硅酸铝短纤维铝基复合材料耐磨性研究

本文研究了以硅酸铝短纤维作增强体，工业纯铝L00，铸造铝合金ZL101为基体的复合材料耐磨性。并与以颗粒状Al_2O_3为增强体进行对比。结果表明：硅酸铝纤维／ZL101复合材料的耐磨性为ZL101的321倍。在相同摩擦条件下，基体相同的铝基复合材料，以硅酸铝短纤维作增强体较以颗粒Al_2O_3为增强体有着更高的耐磨性。应用摩擦理论推导了磨损方程■与实测吻合。     

合金元素对6063铝合金组织性能的影响

以Al-Mg-Si系6063铝合金为研究对象，采用试验的方法研究了主要合金元素Mg、Si和杂质元素Fe,Zn对合金组织性能的影响，并在分析作用机理的基础上给出了改善材料性能的合理化建议。研究表明，主要合金元素Mg、Si对材料的强度和腐蚀性能有重要影响，生产实际中应使二者质量之比略小于正常值1．73；杂质元素Fe、Zn对合金组织的稳定性有一定影响，一般会使制品表面出现不同程度的点缺陷。     

引线框架C194铜合金铸态组织和性能分析

研究了工业化不同生产试验批次的C194铜合金引线框架材料铸态组织和性能。结果表明C194的化学成分、加料顺序等因素对铸态晶内、晶界的球状第二相Fe3P或Fe2P的大小、分布均匀性有较大影响;添加剂对C194铸坯有明显的晶粒细化作用;其导电率达到14%～20%IACS,维氏硬度在95HV左右。     

Effects of deformation on microstructures and properties of submicron crystalline Cu-5%Cr alloy

Warm extrusion of submicron crystalline Cu-5%Cr from 100 ℃ to 600 ℃ was investigated. The effects of different extrusion ratios and different extrusion temperatures on microstructures and properties of submicron crystalline Cu-5%Cr were studied. The microstructures of the extruded Cu-5%Cr were characterized by backscattered electron irnages（BSE） and transmission electron microscopy（TEM）. The mechanical properties of the extruded Cu-5%Cr were measured by means of microhardness and tension test. The results show that, the deformation, dynamic recovery and dynamic recrystallization of the extruded Cu-5%Cr are mainly produced in Cu matrix. The higher extrusion ratio leads to more uniform microstructure and finer Cu grains. When being extruded in the range of 100-600 ℃, dynamic recovery of Cu is the dominant process, and dynamic recrystallization of Cu occurred above 300 ℃ is far from end. The most part of microstructure of as-extruded Cu-5%Cr is subcrystaUines produced by dynamic recovery, only a few recrystallines exist, and the average size of these grains is not larger than 400 nm. With extrusion temperature rising, the tensile strength and microhardness of Cu-5%Cr decrease, and elongation increases gradually.     

Thermodynamic reassessment of the Cd−Zn system

The Cd−Zn system has been thermodynamically reassessed with the CALPHAD method by combining more recent experimental data, in particular the activities of zinc in the liquid phase. A good agreement is obtained between the calculated and experimental thermodynamic parameters as well asphase boundaries.     

Mechanically activated disproportionation of NdFeB alloy by ball milling in hydrogen

1　INTRODUCTIONSincethediscoveryoftheuniaxialNd2 Fe14 Bcompoundin 1983[1,2 ] ,theNdFeBalloyshavebeenwidelyusedforpermanentmagnetapplicationsowingtotheirexcellentmagneticproperties ,suchashighcoercivity ,high energy products[3,4 ] .Intheserareearthpermanentmagnets ,afurtherexcitingrecentdevelopmentisthesuggestionofnano compositeex changemagnetscombiningthelargecoercivitiesinhardmagnetswithlargeinductionsfoundinsoftertransitionmetalmagnets[5,6 ] .Indeed ,thenano com positemagnetshavebeent…     

Effect of NiAl Microcrystalline Coating on the High-Temperature Oxidation Behavior of NiAl–28Cr–5Mo–1Hf

The effect of an NiAl microcrystalline coating prepared by magnetron sputtering on the high-temperature oxidation behavior of NiAl–28Cr–5Mo–1Hf was investigated in static air at 1000–1150°C. The additions of Cr, Mo, and Hf changed the single -phase structure into a multiphase structure [-NiAl, -Cr(Mo), and Heusler phase]. The NiAl–28Cr–5Mo–1Hf alloy formed a nonprotective mixed scale of Al₂O₃+Cr₂O₃+HfO₂ and exhibited relatively large weight gains. The large weight gains were attributed to extensive internal oxidation. The sputtered NiAl microcrystalline coating remarkably improved the oxidation resistance of NiAl–28Cr–5Mo–1Hf due to the formation of a compact and adherent Al₂O₃ scale at all test temperatures. It was found that the --Al₂O₃ transformation caused the anomalous behavior of the oxidation–kinetics curves of the NiAl microcrystalline coating in the temperature range 1000–1150°C. A change in the morphology of scales occurred with the transformation.     

稳恒磁场下Ni-W合金镀膜的制备与耐蚀性

研究了施加稳恒磁场(0~1 T)对电镀Ni-W合金的影响。测定不同方向、不同强度稳恒磁场下的电流效率、合金组成及镀层的耐蚀性,并用扫描电镜和X射线衍射对镀层的微观形貌及结构进行了观察和分析。对实验结果进行了分析讨论,找出稳恒磁场对这些性能指标的影响规律。结果表明:与不施加磁场相比,施加磁场后镀层的表面更均匀、细致、平整;镀层的含钨量上升:当B⊥J,B=1.0 T时,含钨量上升了约7%;当B∥J,B=1.0 T时,含钨量上升了约9%;镀膜的非晶化程度增强;镀膜的耐蚀性提高;但Ni-W合金电镀的电流效率降低。     

A THERMODYNAMIC INVESTIGATION ON SPINODAL DECOMPOSITION BOUNDARY IN Cu－Ti ALLOYS

ＡＴＨＥＲＭＯＤＹＮＡＭＩＣＩＮＶＥＳＴＩＧＡＴＩＯＮＯＮＳＰＩＮＯＤＡＬＤＥＣＯＭＰＯＳＩＴＩＯＮＢＯＵＮＤＡＲＹＩＮＣｕ－ＴｉＡＬＬＯＹＳ￥ＷｅｉＹｉｎｇｈｕｉ；ＷａｎｇＸｉａｏｔｉａｎ（ＩｎｓｔｉｔｕｔｅｏｆＭａｔｅｒｉａｌｓＳｃｉｅｎｃｅａｎ...     

Nonclassical constitutive model involving void evolution of casting magnesium alloy

The void evolution equation and the elastoplastic constitutive model of casting magnesium alloy were investigated. The void evolution equation consists of the void growth and the void nucleation equations. The void growth equation was obtained based on the continuous supposition of the material matrix, and the void nucleation equation was derived by assuming that the void nucleation follows a normal distribution. A softening function related to the void evolution was given. After the softening function was embedded to a nonclassical elastoplastic constitutive equation, a constitutive model involving void evolution was obtained. The numerical algorithm and the finite element procedure related to the constitutive model were developed and applied to the analysis of the distributions of the stress and the porosity of the notched cylindrical specimens of casting magnesium alloy ZL305. The computed results show satisfactory agreement with the experimental data.