Thin films of amorphous and polycrystalline tungsten oxide were produced by reactive dc magnetron sputtering and nanocrystalline films were deposited by advanced gas evaporation. The films were submitted to electrochemical intercalation of Li ions before infrared reflectance measurements were carried out. For crystalline films, the reflectance in the wavelength region 10–30 μm increases upon intercalation, indicating an increasing free-electron contribution. On the other hand, all the films display an increased absorption at wavelengths less than 10 μm when intercalated. The thermal emittance could be varied from about 0.5 to 0.7–0.75 by intercalation in films with thicknesses in excess of 1 μm. Both absorption and interference contribute to the emittance contrast.     

Corrosion behaviour of Ni-Zr-Ti-Si-Sn amorphous plasma spray coating

Ni₅₉Zr₂₀Ti₁₆Si₂Sn₃ amorphous material was deposited by a vacuum plasma spraying technique onto steel and copper substrates in order to investigate their behaviour in a corrosive environment. For comparison, the same alloy was prepared as amorphous ribbons by melt spinning. The amorphous nature of the coatings and ribbons was characterized by XRD, DSC and TEM, while XPS and AES analyses were performed to understand the origin of passivation and mode of corrosion. The corrosion behaviour of the coating was studied in H₂SO₄ and HCl solutions open to air at room temperature. Potentiodynamic polarisation and galvanic coupling tests were carried out on the substrate and the coating. It was found that the formation of Zr-, Ti- and Si-rich passive oxide layers provide a high corrosion resistance in H₂SO₄ solution while the breakdown of the passive layer by chloride ion adsorption was responsible for pitting corrosion of the Ni₅₉Zr₂₀Ti₁₆Si₂Sn₃ amorphous ribbons in HCl solution. Galvanic corrosion was the dominant corrosion mechanism for the coating/copper hybrid structure, in contrast to the Ni₅₉Zr₂₀Ti₁₆Si₂Sn₃ amorphous coating, which efficiently protected the steel substrate in the corrosive environment.     

Cu—Cr合金电极触头板铸件的熔制

含０．４％～１．０％Ｃｒ的Ｃｕ－Ｃｒ合金具有优良的导电、导热性能，铸件经热处理强化后可获得较高的综合力学性能。近年来该合金作为一种新材料被广泛地用于制作电子工业、电器设备上的电极触头板、接触环、夹持体等零件。Ｃｕ－Ｃｒ合金存在易氧化吸气、凝固范围窄、收缩较大、易形成集中缩孔等缺陷，这些铸造特性给生产优良的Ｃｕ－Ｃｒ合金铸件带来一定的困难。以采用常规的熔炼设备和造型材料熔铸出Ｃｕ－Ｃｒ合金铸件——高压大电流电极触头板为例讨论这一熔铸的工艺方法。     

锌铝超塑性合金超塑压缩试验研究

对Ｚｎ－２２％Ａｌ超塑性合金进行了等温超塑压缩试验。在相同的温度、变形速率条件下，研究了不同的变形强度与流动应力及硬度，以及在相同的温度、变形程度条件下，不同的变形速率与流动应力等的关系。     

冷热循环工艺中冷热转移速率对LY12铝合金尺寸稳定性的影响

研究了冷热转移速率对LY1 2铝合金微屈服强度和残余应力的影响。结果表明 ,提高冷热转移速率易使材料中形成稳定的位错组态 ,从而有利于提高微屈服强度 ;对于圆柱和圆环试样 ,提高冷热转移速率不利于降低残余应力。分析认为 ,冷热转移速率应根据工件几何形状和尺寸进行相应调整。     

Zr－1Nb合金吸氢性能研究

研究了１３种不同加工热处理制度的Ｚｒ－１Ｎｂ合金在堆外高压釜内３６０℃、１９ＭＰａ水中的吸氢性能，对其影响因素和吸氢机理进行了分析，并讨论了吸氢动力学，建立了吸氢动力学方程，计算了吸氢动力学参数。     

欧美对我国镁出口反倾销的现状分析及对策

分析了国际、国内镁业现状及国际市场对我国镁出口的反倾销的原因 ,提出了我国镁业应付反倾销的对策及发展方向     

稀土对ZA27合金阻尼性能的影响

研究了稀土对ZA27合金阻尼性能的影响规律。结果表明：稀土变质可提高ZA27合金的阻尼性能，经稀土变质后的试样，其内耗是未变质的试样的1．4倍。ZA27合金为发挥其阻尼作用，在频率高于70Hz时，效果明显，且经稀土变质后的试样强迫振动衰减效果比未变质的试样强。     

挤压变形对Mg95Zn4.3Y0.7合金组织和性能的影响

研究了在250℃、不同挤压比下挤压变形对Mg95 Zn4.3 Y0.7合金组织及性能的影响。结果表明，Mg95 Zn4.3 Y0.7经过挤压变形后，合金中晶界处的共晶相破碎，弥散分布至晶粒内部，并且晶粒显著细化。同时，随着挤压比的增大，晶粒细化程度增加，合金的力学性能单调增加。当挤压比为16时，合金晶粒尺寸为5-8μm，抗拉强度为288.9MPa，显微硬度HV值为117.8。