Synthesis of Ti3SiC2 by spark plasma sintering(SPS)of elemental powders

Ti3SiC2 materials have been fabricated by spark plasma sintering of the elemental powders with the addition of Al.At the heating rate of 80℃/min and under the pressure of 30MPa,the ideal synthesis temperature of Ti3SiC2 is in the range of 1150-1250℃.The addition of Al is in favor of the formation of Ti3SiC2.The synthesized compound has the molecular of Ti3Si0.8Al0.2C2 and lattice parameters of α=0.3069nm,c=1.7670nm.Its grain is plane-shape with a size of about 50μm in the elongated dimension.The prepared material has Vickers hardness of 3.5-5.5GPa(at 1N and 15s) and is as readily machinable as graphite‘s.     

Microstructure and mechanical properties of high strength as—cast Ti—15—3 alloy

The effects of heat treatment and solidification cooling rate on the microstructure and mechanical properties of as-cast Ti-15-3 alloy prepared by induction skull melting method were investigated.Results show that the microstructure of as-cast Ti-15-3 alloy changes from the features of simplified and larger size of beta grains to finer grain size with increasing solidification cooling rate.After solution treatment and different ageing treatment,alpha phase precipitates in grains interior as well as in grain boundaries.Due to the modification of the precipitate phase,the tensile stength and elongation of the alloy are improved simultaneously.A good combination of the values of 1.406GPa of σb and 4.5% of δ was obtained,which will be satisfied the use of this kind of alloy in critical areas.     

Stress relaxation behavior of Ti-6Al-4V alloy

1　INTRODUCTIONTi 6Al 4VisoneofthemostimportantTial loys[1,2 ] .Butthisalloyhasbadformabilityforitshighelasticresilience .Therefore ,hotsizingisimpor tant[36 ] .Asthebaseofhotsizing ,thestudyofstressrelaxationhasimportanttheoreticalvalueandpracticalsignificance .Ontheotherhand ,Ti 6Al 4Visusedasfastenermaterialssometimes .Whenthefastenersworkatthetemperaturehigherthanroomtemperature ,stressrelaxationmayresultsinacci dents .Sohowtopreventthestressrelaxationisveryimportant[7] .Uptonow ,…     

Fabrication of composite wire of lead coated on glass fiber by extrusion

1　INTRODUCTIONCoatingglassfiberwithleadproducesakindofnewcontinuouscomposite ,whichcanfindwideap plicationsinmanydifferentfields ,especiallyinthebatteryoftheEVsandHEVsthathasalreadybecomethemostimportantgoalinmostcountries[13] .Withakindofspecialtechnologythiskindofnewcompos itewirecanbeusedtoproducegridsofnewleadacidbatterythatisveryusefultotheEVsandHEVs .Thiskindofnewleadacidbatteryhasmanyadvan tages ,suchashigherspecificenergy ,lessinnerresis tance ,morequicklychargingcapabilityand…     

氢对Ti合金的Debye温度和晶格常数的影响

使用X射线衍射仪测定出不同氢含量的Ti-30Mo合金的Debye特征温度值以及晶格常数的变化,结果表明随着氢含量的增加,Debye特征温度相应地减小而晶格常数增加,证实了氢含量的增加会导致金属原子间键合力的减弱,从而造成金属脆化。     

压入深度与膜厚对薄膜与基体复合硬度及弹性模量的影响

根据高华建的复合弹性模量模型，提出了用一个测点的载荷-位移曲线计算整个压入深度内薄膜和基体复合硬度分布的方法，探讨了压入深度与膜厚对硬度与弹性模量测量值的影响，指出可由膜-基复合性能反推膜本身的性能。     

Kinetics of synthesis of Li4Ti5O12 through solid-solid reaction

1. Introduction The solid-solid reaction used in synthesizing various kinds of electrochemical materials has many advantages, such as simple process, without using solvent, saving energy, friendly to the environment and easy to obtain good quality materials like nano-size materials. Recently, the manufacturing of electrochemistry materials has been paid more atten- tion due to its increasing needs. Therefore it is a natural interest to study the synthesis of electro- chemical materials by usin…     

钛合金冷坩埚电磁约束铸造工艺研究

针对液态下化学性质相对活泼的钛合金,采用冷坩埚技术对电磁约束铸造工艺过程进行了试验研究,考察了工艺条件对成形坯件表面质量和内部组织的影响.结果表明:试样抽拉速度变化对表面质量和宏观组织的影响明显,加热功率虽然对组织变化影响不大,但对表面质量影响较为显著.通过优化工艺,可以获得既有较光滑铸造表面又具有一次定向凝固组织的钛合金铸件.讨论了铸造过程裂纹和组织缺陷的形成机理,获得到了表面光滑无裂纹,宏观组织为柱状晶的钛合金大尺寸圆坯.     

对涂料发展史及其系统的探讨

提出了涂料发展的三个时期与四个阶段的理论。同时指出,伴随涂料不断发展过程,发生了四次概念更新。在此基础上,提出了广义涂料概念和涂料大系统的新观点,以及建立涂涂层系统料新的理论体系的设想.