高合金钢铸造用涂料的试制与开发

介绍了炉爪用合金钢1Cr25Ni20Si2Re,导板用合金钢2Cr32Ni5采用串箱铸造过程中，有关镁砂粉涂料和石英粉涂料的试制。结果表明：镁砂粉涂料为不透气涂料，不太适用，而合理配方的石英粉涂料使用性能良好。     

热处理对Ti-25V-15Cr-2Al-2Mo-0.2C合金组织稳定性的影响

研究了热处理对Ti-25V-15Cr-2A1-2Mo-0.2C阻燃β钛合金组织稳定性的影响。结果表明，高温固溶并直接时效处理导致合金β基体上析出较多的α相沉淀，尤其在随后的热暴露组织中形成了恶化合金塑性的连续晶界α膜。然而，若在时效前再进行一次低温固溶处理则可明显减少α相的析出数量，合金的热稳定性因此而得到显著改善。     

Al_(10)Zn_(2.9)Mg_(1.7)Cu超高强铝合金的喷射成形制备研究

采用喷射成形技术制备了Al1 0 Zn2 .9Mg1 .7Cu高强高韧铝合金沉积坯件 ,研究了喷射成形制备过程中各工艺参数对沉积坯件的成形性、显微组织、致密度的影响 ,确定了适当的工艺参数 ,研究了沉积坯件的热挤压及热处理工艺 ,对材料的组织进行了分析并对不同状态的材料性能进行了比较。研究结果表明 :当喷射成形工艺参数合理时 ,沉积坯件具有良好的成形性与致密度 ,在随后的热挤压过程中 ,通过较低的挤压比即可使材料达到全致密 ;通过对合金进行适当的热处理 ,材料的极限抗拉强度达到 810MPa ,同时延伸率保持在 8%～ 11% ,该材料是一种理想的轻质高强结构材料。     

钛合金植入物材料的表面改性研究进展

简介了钛合金植入物材料的开发及表面改性技术。     

Experimental Study on Polymer Artificial Bone with HA Coated and Fiber Liners

1Introduction HA(hydroxyapatite)wasakindofbioactiveceram ics,whichhadexcellentbiocompatibilityandtissueaffin ityinthatitscomponentsweresimilartothoseofhuman bone[1].Soitwasthebestknownhumanbonesubstitute,andunprecedentedeffecthadbeenharvestedinrecenttwo d…     

Density Measurement of Liquid Ni-Ta Alloys by a Modified Sessile Drop Method

The density of liquid Ni- Ta alloys was measured by using a modified sessile drop method. It is found that the density of the liquid Ni- Ta alloys decreases with the increasing temperature, but increases with the increase of tantalum concentration in the alloys. The molar volume of liquid Ni- Ta binary alloys increases with the increase of temperature ancl tantalum concentration.     

Plasma Sprayed Hydroxyapatite Coatings with Nano-hydroxyapatite Prepared by Ultrasonic Precipitation Process

Nano-particle hydroxyapatite （ HA ） was prepared with a novel ultrasonic precipitation process and the as-prepared nanopowder was used to produce hydroxyapatite （ HA ） coatings on titanium substrate via plasma spraying. The phase and the microstructare of the coating were characterized by X- ray diffraction （XRD） and scanning electron microscopy （SEM）. Results showed that spherical particles could be prepared by ultrasonic precipitation process; and a corresponding dense HA coating with molten surface and low-porosity cross-section structure was acquired. During the plasma spraying process, new phases of Ca3 （ PO4 ）2 and Ca2 P2O7 were generated. After heat-treating at 800℃ for 1 h, the contents of Ca3 （ PO4 ）2 and Ca2 P2O7 decreased while HA content increased. Tensile adhesion tests showed that the plasma sprayed coating prepared with the spherical nanoparticles exhibited high tensile bond strength.     

Water‐Stable,Magnetic Silica–Cobalt/Cobalt Oxide–Silica Multishell Submicrometer Spheres

A method to produce monodisperse magnetic composite spheres with diameters from less than 100 nm to more than 1 μm in water solution is reported. The spheres consist of a dielectric silica core and a cobalt/cobalt oxide shell which can be protected from further oxidation with an outer shell of silica or, alternatively, they can be covered with the polymer polyvinylpyrrolidone as a stabilizer. The formation of a uniform magnetic shell proceeds with the adsorption of metallic cobalt seeds, produced by the reduction of cobalt chloride with sodium borohydride, on a self‐assembled layer of polyelectrolytes on the silica core. In the second step, an outer silica shell can be formed by the hydrolysis and condensation of (3‐aminopropyl)trimethoxysilane and tetraethoxysilane. The double‐shell composite spheres show excellent sphericity, monodispersity, and a magnetic hysteresis loop at room temperature.     

Cu—Zn—Al系合金热弹性马氏体相变的热滞

本文通过热处理工艺及添加第四组元研究了Cu－Zn－Al系记忆合金的相变热滞。结果表明，淬火冷却速度影响合金的相变热滞大小，随着母相时效时间的延长，马氏体相变热滞变大．Mn元素的加入可以减小CU－Zn－Al合金相变热滞．     

核电反应堆用芯部材料的核物理性能

核物理性能是核电站反就堆芯部结构材料的首要技术条件。本文概述合金材料核物理的有关问题，以及核截面的计算方法。