Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Preparation of a CeO2–ZrO2 based nano-composite with enhanced thermal stability by a novel chelating precipitation method

In this study, a chelating agent is introduced to prepare CeO₂–ZrO₂ nano-composite through a precipitation process. The physicochemical properties of the oxide precursors, nano composite materials are strongly dependent on the preparation method and whether a chelating agent is used. Adding an appropriate quantity of chelating agent SO₄²⁻ can facilitate thermal stability and phase structure uniformity of CeO₂–ZrO₂ mixed oxides. The calculation results showed that the Gibbs free energy of chelating complex of [ZrSO₄]²⁺ (ΔG = −127.2469 kJ/mol) is higher than the [Ce(III)SO₄]⁺ (ΔG = -29.8279 kJ/mol). The precipitation chemical potential of Zr⁴⁺ moves close to the precipitation chemical potential of Ce³⁺. The novel and low-cost chelating precipitation method can modify the homogeneity of the compounds at the atomic scale, which can offer a powerful opportunity for, and provide direction in, the design of materials with exceptional properties.     

Theoretical study of a thermoelectric-assisted vapor compression cycle for air-source heat pump applications

This paper proposes a thermoelectric-assisted vapor compression cycle (TVCC) for applications in air-source heat pump systems which could enhance the heating capacity of the system. Performances of TVCC are calculated and then compared with that of basic vapor compression cycle (BVCC). The simulation results show that when coefficients of performance (COPs) of the two cycles are almost equal, the TVCC under maximum COP condition of the thermoelectric modules still performs better than BVCC by 13.0% in heating capacity through selecting the appropriate intermediate temperature. In addition, the TVCC can also achieve an improvement of 16.4%–21.7% in both the heating COP and capacity when compared with the BVCC with an assistant electric heater that is provided with the equivalent power input of thermoelectric heat exchanger. Thus, the TVCC could be beneficial to the applications in small heat pumps if there is always need for auxiliary electric heat.     

The effect of synthesis conditions on the physicochemical properties of magnesium aluminate materials

Magnesium aluminate-based materials were prepared by applying different methods: (i) mechanochemical milling of the initial mixture of magnesium and aluminium nitrate powders (in appropriate stoichiometric amounts) followed by heat treatment at temperatures of 650 °C and 850 °C and (ii) melting of the mixture of nitrate precursors at 240 °C followed by thermal treatment at 650 °C, 750 °C and 850 °C. The effect of synthesis method on the structure and morphology of the obtained solids was studied by using various techniques such as: nitrogen adsorption-desorption isotherms, powder XRD, IR spectroscopy and SEM. It was shown that the mechanochemical milling performed before calcination procedure leads to obtaining of nanocrystalline magnesium aluminate spinel phase at lower temperature of 650 °C in comparison with the method using thermal treatment only (at 750 °C). The obtained nanomaterials exhibit mesoporous structure.     

Wetting,infiltration and interaction behavior of CMAS towards columnar YSZ coatings deposited by plasma spray physical vapor

Thermal barrier coatings (TBCs) produced by electron beam physical vapor deposition (EB-PVD) or plasma spray (PS) usually suffer from molten calcium-magnesium-alumino-silicate (CMAS) attack. In this study, columnar structured YSZ coatings were fabricated by plasma spray physical vapor deposition (PS-PVD). The coatings were CMAS-infiltrated at 1250?°C for short terms (1, 5, 30?min). The wetting and spreading dynamics of CMAS melt on the coating surface was in-situ investigated using a heating microscope. The results indicate that the spreading evolution of CMAS melt can be described in terms of two stages with varied time intervals and spreading velocities. Besides, the PS-PVD columnar coating (～100?μm thick) was fully penetrated by CMAS melt within 1?min. After the CMAS attack for 30?min, the original feathered-YSZ grains (tetragonal phase) in both PS-PVD and EB-PVD coatings were replaced by globular shaped monoclinic ZrO₂ grains in the interaction regions.     

Methyltransferase Contingencies in the Pathway of Everninomicin D Antibiotics and Analogues

Everninomicins are orthoester oligosaccharide antibiotics with potent activity against multidrug-resistant bacterial pathogens. Everninomicins act by disrupting ribosomal assembly in a distinct region in comparison to clinically prescribed drugs. We employed microporous intergeneric conjugation with Escherichia coli to manipulate Micromonospora for targeted gene-replacement studies of multiple putative methyltransferases across the octasaccharide scaffold of everninomicin effecting the A₁, C, F, and H rings. Analyses of gene-replacement and genetic complementation mutants established the mutability of the everninomicin scaffold through the generation of 12 previously unreported analogues and, together with previous results, permitted assignment of the ten methyltransferases required for everninomicin biosynthesis. The in vitro activity of A₁- and H-ring-modifying methyltransferases demonstrated the ability to catalyze late-stage modification of the scaffold on an A₁-ring phenol and H-ring C-4’ hydroxy moiety. Together these results establish the potential of the everninomicin scaffold for modification through mutagenesis and in vitro modification of advanced biosynthetic intermediates.     

The potential of energy flexibility of space heating and cooling in Portugal

This study assesses the potential of energy flexibility of space heating and cooling for a typical household under different geographical conditions in Portugal. The proposed approach modifies the demand through the optimization of the thermostat settings using a genetic algorithm to reduce either operational costs or interaction with the grid. The results show that the used energy flexibility indicator expresses the available potential and that flexibility depends on several factors, namely: i) thermal inertia of the archetypical household; ii) the time of use electricity tariffs; iii) users’ comfort boundaries; and iv) the geographical location of the houses.     

Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

FE simulation of the curing behavior of the epoxy adhesive Hysol EA-9321

Cold-curing adhesives, characterized by an unsteady curing degree, present various advantages for assembling large scale structures set up under outdoor conditions. Thus various applications can be found in aerospace and automotive industries where structures are affected by thermal and mechanical loads. Hence, the curing state of the adhesive must be known to evaluate the lifetime of such bonded structures. The evolution of the polymerization of the adhesive Hysol EA-9321 during the curing process was examined in this paper. To that end, the curing degree of the adhesive was experimentally and analytically investigated for different curing cycles with a view to a potential application in the aerospace domain, where structures are assembled at low temperatures. Existing dynamic and isothermal curing models were applied to simulate the curing behavior of the adhesive. Then, an FEM model was developed to simulate the process of adhesive curing by taking into account a thermo-kinetic coupling.     

Preparation,characterization and properties of polycaprolactone diol-functionalized multi-walled carbon nanotube/thermoplastic polyurethane composite

Multi-walled carbon nanotubes (MWCNTs) were chemically functionalized to prepare thermoplastic polyurethane (PU) composites with enhanced properties. In order to achieve a high compatibility of functionalized MWCNTs with the PU matrix, polycaprolactone diol (PCL), as one of PU’s monomers, was selectively grafted on the surface of MWCNTs (MWCNT–PCL), while carboxylic acid groups functionalized MWCNTs (MWCNT–COOH) and raw MWCNTs served as control. Both MWCNT–COOH and MWCNT–PCL improved the dispersion of MWCNTs in the PU matrix and interfacial bonding between them at 1 wt% loading fraction. The MWCNT–PCL/PU composite showed the greatest extent of improvement, where the tensile strength and modulus were 51.2% and 33.5% higher than those of pure PU respectively, without sacrificing the elongation at break. The considerable improvement in both mechanical properties and thermal stability of MWCNT–PCL/PU composite should result from the homogeneous dispersion of MWCNT–PCL in the PU matrix and strong interfacial bonding between them.