Corrosion failure of Zn–Al detonator housing

Some batches of detonator housings made up of Chromium plated Zn–Al alloy were found in an extensively cracked condition after few months of storage at room temperature. An analysis of the failure showed that the cracks were due to intergranular corrosion facilitated by segregation of lead at the grain boundaries. Improper chromium plating further aggravated the corrosion problem. This failure case emphasises the need for strict control of chemical composition for components made from Zn–Al alloy and the process of Cr plating of the components.     

Improvement of photon collection in Cu(In,Ga)Se2 solar cells and modules by fluorescent frequency conversion

Fluorescent photon down conversion for the improvement of the blue response of ZnO/CdS/Cu(In,Ga)Se₂ heterojunction solar cells and modules is investigated. Fluorescent dyes of the series Lumogen® F are analyzed by optical transmission and reflection as well as by photoluminescence measurements. A spectral transfer matrix formalism is introduced that allows to predict the suitability of a luminescent dye as a down-converter for a given solar cell from its absorption/emission properties. We find that Lumogen® F Violet 570 and Lumogen® F Yellow 083 as well as a combination of both yields improvements for Cu(In,Ga)Se₂ solar modules. Particularly, we find that the short circuit current density of a Cu(In,Ga)Se₂ mini-module is improved by 1.5 mA cm^− 2 when applying a varnish with a combination of Lumogen® F Violet and Yellow. About 0.5 mA cm^− 2 of this improvement is due to a reduced overall reflectance and an improvement of 1 mA cm^− 2 results from the frequency conversion by the dyes.     

电磁搅拌制备ZL12Y铝合金流变半固态浆料的实验及模拟研究

对不同温度及不同搅拌工艺下得到的材料的显微组织的比较，确定了合理的半固态温度和搅拌工艺，即半固态温度为590℃，震荡电流为500A。随后对单个线圈电磁搅拌过程进行建模及电磁场和流速场的耦合模拟得到了电磁场和流速场分布，此结果与电磁搅拌的原理及实验结果相一致。计算出在该温度和工艺下熔体内部的平均流动速度为3．2cm／s，将该结果作为能否得到半固态浆料的判据。     

含Zr低合金高强度钢中夹杂物的特性

用电子探针研究了含Zr低合金高强度钢中夹杂物的形貌、大小及分布等特性。结果表明 ,钢样中的夹杂物为圆形 ,呈分散分布 ,其组成系含ZrO2 的复合夹杂物 ,而且MnS依附此复合夹杂物成核和长大。钢中添加少量Zr可明显改善夹杂物形态和分布 ,从而改善钢的强度和韧性     

Al2O3对唐钢高炉炉渣性能的影响

针对唐钢近2年提高进口矿配比后，Al2O3含量升高对炉渣流动性带来的不利影响，对唐钢高炉的炉渣性能进行了试验研究。并结合国内同行业的生产实践经验，从理论上分析了炉渣中Al2O3及MgO的适宜含量范围，着重论述了唐钢所处冀东矿区条件下降低Al2O3的主要途径及适应高Al2O3炉渣的具体措施。     

60Si2Mn(A)弹簧钢的脱氧工艺

为了提高60Si2Mn(A)弹簧钢的质量,在LF精炼中进行了不同脱氧工艺的脱氧试验。结果表明:采用铝预脱氧、钡合金终脱氧及夹杂物变性脱氧工艺可使弹簧钢的氧含量降低到15×10-6以下,氧化物夹杂中Al2O3的比例小于40%。     

Hybrid numerical scheme for time-evolving wave fields

Many problems in geophysics, acoustics, elasticity theory, cancer treatment, food process control and electrodynamics involve study of wave field synthesis (WFS) in some form or another. In the present work, modelling of wave propagation phenomena is studied as a static problem, using finite element method and treating time as an additional spatial dimension. In particular, WFS problems are analysed using discrete methods. It is shown that a fully finite element-based scheme is very natural and effective method for the solution of such problems. Distributed WFS in the context of two-dimensional problems is outlined and incorporation of any geometric or material non-linearities is shown to be straightforward. This has significant implications for problems in geophysics or biological media, where material inhomogeneities are quite prevalent. Numerical results are presented for several problems referring to media with material inhomogeneities and predefined absorption profiles. The method can be extended to three-dimensional problems involving anisotropic media properties in a relatively straightforward manner. Copyright © 2006 John Wiley & Sons, Ltd.     

铸铝激光熔融处理后的组织与性能

应用光学和电子显微镜及显微硬度计研究了铸造Al-Si合金经激光表面熔融处理后的组织和性能。指出,组织分熔化区、过度区和基体三层。在熔化区中树枝状先共晶α相的平均宽度由原始组织的20～40μm细化到2～3μm,同时共晶组织也被大大细化。这些变化使显微硬度值由67.4提高至109～115.     

化学镀Ni—P镀层的X射线衍射研究

根据X射线衍射分析结果,对化学镀高P(含P>11wt％或19at％)Ni-P镀层加热时效时,镀层成分和加热温度对结构转变的影响作了研究,结果表明,高P共晶、过共晶(含P>11wt％或19at％)合金的结构转变有如下特征:(1)相同加热时效条件下,Ni-P合金的结构转变与成分有密切关系:(2)对同一成分的过共晶合金,Ni-P合金的结构转变与时效温度密切相关;(3)过共晶合金在290～360℃温度范围内时效处理,出现Ni_xP_y介稳相,X射线衍射分析认为Ni_xP_y为Ni_(12)P_5。     

掺杂WRe3、WRe25合金的高温电阻－温度特性

本文报导了采用一种新型高温陶瓷发热体高温管状炉，通以氩气保护，测量ＷＲｅ合金丝的电阻－温度（１６００℃）特性试验方法，该方法较真空炉简便、实用且试验费用低而准确，测量数据与美国研究报导一致。