低合金高强度钢的微观组织和疲劳裂纹扩展行为

用透射电镜观察了３０ＣｒＭｎＳｉＮｉ２Ａ钢等温的微观组织，疲劳裂纹扩展行为、裂纹尖端塑性区和位错结构，结果表明，等温状态组织由马氏体和贝氏体组成。在一个奥氏体晶粒内一般存在四个板条领域、裂纹尖端的塑性区内存在主位错带，疲劳断裂的基本组织单元为板条晶或板条束。裂纹遇到板条束界时方向发生较大偏斜。     

Failure analysis of a wire rope

Wire ropes, pulleys, counterweights, and connecting systems are used for auto tensioning of contact wires of electric railways. A wire rope in one such auto tensioning system suffered premature failure. Failure investigation revealed fatigue cracks initiating at nonmetallic inclusions near the surface of individual wire strands in the rope. The inclusions were identified as Al-Ca-Ti silicates in a large number of stringers, and some oxide and nitride inclusions were also found. The wire used in the rope did not conform to the composition specified for AISI 316 grade steel, nor did it satisfy the minimum tensile strength requirements. Failure of the wire rope was found to be due to fatigue; however, the ultimate fracture of the rope was the result of overload that occurred after fatigue failure had reduced the number of wire strands supporting the load.     

烷基化换热器的腐蚀失效分析和防护措施

通过对烷基化车间换热器腐蚀形貌、特征、产物、腐蚀介质、积垢、材料以及换热器流体特性的研究和分析,认为烷基化换热器的腐蚀失效主要由空泡腐蚀和湍流腐蚀引起,并提出了4项防腐蚀措施.经现场应用证明:改变设计或安排辅助管可以有效地减缓冷却管与管板结合部位的严重腐蚀.     

线加权余量法及其在正交异性板弯曲分析中的应用

利用有限差分法对控制方程和边界条件进行半离散化,使其定义在一些离散线上,然后采用加权余量法求解。这就是本文提出的线加权余量法,也可称之为有限差分-加权余量分维耦合法。文中以正交各向异性薄板弯曲平衡问题为例推导了有关具体算式,给出了数值算例,说明了本文方法的有效性。     

几种高强度钢腐蚀疲劳裂纹扩展行为的研究

本文研究了ＧＣ－４，３０ＣｒＭｎＳｉＮｉ２Ａ和３００Ｍ超高强钢的腐蚀疲劳裂纹扩展行为。考虑了环境，热处理制度，应力比和频率对裂纹扩展的影响。研究结果表明：腐蚀环境和热处理制度对疲劳裂纹扩展有显著影响。在侵蚀性环境中随频率降低，裂纹扩展大幅度上升，随应力比提高，环境影响加剧。利用扫描电镜对试样断口形貌进行了分析，并讨论了高强钢的腐蚀疲劳机理。     

结构陶瓷的高温疲劳强度衰减理论

提出了陶瓷材料疲劳强度衰减理论并由此导出了各种疲劳关系式。建立了疲劳基本方程ｄσ＿ｒ／ｄ＿ｉ＝一Ａσ（ｔ）￣ｎｔ￣（－ｍ），得出了疲劳寿命公式Ｔ＝Ｍ（σ＿０－σ）／Ａσ￣ｎ（静疲劳时Ｍ＝１，连续增载疲劳时Ｍ＝ｎ＋１，循环疲劳时Ｍ＝（ｎ＋１）／（１＋Ｒ＋Ｒ￣２＋……＋Ｒ￣ｎ），逐级加载时，并导出不同疲劳方式下疲劳寿命间的关系。同时，用多种Ｓｉ＿３Ｎ＿４材料在高温中作了论证试验，结果与理论一致。     

13SiMnNiCrMoV钢切口疲劳裂纹萌生门槛值

本文研究在13SiMnNiCrMoV 结构钢中用尖裂纹的应力强度因子来反映三点弯曲缺口试样的疲劳裂纹萌生规律。当 R=0.1,f=100Hz,试样尺寸 B×W×L=12.5×25×117mm 时,缺口名义应力幅的门槛值为Δσ_(th)=3315ρ~(0.352) MPa,0.5mm≤ρ≤5mmΔK_(th)=250ρ~(0.352) MPam~(1/2)门槛值与ρ有关。同时得到缺口裂纹萌生的循环次数 N_i 与名义应力幅Δσ、缺口曲率半径ρ的定量关系是N_i=3.98×10~(22)ρ~(1.62)/Δσ~(4.85),N_i≤10~(5.5)并讨论了(ΔK_1/ρ~(1/2))_(th)与ρ无关的结论。     

柔性纤维混凝土的疲劳特性研究

将柔性纤维掺入水泥混凝土可以大幅度提高混凝土的弯曲疲劳等路用性能,并通过试验建立了柔性纤维混凝土的疲劳方程.结果表明,柔性纤维不但能使混凝土的强度提高,更主要的是可以在重交通条件下,可成倍地提高混凝土的弯曲疲劳寿命.     

人工神经网络技术在板料激光弯曲中的应用

基于人工神经网络基本理论,建立在板料激光弯曲中预测材料表面最高温度、弯曲角度的BP网络模型。借助于MATLAB仿真软件中的神经网络工具箱作为开发平台,将试验样本数据和经过试验验证的数值计算结果作为补充的样本数据用于BP网络的训练,利用训练好的BP网络对非线性的样本数据规律进行拟合,实现激光加工工艺参数的优化,为实际生产和加工提供有效的依据。     

Displacement Discontinuity Method for Fracture Mechanics Analysis of Reissner Plates: Static and Dynamic

This paper is concerned with the displacement discontinuity method applied to the shear deformable plates (Reissner’s and Mindlin’s theories) with cracks subjected to static and dynamic loads. Fundamental solutions of dislocation are derived using the Fourier transform method and the Laplace transformation technique. Boundary integral equations are presented in terms of rotations/displacement on the crack surfaces. The Chebyshev polynomials of the second kind are used to evaluate the integral equations with hypersingular kernels on the crack boundaries and determine the stress intensity factors at the crack tips. Comparisons are made with other numerical solutions to demonstrate the proposed method is accurate both for static and dynamic problems.