薄膜磁头磁轭制备工艺研究

本文重点讨论了用不同的工艺方法来制备薄膜磁头中的关键元件-磁轭。采用多次光刻的方法克服湿法工艺中磁性膜NiFe层的侧向钻蚀问题，从而实现对磁轭几何尺寸的精确控制，并对几种工艺方法的优缺点作了比较详细的分析。     

用于多种组装技术的厚膜导体复合结构

厚膜导体Ｐｄ－Ａｇ／Ａｕ、Ｐｔ－Ｐｄ－Ａｕ／Ａｕ平面复合结构，Ｐｄ－Ａｇ／Ａｕ立体复合结构可使多种组装技术相互兼容。立体复合结构还可有效地降低导体线电阻，减少线损耗。而且，其超声键合性尤佳     

Photo-reversible Reaction in Polymer Langmuir-Blodgett Films

Preparation of photoreactive Langmuir-Blodgett (LB) films was carried out using polymers/oligomers prepared from long-chain dialkyl esters of di-and tetra-olefins and having cyclobutane rings in the main chain. These polymers/oligomers formed stable monolayers on a water surface when mixed with arachidic acid. These monolayers could be deposited onto a substrate successfully forming Y-type films. The oligomer LB films were polymerized on irradiation. The polymer LB films showed a photo-reversible process between polymers and oligomers, depending on wavelength of the irradiating light. On the basis of spectral data and molecular weight change, this behaviour was found to be caused by cleavage and formation of cyclobutane rings.     

Modification of poly(N-vinyl-carbazole) thin films by bromine doping

Poly(N-vinyl-carbazole) (PVK) thin films doped with bromine has been studied by scanning electron microscopy, X-ray diffraction, infrared absorption, X-ray photoelectron spectroscopy (XPS), electron spin resonance (ESR), optical transmission (visible, near ultra violet) and conductivity measurements. The polymer has been doped at room temperature and at 373 K. It is shown by ESR, XPS and optical measurements that a charge transfer complex (CT-complex) is formed between PVK and Br. However, if some bromine acts as dopant of the polymer there is another bromine contribution, which corresponds to bromine covalently bonded to PVK and some only adsorbed. It is also shown by ESR that there is not only polymer doping by bromine but also some partial polymer degradation. Therefore, it can be said that the optimum doping condition of PVK thin films with bromine has been shown to be room temperature post-doping.     

旧工业建筑的再利用

旧工业建筑与其他旧建筑物相比,具有建筑主体结构坚固,空间高大灵活;体量大,拆除或新建对环境造成的影响大;具有其独特的设计理念和美学价值等特点,从而成为旧建筑再利用过程中一种重要的建筑类型。 本文通过对101厂房再利用案例设计过程的分析,对旧工业建筑再利用的目标、更新程序、方式、策略等方面进行具有可操作性和推广性的探索。     

定电流对LED的重要性

高功率超高亮度LED已经开始大量应用.要实际体现LED(尤其是高功率超高亮度LED)的优点,采用定电流驱动方式必要条件之一.     

Study on Oxygen-Sensing Properties of LaNiO3 Thin Films

The synthesis of rare-earth perovskite-type composition thin films of LaNiO₃ by means of the inorganic-sol-gel (ISG) method was studied. The structural stability under high temperature in reducing atmospheres and the oxygen-sensitivity mechanism of the LaNiO₃ thin films were examined. It is shown that under the experimental conditions, LaNiO₃ decomposes and the valance states of nickel are +2 and +3.     

(Fe_(0.86)Zr_(0.033)Nb_(0.033)B_(0.068)Cu_(0.01))_x(Al_2O_3)_(1-x)颗粒膜的霍耳效应

用磁控溅射方法制备了系列 (Fe0 .86 Zr0 .0 33Nb0 .0 33B0 .0 6 8Cu0 .0 1 ) x(Al2 O3) 1 -x颗粒膜样品 ,体积百分比x从 0 .3 3～ 0 .63 ,样品厚度约为10 0nm。室温下在Fe0 .86 Zr0 .0 33Nb0 .0 33B0 .0 6 8Cu0 .0 1 体积百分比x =0 .43时得到 17.5 μΩ·cm的最大饱和霍耳电阻率 ,比纯铁磁金属提高了 3～ 4个量级。对其磁性和微结构进行了研究 ,样品霍耳电阻率随外场的变化曲线 ρxy～H与磁场平行于膜面时的磁化曲线M～H有相似性 ,说明霍尔电阻率 ρxy与磁化强度M相关。样品电阻率 ρxx随金属体积百分比x的减小而增加 ,在x =0 .43附近发生突变 ,从金属导电变为绝缘体。根据微结构和输运性质对可能的机制进行了探讨     

石英晶体监控法镀制高精度光学薄膜

讨论了石英晶体监控法在光学薄膜镀制过程中的应用原理。通过与常规的光学监控法镀制的膜层相比较．证实了石英晶体监控法有助于提高光学薄膜的光学品质。试验表明所镀膜层的光学性能优异，在光通信和激光器等领域具有广阔的应用前景。     

Butyltin Species and Inorganic Tin in Water and Sediment of the Detroit and St. Clair Rivers

Water and sediment samples from 29 locations in the Detroit and St. Clair rivers were analyzed for the highly toxic tri-n-butyltin (Bu₃Sn⁺) species and for the less toxic di-n-butyltin (Bu₂Sn²⁺) and n-butyltin (BuSn³⁺) species and inorganic tin. In general, locations sampled in the St. Clair River were less contaminated with butyltin species than those in the Detroit River. Inorganic tin and BuSn³⁺ were detected in over 90% of all subsurface water samples, while Bu₂Sn²⁺ and Bu₃Sn⁺ were detected in 45 and 28% of the same samples, respectively. The highest concentration ofBu₃Sn⁺ in subsurface water, 5.9 × 10^?10 mol Sn/L, was at the mouth of the Ecorse River, a tributary of the Detroit River. The three butyltin species and inorganic tin were also detected in 23–46% of all sediment samples. The highest concentrations of Bu₃Sn⁺ in sediment were found close to the mouths of the River Rouge, another tributary of the Detroit River, and the Ecorse River, and were 6.2 × I0^–7 and 1.7 × I0^–7 mol Sn/kg dry weight, respectively, for the top 2 cm of sediment.