LLDPE-g-GMA对PA66/PE性能影响的研究

研究了LLDPE—g—GMA(甲基丙烯酸缩水甘油酯)对PA66／PE相容性的影响。结果表明LLDPE-g-GMA是PA66／PE合金良好的反应型增容剂，对于PA66／PE合金，LLDPE—g-GMA的加入使合金的拉伸强度、弯曲强度、Izod缺口冲击强度有明显提高。但刚性和耐热性略有降低，并且DMA谱图证实了LLDPE—g-GMA对PA66／PE的反应增容作用，计算出了PA66／PE玻璃化转变活化能。     

低压片状模塑料增稠工艺研究

采用氧化镁为增稠剂、结晶树脂以粉料形式加入而降低片材热模内粘度的工艺，改进了对低压片状模塑料的增稠方法。结果表明：采用此工艺，设备不需要加热，增稠符合传统SMC增稠曲线；片材在模腔内有较低的粘度，适宜于低压成型。     

抗静电粉末涂料的制备

简述了抗静电粉末涂料的制备机理及铝粉、氧化镁、二氧化钛和抗静电助剂添加量对涂料性能的影响，并简述其应用。     

PA-1010/ABS合金的性能研究

研究了以自制的马来酸酐 (MAH)接枝改性ABS(MABS)作为PA 10 10 /ABS增容剂所形成的PA 10 10 /ABS合金的性能。研究结果表明 ,随ABS中马来酸酐接枝量的上升 ,PA 10 10 /ABS合金的冲击强度提高 ,保持PA 10 10与ABS用量在某一恰当配比范围内 ,可得到冲击强度高 ,维卡软化温度较高的合金。     

Electrochemical micromachining of nitinol by confined-etchant-layer technique

The confined etchant layer technique has been applied to fabricate complex three-dimensional microstructures on nitinol for the first time. HF and HNO₃ were locally and simultaneously electrogenerated at the mold surface to etch a nitinol workpiece. NaOH was used as an efficient scavenger to confine the etchant close to the mold. Cyclic voltammetry was employed to study the electrochemical behavior of a Pt electrode in the etching solution in order to choose an appropriate potential for etchant generation on the mold. The thickness of the confined etchant layer was estimated to be several micrometers by inspecting the deviation of the sizes of the etched spots from the sizes of those on the microelectrode. Thus, the composition of the electrolyte could be optimized for better etching precision. By optimizing the composition of the electrolyte, complex microstructures on a Pt-Ir mold bearing the logo “XMU” of Xiamen University were successfully fabricated on nitinol. The etched patterns were approximately negative copies of the mold, and the precision of duplication could easily reach the micrometer scale.     

Performance and stability of Pt-based ternary alloy catalysts for PEMFC

Carbon-supported Pt-based ternary alloy electrocatalysts were prepared by incipient wetness method in order to elucidate the origin of the enhanced activity of oxygen reduction reaction in PEMFC. To measure the catalytic activity and stability of the cathode alloy catalysts (electrodes containing Pt loading of 0.3 mg/cm², 20 wt.% Pt/C, E-TEK), the I-V polarization curves were obtained. All alloy catalysts showed higher performances than Pt/C. It can be concluded that as platinum formed alloys with transition metals, the electronic state of Pt and the nearest neighbor Pt-Pt distance changes, which significantly influence the electrocatalytic activity for oxygen reduction.Long-term stability test was performed with the Pt₆Co₁Cr₁/C alloy catalyst for 500 h. According to XPS analysis, the lower oxide component with Pt₆Co₁Cr₁/C electrocatalyst provides a large portion of platinum in metallic species in the electrocatalyst and it seems to be mainly responsible for its enhanced activity towards oxygen reduction.     

Preparation of nano-sized silicon carbide powder using thermal plasma

Nano-sized silicon carbide (SiC) powder was prepared by thermal plasma process using silicon tetrachloride (SiCl₄) and methane (CH₄). The synthesized powder was characterized by X-ray diffraction pattern, scanning electron microscopy, transmission electron microscopy, FT-IR spectroscopy and particle size analyzer. The powder was dominated by β-SiC including some of α-SiC and free carbon species. The quality of the powder was varied with process conditions such as the molar ratio of H/Si and C/Si, and collecting positions. It was known that the conversion to SiC was mainly affected by the addition of hydrogen gas because it promoted the decomposition and reduction of SiCL. CH₄ was easily decomposed to carbon species for the formation of SiC as well as removal of impure oxygen, but excessive carbon suppressed the formation of crystalline SiC and resulted in the solid carbon contamination. The optimum ratio of H/Si was approx. 26 and that of C/Si was 1.1. For collecting positions, the powder collected at the vessel and filter was preferable to that at the reaction tube. The average size of the powder synthesized was estimated to be below 100 nm and uniform in distribution.     

PPO/PA合金的研制

比较了三条技术路线、PPO／PA质量比、各种抗冲击剂对PPO／PA合金性能的影响。应用FTIR．Molau实验、DSC曲线证实了改性反应原理及增容作用。结果表明：在双螺杆挤出机中，聚苯醚(PPO)与马来酸酐(MAH)接枝反应，然后与聚酰胺(PA66)、SEBS挤出共混，制成的PPO／PA合金，抗冲击性能高。     

EVA／EPDM／PVC三元聚合物合金软质泡沫体的制备及其在复合衬垫中的应用

采用物理共混以及化学交联模压发泡成型工艺制备聚乙烯－醋酸乙烯酯（ＥＶＡ）／乙丙橡胶（ＥＰＤＭ）／聚氯乙烯（ＰＶＣ）三元聚合物合金软泡沫体，并制成贴布复合衬垫。讨论了该体系的相容性，动态共交联与发泡的适配，以及贴布复合，造型等问题，结果表明，该衬垫可完合替代国外同类先进产品。     

PPO/PP及PPO/PA合金

PPO与PA,PP是不相容的,制造PPO PA及PPO PP合金需要提高合金中两组分的相容性。本文叙述改善相容性的原理和途径、两种合金的特点及其重要性能。