氯代四官能耐热环氧树脂复合材料性能研究

在确定了氯代四官能环氧/DDS树脂体系成型工艺的基础上,对浇注体的力学性能、复合材料的力学性能和耐热性进行了分析。结果表明,固化工艺为130℃/1h+150℃/2h+175℃/2h时,浇铸体具有较好的力学性能,高温力学性能保持率和较高的玻璃化温度tg和热分解温度,产品性能与国外同类产品相当。     

聚氨酯弹性体复合抗磨环的研制

介绍了聚氨酯弹性体复合抗磨环的设计及制作过程，并将该产品应用于挖泥船泥泵中。经过试验证明，该产品比传统的钢质抗磨环耐气蚀、耐磨损，使用寿命可延长3倍以上。     

Si加入量对Si_3N_4-SiC复合材料性能的影响

固定其他组分配比不变,仅改变配方中Si粉加入量即Si粉从10％增加到60％,经过准静态氮化法反应烧结制得Si3N4——SiC复合材料,并对其进行力学性能、XRD和SEM检测,实验结果显示:随着Si加入量的增加,复合材料的强度逐渐增大,而密度却呈现减小趋势,生成的Si3N4-中β-Si3N4含量增加,形成的网络结构的致密度也相应增大,但β-Si3N4晶粒减小。     

Effects of Admixtures on the Anti—oxidation Property of MgO／Si3N4 Composite Refractory

The effect of the admixtures of Al and Si metals and B4C and MgAlON compounds on the oxideation of MgO/Si3N4 composite refractory has been studied,which is a promising carbon free refractory for steel-making applicatlon.The four kinds of admixtures can be used as anti-oxidants for Si3N4,ut the mixture of Al and Si achieved the best result .The mixture can not only play the role as antioxidant,but also assist the sintering process and help form dense sintering layer,improving the property of the composite.     

基于复合左右手传输线结构的新型微带天线

基于复合左右手传输线结构的零阶谐振理论,提出了一种新型双层结构的微带天线,仿真结果表明该天线具有比单层微带天线更小的尺寸。研究了天线各结构参数对天线特性的影响,并对各参数进行了优化仿真。仿真结果表明该天线具有全向辐射特性,与传统微带天线相比,该天线具有体积小的特点。     

SCM晶须/高密度聚乙烯复合材料力学性能的研究

研究了硅钙镁晶须(SCM晶须)／高密度聚乙烯(HDPE)复合材料的力学性能。实验结果表明：随着SCM晶须用量的增加，复合材料的拉伸强度、弯曲强度、弯曲模量显著提高而缺口冲击强度稍有降低；利用改性聚乙烯作增容剂，可以改善基体树脂与SCM晶须的界面结合性，有助于力学性能的提高。     

牙科用氧化锆/氧化铝/玻璃复合材料的研制

采用熔融渗入法制备了牙科用氧化铝基玻璃复合材料，为了提高材料的强度和韧性，在氧化铝预制体中加入一定量的氧化锆。借助sEM和XRD对材料的微观结构和晶相组成进行了研究。研究结果表明：4Y—TZP的引入量为15wt％，掣合材料的抗折强度可达到182MPa，氧化铝基体经玻璃渗透以后，抗折强度等性能明显改善，而且材料化学性能稳定，色泽逼真，是一种较理想的牙科用材料。     

基于中心组合实验设计的注塑成型过程优化

从统计过程控制（SPC）的观点出发，在中心组合实验设计方案的基础上，对注塑成型过程的过程参数进行优化，对参与实验的因素及各因素的交互作用对注塑制品质量特性的影响进行定量非线性分析，获得制品质量与注塑过程参数之间的非线性回归方程，寻找出对制品质量特性影响较大的因素，找出它最有利于关键指标的水平，并对其加以统计控制从而达到优化过程的目的。     

The permeation resistance of interface and the directional dependence of permeation in plasma-grafted composite membranes

Composite membranes were prepared by grafting plasma-polymerized films onto the surface of nonporous poly (dimethylsiloxane) films. Gas permeabilities of the composite membranes were measured at 35°C, 1 atm for N₂, 0₂, CO₂ and CH₄. The permeation properties of the composite membrane was analyzed using the series resistance model. There was a great interfacial resistance to CH₄ permeation through the composite membrane. The interfacial resistance was negligible for the other gases. The interfacial resistance seems to be a result of an interfacial layer caused by the interaction between the bulk two layers. For CH₄ gas, the permeation rate through the composite membrane was affected by the direction of flow. The directional dependence was negligible for the other gases.     

Electrodeposition of smooth and adherent film of polypyrrole on lead electrode

Electropolymerization of pyrrole on lead substrate electrode was studied. Due to electrochemical activity of Pb in acidic media, this process is only possible at basic pHs. For this purpose, electropolymerization process was performed in an aqueous solution of Na₂SO₄ with pH 12. Potentiodynamic cycling shows the Pb oxidation at the first cycles. In subsequent cycles, polypyrrole film grows on the oxidized lead substrate. Of course, as the passive film is highly porous, a composite of polypyrrole/PbSO₄ is formed in the first layers. However, subsequent cycling leads to the formation of pure polypyrrole film. According to this structure and strong connection of the polymer film to the substrate surface via this composite layer, the polypyrrole film deposited on the lead surface has enhanced mechanical stability. AFM measurements showed peculiar smoothness of both composite and lateral polypyrrole films. This synthesis approach is of particular interest for the preparation of highly stable polymer films and fabrication of supercapacitors with a polymer/PbSO₄ conductive structure.