铝活塞余热淬火和自然时效的应用研究

图 1所示的活塞试件 ,在开型时间为 5 0s～ 5 5s时 ,其表面温度为 (4 90± 5 )℃ ,可满足淬火要求。自然时效时间为 2 4天时 ,其机械性能可达到国标技术要求。这种新工艺有明显的经济效益。     

非晶Sm5Fe74.3Nb1.5Si11.7B4.5C2.5Cu0.5合金经预退火后的晶化动力学的DTA研究

研究了非晶Sm5Fe74.3Nb1.5Si11.7B4.5C2.5Cu0.5合金经400℃，保温10min预退火后的晶化动力学。结果表明；该合金的晶化相为α-Fe固溶体和Sm2Fe17Cx金属间化合物，两相的晶化表观激活能分别为557KJ/mol和514KJ/mol，当晶化体积分数为60%时，α-Fe相的晶化激活能达极大值；Sm2Fe17Cx相晶化激活能则随其晶化体积分数的增加而逐渐减小。     

压力对Fe－29wt％Ni合金超细微粒特性的影响

利用蒸发冷凝法，制备了不同平均粒径的Ｆｅ－２９ｗｔ％Ｎｉ合金超细微粒。在不同压强下，将超细微粒压制成片。随压强增大，马氏体体积分数和比饱和磁化强度σｓ明显增大，而矫顽力Ｈｃ呈线性下降。压力效应与平均粒径ｄ大小密切相关     

Direct electroless Ni-P deposition on AM50 magnesium alloy from sulfate bath

A bright electroless Ni-P deposition on AM50 magnesium alloy in a sulfate plating bath was proposed by using direct plating process with non-chromate pretreatment. The electroless Ni-P plating on AM50 magnesium alloy has an admirable appearance and good adhesion. The results indicate that the electroless Ni-P deposition with non-chromate pretreatment has better adhesion than that of zinc immersion coating. Anodic polarization curves indicate that the electroless Ni-P deposition obtained from the sulfate bath has similar corrosion-resistance to that obtained from basic nickel carbonate bath. The deposition process generates less pollutant by a non-chromate plating bath and is suitable for the magnesium alloys manufacture because of its low cost. The hardness of the electroless Ni-P plated AM50 is about HV 720.6 and HV 969.7 after heat treatments at 180℃ for 2 h. The wear resistance of Ni-P plated magnesium alloy specimens is about 5 to 9 times as high as that of bare magnesium alloys.     

热强钛合金BT25组织与性能

介绍了前苏联航空发动机用热强钛合金（或高温钛合金）BT25的发展概况，并对BT25合金的成分特点、热处理强化优点等做了进一步阐述，给出了退火状态下的物理性能，在说明热强钛合金微观组织与力学性能关系的基础上给出了BT25合金的各种力学性能。     

Homogeneous Plastic Flow of Fully Amorphous and Partially Crystallized Zr_(41.2)Ti_(13.8)Cu_(12.5)Ni_(10)Be_(22.5) Bulk Metallic Glass

The homogeneous plastic flow of fully amorphous and partially crystallized Zr(41.2)Ti(13.8)Cu(12.5)Ni(10)Be(22.5) bulk metallic glass (Vitl) has been investigated by compression tests at high temperatures in supercooled liquid region. Experimental results show that at sufficiently low strain rates, the supercooled liquid of the fully amorphous alloy reveals Newtonian flow with a linear relationship between the flow stress and strain rate. As the strain rate is increased, a transition from linear Newtonian to nonlinear flow is detected, which can be explained by the transition state theory. Over the entire strain rate interval investigated, however, only nonlinear flow is present in the partially crystallized alloy, and the flow stress for each strain rate is much higher. It is found that the strain rate-stress relationship for the partially crystaltized alloy at the given temperature of 646 K also obeys the sinh law derived from the transition state theory, similar to that of the initial homogeneous amo     

LF6铝合金的超塑性／扩散连接组合工艺试验及理论研究EI

本文研究了ＬＦ６铝合金的超塑性／扩散连接组合工艺，用变形和再结晶的方法细化晶粒，成功地进行了ＳＰＦ／ＤＢ工艺试验，利用电子探针观察了扩散连接接头的界面微观区域，并从机理上分析了金属的超塑性／扩散连接两种工艺之间的内部联系及其金属学行为。     

铸造铝合金(ZL109)激光表面处理

采用功率为2kW级CO_2连续可调式横流激光光源,对不同涂层的ZL109试样表面进行了激光熔凝的实验研究。     

The influence of NaCl and CO2 on the atmospheric corrosion of magnesium alloy AZ91

The influence of NaCl and CO₂ on the atmospheric corrosion of magnesium alloy AZ91 is studied in the laboratory. Samples were exposed under carefully controlled air and flow conditions; the relative humidity was 95%, the temperature was 22.0°C and the concentration of CO₂ was < 1 ppm or 350 ppm. Different amounts of sodium chloride (0–70 μg/cm²) were added before exposure. The corrosion products were analyzed by gravimetry, ion chromatography, X‐ray diffraction and scanning electron microscopy. Mass gain and metal loss results are reported. The combination of high humidity and NaCl is very corrosive towards AZ91. However, the NaCl‐induced corrosion is inhibited by ambient concentrations of CO₂. Exposure in the absence of CO₂ gives rise to heavy pitting, with brucite, Mg(OH)₂, being the dominant corrosion product. In the presence of CO₂ a layer of hydrated magnesium hydroxy carbonate, Mg₅(CO₃)₄(OH)₂ · 5 H₂O forms. A tentative corrosion mechanism is presented that explains the behavior in the two environments.     

离子注入对铁及其低合金、铝及其合金耐腐蚀性能的影响

离子注入对金属腐蚀行为的研究已达30年．研究结果表明离子注入对改变金属表面成分和表面性能是极为有效的技术．本文概述了离子注入对铁及其低合金、铝及其合金的腐蚀电化学行为的影响．涉及的注入离子达十余种。