InSb/InAsSb Strained Layer Superlattice Grown by MBE

叙述了采用国产 MBE 装置,在 GaAs 或 InSb 衬底上生长 InSb,InAsSb薄膜材料一些基础研究工作。采用二步生长法在 GaAs 衬底上生长优质 InSb 薄膜,厚度4.8μm,其室温迁移率达到4.3×10~4cm~2V·s,载流子浓度为2.4×10~(18)cm~(-3),77K 时载流子浓度为7.49×10~(15)cm~(-3);并在生长各种类型 InAsSb 超晶格材料的基础上,首次生长了 InAs_(0·05)Sb_(0·95)/InSb 应变层超晶格结构材料,其周期厚度为21nm,InSb 应变层与 InSb 层之间的共格度为0.65,本文还将叙述制作 InAsSb 长波红外探测器的具体工艺及其一些想法。     

High-mobility pentacene phototransistor with nanostructured SiO2 gate dielectric synthesized by sol-gel method

We have fabricated a pentacene based phototransistor by employing a modified nanostructured SiO₂ gate dielectric. The photosensing properties of the pentacene thin film transistor fabricated on n-Si substrate with nanostructured SiO₂ as gate dielectric have been investigated. The photocurrent of the transistor increases with an increase in illumination intensity. This suggests that the pentacene thin film transistor behaves as a phototransistor with p-channel characteristics. The photosensitivity and responsivity values of the transistor are 630.4 and 0.10 A/W, respectively at the off state under AM 1.5 light illumination. The field effect mobility of the pentacene phototransistor was also found to be 2.96 cm²/Vs. The nanostructured surface of the gate possibly is the cause of the high-mobility value of the phototransistor due to light scattering from the increased surface area.     

Facile deposition of ZnO:Cu films: Structural and optical characterization

Sol–gel technology has been applied for preparation of ZnO:Cu films. The proposed facile approach allows obtaining a wide variety of copper doped zinc oxide systems, revealing different structural and optical behaviors. The work presents structural and optical studies depending on Cu concentration and thermal treatments in the range of 500–800 °C. The structural analysis is performed by X-Ray diffraction (XRD). It reveals that small Cu addition enhances the film crystallization. Increasing copper concentration results in deterioration of ZnO:Cu crystallization. XRD study manifests no Cu oxide phases in ZnO:Cu film structure for lower Cu additions. For a specific higher copper concentration, an appearance of a small fraction of copper oxide is detected. Vibrational properties have been characterized by FTIR spectroscopy. The effect of the copper introduction into ZnO reveals a slight change of optical properties compared to ZnO films for certain Cu ratios. ZnO:Cu films with higher copper contents manifest different optical behaviors with very high transparency in spectral visible range.     

Effect of annealing temperature on optical and electrical properties of lead sulfide thin films

Lead sulfide (PbS) thin films with 150 nm thickness were prepared onto ultra-clean quartz substrate by the RF-sputtering deposition method. Deposited thin films of PbS were annealed at different temperatures 100 °C, 150 °C, 200 °C, 250 °C and 300 °C. X-ray diffraction pattern of thin films revealed that thin films crystallized at 150 °C. Crystalline thin films had cubic phase and rock salt structure. The average crystallite size of crystalline thin films was 22 nm, 28 nm and 29 nm for 150 °C, 200 °C and 250 °C respectively. From 150 °C to 250 °C increase in annealing temperature leads to increase in crystallite arrangement. FESEM images of thin films revealed that crystallite arrangement improved by increasing annealing temperature up to 250 °C. Increase in DC electrical conductivity by increasing temperature confirmed the semiconductor nature of crystalline thin films. Increase in dark current by increasing annealing temperature showed the effect of crystallite arrangement on carrier transport. Photosensitivity decreased by increasing annealing temperature for crystalline thin films that it was explained at the base of thermal quenching of photoconductivity and adsorption of oxygen at the surface of thin films that leads to the formation of PbO at higher temperatures.     

