Influence of chromium on the local structure and morphology of ferric oxyhydroxides

The extended X-ray absorption fine structure (EXAFS) method and transmission electron microscopy (TEM) have been used for characterizing the local structure and morphology of ferric oxyhydroxides, α-FeOOH and γ-FeOOH, with and without chromium. These ferric oxyhydroxide powders were prepared from aqueous solutions containing iron and chromium ions. Radial structural functions for iron obtained by Fe K edge EXAFS spectra showed that the linkage of structural units formed by FeO₆ octahedra in γ-FeOOH is distorted by chromium addition, while such distortion in α-FeOOH is not clearly detected. On the other hand, Cr K edge EXAFS spectra showed that the local structure around chromium does not necessarily correspond to the local structure around of iron, which is observed by Fe K edge EXAFS spectra. This suggests that the structural units containing iron and chromium are heterogeneously distributed in these ferric oxyhydroxides. The local structural information was discussed coupled with morphological features of these ferric oxyhydroxides observed by TEM.     

高精度冷轧不锈钢管生产

介绍了用ＬＤ型冷轧管机生产高精度冷轧不锈钢管的经验和质量保证措施。     

奥氏体化温度及冷却方式对20Mn2SiVB钢组织及性能的影响

通过各种试验手段,研究了20Mn2SiVB钢不同奥氏体化温度及不同冷却方式处理后其显微组织及其强度和塑性的变化,确定了最佳的热处理工艺。结果表明:900℃奥氏体化后风冷时钢的强塑性最好;在强塑性最佳时的微观组织是铁素体+粒状贝氏体。     

20G高压锅炉管裂纹原因分析

对20G高压锅炉管产生裂纹的原因进行了分析，结果表明是冷拔工艺不当所致。     

Microstructural Investigation of Protective and Non-Protective Oxides on 11% Chromium Steel

FIB, SEM and STEM/EDX were used to investigate X20 stainless-steel samples exposed to dry O₂, or O₂ containing 40% H₂O, with a flow velocity of 0.5 cm/s or 5 cm/s, for 168 hr or 336 hr at 600°C. Thin protective Cr-rich (Cr,Fe)₂O₃ was maintained on the samples exposed to dry O₂, even after 336 hr, and on the sample exposed to O₂/H₂O mixture with the low-flow velocity (0.5 cm/s) for 168 hr. The oxide scale formed in the latter environment contained less Cr, due to Cr loss through CrO₂(OH)₂ evaporation. Breakaway oxidation occurred on the samples exposed in high-gas-flow velocity for shorter time (168 hr) or in low-gas-flow velocity (0.5 cm/s) for longer time (336 hr). The breakaway scales featured a two-layered structure: an outward-growing oxide “island” consisting of almost pure hematite (α-Fe₂O₃), and an inward-growing oxide “crater” consisting of (Cr,Fe)₃O₄. The transition from a thin protective (Cr,Fe)₂O₃ scale to a non-protective thick scale on this martensitic/ferritic steel originated locally and was followed by rapid oxide growth, resulting in a thick scale that covered the whole sample surface.     

国内外不锈钢精炼剂研究发展现状

分析了精炼剂组元元素的作用能力，讨论并总结了精炼剂组元的复合作用，介绍了几种国内、国外精炼剂产品，提出发展高效复合精炼剂的想法。     

含Cl^-溶液中SO4^2-对316不锈钢临界点蚀温度的影响

采用外加恒电位下腐蚀电流-温度扫描方法研究了在0．5％Cl^-溶液中，SO4^2-浓度对316不锈钢点腐蚀行为的影响．结果表明，随着SO4^2-浓度的增加，钝化电流增加，开路电位降低．当SO4^2-浓度低于0．42％时，316不锈钢的临界点蚀温度比不存在SO4^2-时的临界点蚀温度低；当SO4^2-浓度大于0．42％时，临界点蚀温度比不存在SO4^2-时的临界点蚀温度高．从离子竞争吸附的角度进行分析，对SO4^2-加速与抑制点蚀两种作用规律的形成原因进行了解释．     

低碳低合金铸钢力学性能的研究

利用Olympus光学显微镜、扫描电镜(SEM)及能谱分析(EDAX)探讨了等温淬火工艺对低碳低合金CrMnSi铸钢力学性能的影响,并通过XRD定量分析了相的组成.结果表明,合适的等温淬火工艺,可获得一定数量的贝氏体和残余奥氏体(约6%)的复合组织,冲击断口形貌由解理刻面变为韧窝状,铸造成形无缺口试样(10 mm×10 mm×55 mm)的冲击韧度由ακ≤30 J/cm2增加至ακ≥170 J/cm2,硬度HRC≥40,具有较高硬度和冲击韧度的配合.     

简单断面孔型计算机绘图系统简介

介绍了简单断面孔型计算机绘图系统的编制方法、使用范围 ,计算机绘图的步骤及特点