Preparation and characterization of oxygen deficient perovskites,BaBiO3−x

Oxygen nonstoichiometry in the distorted perovskite BaBiO₃ has been studied by thermogravimetric analysis using controlled oxygen pressures. Three distinct regions of nonstoichiometry are observed with composition ranges which narrow as the temperature is lowered. Samples isolated from each region were shown by powder X-ray diffraction to retain the perovskite subcell but show different types of framework distortion. Low temperature reoxidation of the oxygen deficient phases is also described.     

催化氧化法合成脂肪醇醚羧酸盐的研究进展

详细介绍了氮氧自由基催化氧化法和贵金属催化氧化法合成脂肪醇醚羧酸盐。氮氧自由基催化时,反应温度20～60℃,反应时间3～6 h,得到酸型产品。贵金属催化剂中,钯的催化活性比铂高。贵金属催化时,加入铅、铋等助催化剂,并以活性炭为载体,碱性条件下于50～90℃反应2～6 h,得到盐型产品。在适当的条件下,这两种方法均可使醇醚转化率达95％,选择性达90％以上。     

乙烯直接氧化合成乙酸

用常规固定床反应器考察了Pd-SiW12/SiO2催化剂还原条件对乙烯直接氧化合成乙酸催化性能的影响。催化剂用H2在200－300℃还原后Pd 的分散度较高，其催化活性远高于肼在液相中还原的催化剂，在乙烯气相氧化合成乙酸反应的原料气中，适量1，2－二氯乙烷的存在有助于提高乙酸的选择性和时空产率，初步考察了Pd-Se-SiW12/SiO2催化剂连续206h运转的稳定性，结果表明，催化剂中Pd晶粒的长大和硅钨酸的流失是造成催化剂失活的主要原因。     

重油接触裂解制乙烯的HCC工艺研究

重油裂解制乙烯的HCC技术采用与FCC类似的“反应—再生”工艺技术,利用重油直接裂解制乙烯,兼产丙烯、丁烯和轻质芳烃,既可扩大乙烯的原料的来源,又可降低生产成本。HCC工艺的乙烯产率可达19%～27%,总烯烃产率大于50%。     

聚酯新型催化剂乙二醇锑的工业应用

介绍了国产新型催化剂惭二醇锑在洛阳石油化工总厂聚酯装置上的使用情况，结果表明：乙二醇锑催化剂活性高、易溶解；以乙二醇锑催化剂合成的聚酯产品质量稳定，纺丝时的加工性能明显得到改善。     

甲醇氧化制甲醛铁钼催化剂的研究

采用共沉淀法制备甲醇氧化制甲醛无载体铁钼催化剂,并考察了催化剂制备老化条件、焙烧温度、外型尺寸以及活性测试反应温度、空速对催化剂性能的影响。该催化剂在280~300℃、气空速7000 h-1~8000 h-1、进料φ(甲醇)为5.5%的下,可获≥98%的甲醇转化率,≥92%的甲醛选择性和≥90%的甲醛产率。催化剂活性高,强度好,性能稳定。     

抽余C_4烃中异丁烯催化逆流水合制叔丁醇

采用大颗粒离子交换树脂催化剂,在φ100mm×10m的反应器中进行了异丁烯催化逆流水合制叔丁醇的中间试验。考察了反应温度、水油体积比和抽余C4烃的流速等对异丁烯转化率的影响。试验结果表明,异丁烯催化逆流水合制叔丁醇的适宜操作条件为:反应温度80~90℃,水油体积比为4~5,抽余C4烃的流速为0.45~0.55mm/s。在此条件下,异丁烯的转化率可达88.8%。工业装置运转结果表明,异丁烯转化率大于75%。     

Long-term stability of an Au/Al2O3 catalyst prepared by incipient wetness in continuous-flow glucose oxidation

A 0.3% Au/Al₂O₃ catalyst prepared by the incipient wetness (IW) method was investigated in the continuous-flow liquid-phase glucose oxidation. Therefore, a continuous stirred tank reactor (CSTR) system equipped with an ultrasonic separator was used. The continuous-flow glucose oxidation was carried out at 40 °C, pH 9 and 1 bar oxygen partial pressure. Residence time and glucose concentration were varied. The IW gold catalyst showed very high activity and selectivity to gluconic acid within its 110 days of operation and, thus, an excellent long-term stability. Even after severe microbial contaminations of the catalyst, its activity could be completely restored by in situ regeneration with 2-propanol.     

担载型含稀土三组份体系在二氧化碳甲烷化反应中的催化性能

用浸渍法制备了一系列氧化锆担载的含稀土Ⅷ族金属催化剂，对其在二氧化碳甲烷化过程中的催化活性作了研究，并用漫反射紫外可见光谱，ＦＴＩＲ等手段对催化剂作了表征。结果表明，含稀土新型催化剂具有催化活性高，目标产物选择性好等优点；稀土主要以氧化物形式存在于催化剂表面，参与对氢及表面含碳物种的吸附及活化；含稀土三组份催化剂的活性与所添加稀土三价离子的４ｆ电子数有关。     

锌空气电池空气电极催化材料的研究

采用将Li2CO3,电解二氧化锰(EMD)和Co(NO3)2·6H2O混合进行高温固熔反应的合成方法,制备了1种尖晶石型金属氧化物催化材料LiMn2-xCoxO4。通过电化学测试(极化曲线、放电曲线)、X射线衍射分析(XRD)以及扫描电镜(SEM)等方法对电极的微观结构和性能进行了研究。实验结果表明,以LiMn1.95Co0.05O4为催化材料的气体扩散电极具有最好的综合电化学性能。其0.9V极化电位时的最大电流密度可达210mA/cm2AA型(5号)样品电池以100mA电流恒流放电,容量可高达4439mAh。