弧形曲面零件组合加工的工艺研究

针对弧形曲面零件的加工生产,为了提高产品的质量及生产效率,提出让加工工艺人员参与到产品的结构设计过程,与设计师共同商讨零件的工艺,得出零件组合加工的工艺方法,以成功完成零件的加工。这种方法有利于批生产零件的一致性和成本控制。     

AlN基板与金属化层界面的分析电镜研究

利用各种分析电镜观察了掺杂助烧剂和未掺杂助烧剂的ＡｌＮ陶瓷的微观结构特征，鉴别了ＡｌＮ中的第二相，研究了ＡｌＮ基板上薄膜（Ａｕ－Ｐｔ－Ｔｉ）和厚膜（Ｍｏ－Ｍｎ）金属化界面的结构。     

Influences of post-annealing temperature on the structural and electrical properties of mixed oxides (CuFeO2 and CuFe2O4) thin films prepared by spray pyrolysis technique

P-type mixed oxides (CuFeO₂ and CuFe₂O₄) transparent conducting thin films have been successfully deposited on p-type Si (111) substrates at 450 °C by spray pyrolysis deposition (SPD) and annealed at 800 °C for 2 h. The crystal structure, surface morphology and electrical property have been investigated. It is observed that the CuFeO₂ and CuFe₂O₄ thin films as deposited and annealed, have polycrystalline hexagonal structure and the crystallite size increases by annealing processes. The electrical property of the Ni/CuFeO₂/Si Metal–Semiconductor–Metal (MSM) photo detectors was investigated using the current–voltage (I–V) measurements. The barrier heights ϕ_Β of Ni/CuFeO₂/Ni MSM thin films of as deposited and annealed on Si substrates were calculated and its values are 0.478, 0.345 eV, respectively with an applied bias voltage of 3 V.     

Amorphous InGaZnO thin film transistors with sputtered silver source/drain and gate electrodes

The amorphous InGaZnO (a-IGZO) thin film transistors (TFTs) with sputtered silver source/drain (S/D) and gate electrodes were investigated and developed. The sputtered single-film Ag was confirmed to be unfit for the electrodes of a-IGZO TFTs because of its bad contact with a-IGZO and atom diffusion into insulators. Accordingly the sputtered Mo films were proposed to serve as the capping layers, indicating that the 20-nm-thick Mo could effectively form ohmic contact with the a-IGZO, prevent the Ag diffusion into the SiO_x, and make good adhesion to the glass substrates. The devices with multi-layer S/D and gate electrodes (Mo/Ag/Mo) were successfully fabricated, exhibiting the reasonably good performance and thus proving the application of the sputtered silver electrodes into a-IGZO TFTs was possible.     

Nanonecklace of CdO through simple solution chemistry

CdO nanonecklace like structure with interconnected nanobeads were produced by air annealed Cd(OH)₂ nanowire structure thin film at 290 °C. Simple and low cost chemical route has been successfully employed for the synthesis of Cd(OH)₂ nanowires on fluorine doped tin oxide (FTO) coated glass substrates at room temperature (27 °C). Structural analysis confirmed the conversion of hydroxide phase to the oxide phase by annealing which also leads to change in optical band gap from 3.5 to 2.34 eV. The necklace like nanostructure represent unique surface morphology which can be emerged as a potential candidate towards wide range of applications in different fields of nanotechnology such as solar cell, gas sensor, supercapacitor and photo-catalyst.     

Effect of sputter deposited Zn precursor film thickness and annealing time on the properties of Cu2ZnSnS4 thin films deposited by sequential reactive sputtering of metal targets

Cu₂ZnSnS₄ (CZTS) is made of earth abundant elements and also have suitable optical properties for solar cell applications. But, in phase diagram, CZTS exists in a narrow range of temperature and composition. Therefore, optimizing the elemental composition and annealing time is very important for obtaining phase pure CZTS. In this study, the effects of elemental composition and short annealing time on the structural and optical properties of reactively sputtered CZTS thin films are reported. Thin films were deposited by reactive sputtering of Cu: Sn (60:40 wt%), Sn and Zn targets sequentially in the presence of H₂S at room temperature. Amount of Zn precursor was varied by changing the sputter time for Zn. The films were rapidly annealed in inert atmosphere for varying time. The band gap of sample changed with change in the composition as well as annealing time. Sample with higher Zn content showed better crystallinity. With increase in the annealing time the crystallinity of samples improved. Sample annealed for 12 min at 550 °C was phase pure. Obtaining good quality film even for very short anneal time is the novelty of reactive sputtering method as all the elements are already mixed and short annealing is required only for crystal growth. Through detailed experiments, the optimum composition and annealing time required for the growth of phase pure CZTS has been established.