Analysis of crack tip plasticity for microstructurally small cracks using crystal plasticity theory

Crack tip plastic zone sizes and crack tip opening displacements (CTOD) for stationary microstructurally small cracks are calculated using the finite element method. To simulate the plastic deformation occurring at the crack tip, a two-dimensional small strain constitutive relationship from single crystal plasticity theory is implemented in the finite element code ANSYS as a user-defined plasticity subroutine. Small cracks are modeled in both single grains and multiple grains, and different crystallographic conditions are considered. The computed plastic zone sizes and CTOD are compared with those found using conventional isotropic plasticity theory, and significant differences are observed.     

Characterisation of plasticity-induced closure--crack flank contact force versus plastic enclave

This paper presents some results from a totally new and powerful fusion between automated, digital photoelastic techniques and mathematical analysis of a crack experiencing closure. In essence, real-time photoelastic stress field data is acquired and fitted to a Muskhelishvili complex potential model of a loaded crack experiencing closure. The fit entails optimisation of multiple variables via a memetic algorithm, which combines a genetic algorithm and a local search. From observations made in this work, it is proposed that the plastic enclave around a crack tip will shield the crack from the full influence of the applied stress field. Furthermore, the effects of this ‘back stress’ are overcome by the applied tensile load in a way that, often, cannot be readily correlated with crack contact length, wake contact force, or with compliance.     

RETARDATION AND REPAIR OF FATIGUE CRACKS BY ADHESIVE INFILTRATION

Abstract— This paper presents results which demonstrate that polymeric filler materials, such as low-viscosity epoxies, can be vacuum-infiltrated into fatigue cracks in 7050 aluminium alloy to produce significant levels of fatigue crack retardation. It was found that the main test variable affecting the degree of retardation was the stress level at which the adhesive was introduced and cured. Two infiltrated adhesives were tested.
Infiltration at 0% (of the original) peak fatigue stress level produced negligible retardation, while infiltration at the 80% stress level produced about 300% increase in fatigue life for one adhesive and 3000% for the other adhesive. For the highest infiltration stress level both crack-face wedging and adhesion contributed initially to the retardation, but the adhesive component ceased after a crack grew through the adhesive to the original crack tip position. The results are discussed in terms of the applicability of the technique to highly-stressed aircraft components.     

How to study drying shrinkage microcracking in cement-based materials using optical and scanning electron microscopy?

Three different ‘destructive’ microscopy methods were tested on their ability to show drying shrinkage microcracks on a specimen cross-section. The first two were methods in which the microcracks were impregnated with a fluorescent epoxy and examined with fluorescence microscopy. In one method, the impregnation was applied before making the cross-section and in the other after making the cross-section. In the third method, the sample was kept wet constantly and examined in an environmental scanning electron microscope (ESEM). It was concluded that the method in which the dried specimen was impregnated before making the cross-section was the most reliable method to record drying shrinkage microcracks. With this method, it was possible to impregnate the complete drying shrinkage microcrack pattern in the studied cement-based materials from the surface, and there was no risk of recording microcracks introduced by sample preparation.     

Low-cycle fatigue behavior of Sn-Ag, Sn-Ag-Cu, and Sn-Ag-Cu-Bi lead-free solders

Low-cycle fatigue (LCF) tests on as-cast Sn-3.5Ag, Sn-3Ag-0.5Cu, Sn-3Ag-0.5Cu-1Bi, and Sn-3Ag-0.5Cu-3Bi solders was carried out using a noncontact strain-controlled system at 20°C with a constant frequency of 0.1 Hz. The addition of Cu does not significantly affect the fatigue life of eutectic Sn-Ag solder. However, the fatigue life was significantly reduced with the addition of Bi. The LCF behavior of all solders followed the Coffin-Manson relationship. The fatigue life of the present solders is dominated by the fracture ductility and can be described by the ductility-modified Coffin-Manson’s relationship. Steps at the boundaries of dendrite phases were the initiation sites for microcracks for Sn-3.5Ag, Sn-3Ag-0.5Cu, and Sn-3Ag-0.5Cu-1Bi solders, while for Sn-3Ag-0.5Cu-3Bi solder, cracks initiated along both the dendrite boundaries and subgrain boundaries in the dendrite phases. The linking of these cracks and the propagation of cracks inside the specimen occurred both transgranularly through eutectic phases and intergranularly along dendrite boundaries or subgrain boundaries.     

高强度船板纵裂纹的成因及预防

针对高强度船板纵裂纹轧后退废过高的现状，分析原因并优化冶炼、连铸工艺及操作，有效地降低高强度船板的退废率。     

含能材料的燃烧转爆轰研究

本文综述了近年来在可燃气体、推进剂和炸药内，燃烧转爆轰问题的研究成果。对气、固与混合相含能材料的燃烧转爆轰机制、理论研究方法以及目前还存在的问题，作了较系统的介绍与探讨。     

控制连铸板坯星状裂纹的对策

回顾重钢七厂连铸板坯星状裂纹导致轧制钢板表面产生龟裂缺陷、以及对钢坯产生星裂的机理的认识过程,借助国外在这方面的研究成果进行对比分析,认为控制板坯星裂的最重要技术措施是采用"结晶器软冷却”工艺、以及控制钢的铁素体势和铜当量。     

ATP-Independent Initiation during Cap-Independent Translation of m6A-Modified mRNA

The methylation of adenosine in the N⁶ position (m⁶A) is a widely used modification of eukaryotic mRNAs. Its importance for the regulation of mRNA translation was put forward recently, essentially due to the ability of methylated mRNA to be translated in conditions of inhibited cap-dependent translation initiation, e.g., under stress. However, the peculiarities of translation initiation on m⁶A-modified mRNAs are not fully known. In this study, we used toeprinting and translation in a cell-free system to confirm that m⁶A-modified mRNAs can be translated in conditions of suppressed cap-dependent translation. We show for the first time that m⁶A-modified mRNAs display not only decreased elongation, but also a lower efficiency of translation initiation. Additionally, we report relative resistance of m⁶A-mRNA translation initiation in the absence of ATP and inhibited eIF4A activity. Our novel findings indicate that the scanning of m⁶A-modified leader sequences is performed by a noncanonical mechanism.