Bi-based superconductors fabricated in high magnetic fields

The microstructure and superconducting properties of Bi-2223 superconductor fabricated in high magnetic fields were investigated. The results shows that the Bi-2212 grains with their c-axis parallel to the magnetic field were formed after the partial-melting and solidification in 8 T magnetic field, and transformed into the Bi-2223 grains with c-axis alignment during the further sintering process at 840 ℃ without magnetic field. The conversion of Bi-2212 grains to Bi-2223 grains has the heredity in grain alignment. The mixed structures of the Bi-2223 and the Bi-2212 grains with their c-axis parallel to the magnetic field are formed in samples sintered at 850-855 ℃ in 10 T magnetic field. When sintered in 10 T below 845 ℃, a high proportion of Bi-2223 phase is obtained, however no preferred orientation is observed. The Bi-2223 grains with their c-axis parallel to the axial direction of the vertical tube furnace are formed not only on the surface, but also in the center of the sample sintered at 850 ℃ for 120 h in a 15 ℃/cm temperature gradient without magnetic field. Moreover, the samples sintered in the temperature gradient and in a 10 T magnetic field have a stronger c-axis alignment ofbi-2223 phase.     

基于漏磁原理的钢丝绳探伤仪影响因素研究

介绍了钢丝绳探伤仪漏磁检测原理,并使用有限元分析方法分析了传感器零件的材料、钢丝绳的提离距离及断丝根数等对基于漏磁原理的钢丝绳探伤仪检测结果的影响。分析结果表明,提离距离、断丝根数等因素对探伤仪检测结果影响较大,断丝角度、深度等因素影响较小。     

Optimal experimental design and some related control problems

This paper traces the strong relations between experimental design and control, such as the use of optimal inputs to obtain precise parameter estimation in dynamical systems and the introduction of suitably designed perturbations in adaptive control. The mathematical background of optimal experimental design is briefly presented, and the role of experimental design in the asymptotic properties of estimators is emphasized. Although most of the paper concerns parametric models, some results are also presented for statistical learning and prediction with nonparametric models.     

红芪活性成分免疫调节作用及机制研究进展

免疫功能受损或免疫系统紊乱会导致机体疾病发生,影响人身体健康,基于调节机体免疫治疗疾病已成为临床应用热点。红芪作为甘肃大宗药材,临床应用广泛,具有抗肿瘤、抗炎、免疫调节等多种药理作用。红芪活性成分主要有红芪多糖、黄酮类、萜类、皂苷类等,其中红芪多糖为红芪发挥免疫调节作用主要的物质基础。红芪增强机体免疫力主要体现在增强免疫器官功能,诱导免疫细胞分化、促进免疫因子分泌,提高单核巨噬细胞吞噬功能、调节炎性因子水平以及激活相关通路等方面来达到其抗肿瘤、抗炎作用。本文主要对红芪活性物质免疫调节作用进行阐述,为红芪的进一步临床开发应用提供思路。     

Proximity-Induced Fully Ferromagnetic Order with Eightfold Magnetic Anisotropy in Heavy Transition Metal Oxide CaRuO3

Ferromagnetic materials with a strong spin-orbit coupling (SOC) have attracted much attention in recent years because of their exotic properties and potential applications in energy-efficient spintronics. However, such materials are scarce in nature. Here, a proximity-induced paramagnetic to ferromagnetic transition for the heavy transition metal oxide CaRuO₃ in (001)-(LaMnO₃/CaRuO₃) superlattices is reported. Anomalous Hall effect is observed in the temperature range up to 180 K. Maximal anomalous Hall conductivity and anomalous Hall angle are as large as ∼15 Ω⁻¹ cm⁻¹ and ∼0.93%, respectively, by one to two orders of magnitude larger than those of the typical 3d ferromagnetic oxides such as La_0.67Sr_0.33MnO₃. Density functional theory calculations indicate the existence of avoid band crossings in the electronic band structure of the ferromagnetic CRO layer, which enhances Berry curvature thus strong anomalous Hall effects. Further evidences from polarized neutron reflectometry show that the CaRuO₃ layers are in a fully ferromagnetic state (∼0.8 μ_B/Ru), in sharp contrast to the proximity-induced canted antiferromagnetic state in 5d oxides SrIrO₃ and CaIrO₃ (∼0.1 μ_B/Ir). More than that, the magnetic anisotropy of the (001)-(LaMnO₃/CaRuO₃) superlattices is eightfold symmetric, showing potential applications in the technology of multistate data storage.     

