Finite element analysis of femoral components paper III – hip joints

Finite element analysis of the hip implant is conducted in this paper for representative femoral cross-section geometries and development of stress in the presence of bone cement is elucidated. Differences in cement stresses generated by varying implant cross-sections were compared with conventional features derived from representative implants. The analysis was performed under idealized implant assemblies by constraining the implant movement in the assembly. The cross-sections and implant geometries used are generic and intended to be representative of available geometries. This paper is a part of student research projects, prepared from a series of activities in biomedical implant research currently underway at Ohio Northern and Arkansas Tech Universities.     

Intergranular corrosion of a light aircraft aluminum alloy propeller

Examination of the wreckage of a light aircraft revealed that approximately 20 cm was missing from one tip of the aluminum alloy propeller. Fractographic and metallographic examination of the remaining portion of the propeller revealed extensive grain-boundary separation in the vicinity of the fracture, and grain edges and corners rounded by corrosion on the fracture surface. Energy dispersive X-ray analysis (EDXA) revealed fluorine on, and in the vicinity of, the fracture surface. In the ensuing litigation, it was asserted that the crash occurred because the propeller fractured in flight as the result of intergranular attack caused by the use of a fluorine-bearing cleaner.     

激光熔覆专用铁基合金粉末的研究进展

指出了目前防止熔覆层开裂所采取的主要措施中存在的问题,阐述了激光熔覆和热喷涂对于所用合金粉末性能要求之异同,评述了激光熔覆专用铁基合金粉末的研制现状,提出了成分与组织设计的新思想。     

镍铬合金在酸性CuCl2溶液中反应机理

对铜在酸性CuCl_2溶液中蚀刻反应机理论述,利用氧化-还原电动势原理,详细论述了Ni80Cr20合金在酸性CuCl_2溶液中化学蚀刻反应机理,以及影响蚀刻速度的因素,并对溶液中金属离子的存在形式作了验证。     

防止干燥塔塔顶及锥节产生焦粉的方法

描述及分析了干燥塔在生产乳粉过程中出现的塔顶及锥节焦粉现象，并提出了改进方法。     

An integrated approach to the optimum utilization of national tungsten resources: Technology gaps

A critical review of the current status of tungsten resources, of state-of-the-art processing technology and of product development in India vis-a-vis the world scenario is presented. An attempt has been made to identify technology gap areas requiring attention.     

锰铜基高阻尼合金中锌量的测定──硫氰酸盐萃取分离络合滴定法

基于甲基异丁基甲酮于稀盐酸介质中定量地萃取Ｚｎ￣（２＋）与ＣＮＳ￣－形成的络阴离子。从而达到与共存的锰、镍、铝、铬的完全分离。在有氟化物、硫脲存在时Ｆｅ￣（３＋）、Ｃｎ￣（２＋）和Ａｇ￣＋也不被萃取。有机相中的锌于ＰＨ５．５“六胺”缓冲介质中返萃取回水相，用ＥＤＴＡ滴定。在文中给定的条件下锌的一次被萃取率可达９９％以上，成功地解决了锰铜基高阻尼合金中共存离子对锌量测定的干扰问题。     

On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.     

COMPRESSION FATIGUE CRACK GROWTH BEHAVIOUR OF AN ALUMINIUM ALLOY: EFFECT OF OVERLOADING

Abstract— The behaviour of fatigue cracks in an Al-alloy under cyclic compression, either with or without overloads, was studied. For constant-amplitude compressive cycling, a non-catastrophic (saturation) character of the fatigue crack behaviour was confirmed, with the final depth of a crack depending on the applied load level. Single (tensile or compressive) intermittent overloads were shown to re-activate a previously arrested crack while reversed (tensile—compressive or compressive—tensile) ones were also shown to maintain continual fatigue crack extension under otherwise fully compressive cycling.     

绝缘涂敷制件的加工工艺研究与应用

主要论述了电工绝缘粉末的性能及其在高压电器设备应用中的有关试验项目。