Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

Corrosion behaviour of AA2024 aluminium alloy in different tempers in NaCl solution and with the CeCl3 corrosion inhibitor

The paper analyses the corrosion behaviour of naturally and artificially aged AA2024 alloy in NaCl solution and in the presence of an environment-friendly corrosion inhibitor, CeCl₃. On the basis of the values of polarisation resistance and corrosion current density, the corrosion resistance of the protective inhibitor film is established as well as the general corrosion resistance of this aluminium alloy. Resistance to pit formation is determined based on the difference in pitting and corrosion potentials while resistance to pit growth is determined based on the amount of charge consumed during pit growth. A scanning electron microscope is used to examine the morphology of the pits formed during the pitting corrosion testing, as well as to determine the cerium content on intermetallic particles and the matrix AA2024 alloy. The corrosion behaviour of AA2024 alloy is investigated after different test periods in NaCl solution and in the same solution with the CeCl₃ inhibitor. The corrosion resistance of both tempers of AA2024 alloy is more than one order of magnitude higher in the presence of CeCl₃. An explanation of the observed differences in the corrosion behaviour of the naturally and artificially aged AA2024 alloy is proposed. Different corrosion behaviour of the alloy after different test periods is also explained.     

雕刻技术的研制和应用

在对铝合金铸件进行X射线实时探伤时，由于采集回来的许多图像的目标物体的轮廓比较模糊，这样在评片时容易造成对铸件的误判和漏判。针对这种现象并结合这类图像噪声源多的特点，在研究常用卷积算法的基础上，采用特殊卷积（特殊的卷积核）操作，同时根据雕刻的艺术底色为灰色，最后给卷积结果加上灰度值128，实验结果表明图像中目标物体的轮廓变得更清楚，同时处理后的图像具有比较好的三维效果，这给工作人员在看图时带来了方便。     

Microstructures and Phase Transition Points of As-Cast Mg-Zn-Y System Alloys

As-east mierostruetures and their distribution of Mg-Zn-Y ternary alloy with high magnesium, low zinc and yttrium were examined using Nikon Epiphot optical microscopy （OM）, RigakuD/max-3C X- ray diffraetion （XRD）, and JEOL JSM-6700F scanning electron microscopy （SEM） equipped with an energydispersive X-ray spectroscopy （EDS）. In the as-east mierostructures, Yttrium and zinc tend to segregate at grain boundaries,     

Oxidation of Hastelloy-XR Alloy for Corrosion-Resistant Glass-Coating

The oxidation behavior of Hastelloy-XR alloy was investigated to obtain the optimum surface condition for corrosion-resistant glass-coatings. The surface morphology of oxide scales changed significantly with variation of temperatureand oxygen partial pressure (po2 ). The oxidation kinetics was mainly parabolic independent of oxidation conditions.The oxide scales were consisted of inner Cr2O3 and outer spinel layers. The phase component of spinel layers wereMn1.5Cr1.5O4 and (Mn,Ni)(Cr,Fe)2O4 for the oxygen partial pressures po2<10 kPa and po2>10 kPa, respectively.The optimum oxidation condition to obtain an oxide scale for well-adhered glass-coating to the substrate was 1248 Kand po2 =0.01 kPa for the oxidation time of 43 ks.     

噻吩在镍基非晶态合金上的吸附和脱附

应用静态吸附、动态吸附、程序升温脱附和程序升温还原等实验方法，考察了噻吩在Ni基非晶态合金上的吸附和脱附行为。常温下，噻吩分子首先吸附在清洁的Ni表面，并立刻被活化，发生氢解反应，C-S键断裂，释放出烃类部分，S留在Ni原子上。噻吩可以在Ni基非晶态合金表面发生强度不同的化学吸附。弱化学吸附的噻吩可以脱附；强化学吸附的噻吩不会脱附，而在高温下发生氢解反应。     

沉管隧道水下最终接头施工技术初探

简述了沉管隧道水下最终接头施工技术的应用现状，结合具体隧道工程实例，从外模工程、混凝土结构两方面介绍了最终接头施工技术，表明了该技术具有运用价值。     

不锈钢管道坡口加工的新方法

对于不锈钢管及合金钢管坡口的加工,采用以往的加工方法切割出来的坡口一般参差不平、比较粗糙,难于打磨平整。使用LGK空气等离子切割机和磁力管道切割机的组合加上一定的辅助手段,改善了不锈钢管及合金钢管的坡口加工效果,使加工出来的坡口像碳钢管一样平整,更加容易打磨组焊。文章介绍了这一新方法所用的设备、材料、切割原理以及操作过程。     

Improving narrow bandgap a-SiGe:H alloys grown by hot-wire chemical vapor deposition

We have improved the electronic properties of narrow-bandgap (Tauc gap below 1.5 eV) amorphous-silicon germanium alloys (a-SiGe:H) grown by hot-wire chemical vapor deposition (HWCVD) by lowering the substrate temperature and deposition rate. Prior to this work, we were unable to grow a-SiGe:H alloys with bandgaps below 1.5 eV that had photo-to-dark conductivity ratios comparable with our plasma-enhanced CVD (PECVD) grown materials [B.P. Nelson et al., Mater. Res. Soc. Symp. 507 (1998) 447]. Decreasing the filament diameter from our standard configuration of 0.5 mm to 0.38 or 0.25 mm provides first big improvements in the photoresponse of these alloys. Lowering the substrate temperature from our previous optimal temperatures (T_sub starting at 435 °C) to at 250 °C provides additional photo-to-dark conductivity ratio increasing by two orders of magnitude for growth conditions containing 20–30% GeH₄ in the gas phase (relative to the total GeH₄+SiH₄ flow).     

Improving Short-Circuit Current Capacity, Resistance, and Breaking Load of OPGW Constructions by Modifying Aluminium Alloy With AlB2

This article presents a method that can be applied to molten AA-6101 alloy to improve electrical properties of the aluminium part of the optical ground wire (OPGW) used in overhead transmission lines to protect phase conductors from lightning strike and to transmit signals and data. AA-6101 alloy in casting of the log as 6 m length and 178 mm diameter for extrusion has been inoculated by AlB₂ to decrease detrimental effects of Cr, Ti, V, and Zr on the conductivity of the material. After inoculation, improved billets were extruded as 9.5 mm diameter feedstock. Required wires drawn from the feedstock according to the construction types of OPGW to be tested were exposed to aging at 175°C, 6 h (T-8). Upon completion of the back-twist and performing-type stranding process, resistance, and short-circuit current capacity and breaking load of the OPGW 88/44 constructions with other metal combinations have been examined and tested to show improvement. Results are summarized in tables and graphically.