｍｉｎｅｓｈａｖｅｂｅｅｎｒｅｐｏｒｔｅｄｓｉｎｃｅ1960 [1] .Ｉｎｒｅｃｅｎｔｙｅａｒｓｍｕｃｈａｔｔｅｎｔｉｏｎｈａｓｂｅｅｎｐａｉｄｔｏｑｕａｔｅｒｎａｒｙｃｏｍｐｌｅｘｅｓｏｆｌａｎｔｈａｎｉｄｅｓｂｅｃａｕｓｅｏｆｉｎ ｔｅｒｅｓｔｉｎｇｓｔｒｕｃｔｕｒｅ ,ｃｏｏｒｄｉｎａｔｉｏｎｍｏｄｅ ,ｃｏｍｐｅｔｉｔｉｏｎｒｅ ａｃｔｉｏｎａｎｄｐｒｏｐｅｒｔｙ[2～ 9] .ＥＳＲｃａｎｅ…     

稀土改善09CuPTiRE耐候钢耐蚀性的作用机理

应用扫描电镜(SEM)、离子探针(IMA)、X射线光电子能谱(XPS)和交流阻抗法研究含不同稀土耐候钢稀土提高耐大气腐蚀作用机理。结果表明,合适的稀土含量可显著提高钢的耐腐蚀性,稀土能促进Si、Cu和P在内锈层中以Si~(4+)、Cu~+和P~(5+)形态富集,并观察到锈层中的稀土。钢中加入稀土形成了致密连续厚而粘附性好的含硅铜稀土的复合铁锈层,从而提高了抗大气腐蚀性能。     

Nd—Fe—B新型稀土永磁材料

近20年来,稀土永磁材料的开拓及其发展经历了三代,即第一代RCo_5型(1966年),第二代R_2Co_(17)型(1972年)和第三代Nd-Fe-B系(1983年)永磁合金(R为稀土或混合稀土族元素)。永磁合金的最大磁能积(BH)_(max)随年代呈指数式增加。早就发现的R_2Fe_(17)居里温度太低,而且Nd_2Fe_(17)还缺少必要的磁晶各向异性。这些性质限制了它的发展。但在其中添加B后,稳定了四方结构,显示出易磁化轴各向异性和较高的居里点(580K。自此,第三代稀土永磁体发展起来了。1983年日本正式公布了无钻、高性能的新型Nd-Fe-B永磁体,最大磁能积达到36.3MGOe;1984年达到42.9MGOe,1985年达到44.8MGOe。目前日本最大磁能积已突破50MGOe,并达到50.6MGOe的最高水平。     

Study on Luminescence Properties of High-Density Phosphors BiTaO4：Pr^3＋ and BiTaO4

The photoluminescence properties of BiTaO4:Pr^3 and BiTaO4 at room temperature were studied, and the infrared transmission and diffusion reflection spectra of BiTaO4 were measured. The photoluminescence spectrum of BiTaO4 peaks at about 420, 440 and 465nm. There has an obvious excitation band from 330 to 370nm. The photoluminescence spectrum of BiTaO4:Pr^3 consists of the characteristic emission of Pr^3 , and its main peak is at 606 nm from ^3P0→^3H6 transition of Pr^3 . Its excitation spectrum consists of the wide band with maximum at 325nm, the wide band in the range of 375-430nm, and the characteristic excitation of Pr^3 .The bands at 325nm and 375-430nm may be from the absorption of the charge transfer transition of the tantalate group and defect energy levels in its forbidden band, respectively.There is energy transfer from host to Pr^3 . Because both the host density and photoluminescence peak intensity of BiTaO4:Pr^3 are superior to PbWO4, BiTaO4:Pr^3 may be a potential heavy scintillator.