35 T强磁场下Cernox和氧化钌温度传感器的磁致电阻效应研究

以Cernox(CX-1050、CX-1030)和氧化钌(RX-202、RX-102)温度传感器为研究对象,研究了其在0—35 T场强、0.75—69.5 K温区下的磁致电阻效应。实验结果表明:CX-1050和RX-202的磁效应和在35 T下的测量误差都随温度的变化出现正负磁效应和正负温度误差交替的现象,且低于10 K时,磁效应随温度的变化率明显增大,在35 T、4.2 K处CX-1050和RX-202的磁效应分别为-6.63%、2.21%;总体来说强磁场下受磁阻影响由小到大分别为RX-202、CX-1050、CX-1030、RX-102,尤其RX-202,在1—35 T、4.2 K以下产生的测量误差小于-0.1 K。Cernox和氧化钌温度传感器受磁场的影响都较小。     

强磁场对硅锰铸钢于A_1点附近等温珠光体相变的影响

通过开展12 T强磁下硅锰铸钢(50Si_2Mn_3)于A_1点温度附近不同等温时间的热处理试验,并对比强磁场与无磁场条件下等温珠光体相变试验结果,研究了磁场对珠光体转变量及组织形貌的影响。研究表明,对于50Si_2Mn_3在A1点以下较高温度范围内,强磁场可缩短珠光体相变的孕育期,促进硅锰铸钢珠光体转变,使其转变量明显增加;强磁场能够提高珠光体转变临界点,使50Si_2Mn_3在A1点以上等温过程中能够发生珠光体相变。     

Operational active fire mapping and burnt area identification applicable to Mexican Nature Protection Areas using MODIS and NOAA-AVHRR direct readout data

Since 1999, the National Commission for the Knowledge and Use of the Biodiversity (CONABIO) in Mexico has been developing and managing the “Operational program for the detection of hot-spots using remote sensing techniques”. This program uses images from the MODerate resolution Imaging Spectroradiometer (MODIS) onboard the Terra and Aqua satellites and from the Advanced Very High Resolution Radiometer of the National Oceanic and Atmospheric Administration (NOAA-AVHRR), which are operationally received through the Direct Readout station (DR) at CONABIO. This allows the near-real time monitoring of fire events in Mexico and Central America. In addition to the detection of active fires, the location of hot spots are classified with respect to vegetation types, accessibility, and risk to Nature Protection Areas (NPA). Besides the fast detection of fires, further analysis is necessary due to the considerable effects of forest fires on biodiversity and human life. This fire impact assessment is crucial to support the needs of resource managers and policy makers for adequate fire recovery and restoration actions. CONABIO attempts to meet these requirements, providing post-fire assessment products as part of the management system in particular for satellite-based burnt area mapping. This paper provides an overview of the main components of the operational system and will present an outlook to future activities and system improvements, especially the development of a burnt area product. A special focus will also be placed on the fire occurrence within NPAs of Mexico.     

Finite Element Analysis of 6300 Deep Groove Ball Bearing

Rolling bearing is widely used in mechanical support, its general components are the inner ring, outer ring, the ball, retainer etc.. Now many companies in developed countries and university in the rolling bearing as the research object, and has made great progress in design theory, the experiment method and production technology etc. We will use the finite element ANSYS to establish the model of deep groove ball bearing. Through the contact analysis, we can get the contact stress between the rings and balls, strain, contact state, penetration, sliding distance and the friction stress distribution. These values are compared to the theoretical values with Hertz theory, and they have better consistency, provide the good theoretical basis for the optimization design of rolling bearings.