模糊层次分析法在腐蚀影响因素分析中的应用

结合国内外对碳钢CO2腐蚀影响因素的研究成果,采用模糊层次分析法对影响输油管道 CO2腐蚀的因素进行定量分析,明确界定出这些因素对二氧化碳腐蚀影响的相对重要性(权重),为后续制定经济有效的管道内腐蚀防护措施提供了客观依据。     

Intergranular corrosion of a light aircraft aluminum alloy propeller

Examination of the wreckage of a light aircraft revealed that approximately 20 cm was missing from one tip of the aluminum alloy propeller. Fractographic and metallographic examination of the remaining portion of the propeller revealed extensive grain-boundary separation in the vicinity of the fracture, and grain edges and corners rounded by corrosion on the fracture surface. Energy dispersive X-ray analysis (EDXA) revealed fluorine on, and in the vicinity of, the fracture surface. In the ensuing litigation, it was asserted that the crash occurred because the propeller fractured in flight as the result of intergranular attack caused by the use of a fluorine-bearing cleaner.     

泡沫夹克管的防水与保温

针对辽河油田应用泡沫夹克管道的情况，从泡沫夹克管的制作和敷设施工直到设计等环节，结合泡沫夹克管防腐保温的机理，并从理论与实践相结合角度出发，提出导致泡沫夹克管腐蚀损坏的最主要原因是管道保温层漏水，进而提出了在设计和施工过程中提高泡沫夹克管质量的措施。     

On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.     

STRESS INTENSITY FACTORS AND WEIGHT FUNCTIONS FOR SEMI-ELLIPTICAL SURFACE CRACKS IN FINITE-THICKNESS PLATES UNDER TWO-DIMENSIONAL STRESS DISTRIBUTION

Abstract— A Fourier series approach is proposed to calculate stress intensity factors using weight functions for semi-elliptical surface cracks in flat plates subjected to two-dimensional stress distributions. The weight functions were derived from reference stress intensity factors obtained by three-dimensional finite element analyses. The close form weight functions derived are suitable for the calculation of stress intensity factors for semi-elliptical surface cracks in flat plates under two-dimensional stress distributions with the crack aspect ratio in the range of 0.1 ≤ a/c ≤ 1 and relative depth in the range of 0 ≤ a/t ≤ 0.8. Solutions were verified using several two-dimensional non-linear stress distributions; the maximum difference being 6%.     

核电材料在模拟反应堆环境中应力腐蚀破裂测试技术与性能评价

简要介绍了采用慢应变速率试验，Ｕ型弯曲和Ｃ形环试验等技术，分别对８００合金，３０４和３１６及３１６Ｔｉ不锈钢Ａ５３３Ｂ压力容器用多在模拟核反应堆环境中的应力腐蚀破裂敏感性性进行的试验研究的一些主要结果；并结合电化学测试和表面膜俄歇电子能谱分析结果进行了讨论。     

湿硫化氢环境下的球罐腐蚀状况分析

在湿硫化氢环境下 ,尤其储存介质中的硫化氢含量超标时 ,很容易对储存容器壳体 (含焊缝和母材 )造成硫化氢应力腐蚀或氢鼓包。作者较仔细分析了 1 0 0 0m3 丙烯球罐产生硫化氢应力腐蚀开裂和40 0m3 LPG球罐产生氢鼓包的原因。提出了此类设备在设计选材、设备制造、施工安装和使用维护等环节应注意的问题。     

合成氨中置锅炉的修复

本文在分析中置锅炉失效原因的基础上，提出了详细的修复措施，为类似情况的设备修复提供了借鉴。     

The corrosion behavior of sputter-deposited aluminum-tungsten alloys

Thin films on aluminum-tungsten alloys were prepared by co-deposition of pure aluminum and pure tungsten, each sputtered by an independently controlled magnetron source, on glass and sapphire substrates. Completely amorphous films were obtained in the Al₈₀W₂₀-Al₆₇W₃₃ composition range. Passivity and corrosion behavior of amorphous Al-W alloys were investigated in 1 M deaerated hydrochloric acid solution using polarization and impedance spectroscopy measurements and have been correlated with the properties of pure alloy components. Tungsten and sputter-deposited Al-W thin films are inherently passive materials while aluminum undergoes pitting corrosion in hydrochloric acid solution. The passive film formed at the OCP on each alloy possesses excellent electric and dielectric properties comparable to those of the isolating film on tungsten. The absolute impedance increases with increasing tungsten content in the alloy. According to electrochemical polarization measurements, alloying Al with W in solid solution significantly enhances the material's resistance to pitting corrosion by shifting the breakdown potential above 2000 mV (Al₆₇W₃₃) and lowering the corrosion rate at the OCP by more than two orders of magnitude. The most likely mechanism explaining the passivity of amorphous Al-W alloys, the Solute Vacancy Interaction Model (SVIM), involves the formation of complexes between highly oxidized solute atoms (W⁺⁶) and mobile cation vacancies, which restrict the transport of Cl⁻ through the oxide film and inhibit its breakdown in hydrochloric acid solution. The role that film stress relaxation effects and microscopic defects in amorphous Al-W films, of the some composition, and deposited on various substrates play in their corrosion resistance is discussed.