碳铬镍含量对高铬铸铁测温保护管性能的影响

通过高温氧化和高温磨损实验,研究了C、Cr、Ni 3个主要元素对高铬铸铁在高温条件下抗氧化和抗磨损性能的影响。结果表明:Cr含量越高,抗氧化性能和抗磨损性能越好;提高碳含量,明显提高高铬铸铁的高温抗磨性能;当w(Cr)=16％时,加入Ni能提高高铬铸铁的高温抗氧化性能;w(Cr)=30％时,Ni对高铬铸铁的抗氧化性能和抗磨损性能影响不明显.在1100℃以下,选用w(C)=2.8％,w(Cr)=30％、不加Ni的高铬铸铁铸造高温抗磨热电偶保护管,既有较好的使用寿命,又可降低成本.     

Effect of Rare Earth Elements on Thermal Fatigue Property of Low Chromium Semi-Steel

The effect of rare earth elements on eutectic carbide‘s morphology of low chromium semi-steel in as-cast state and after heat treatment was investigated, and accordingly, the thermal fatigue property of this material was studied. The results show that RE can improve the eutectic carbide‘s morphology, inhibit the formation and propagation of thermal fatigue cracks, therefore, promote the thermal fatigue property, which is more noticeable in case of the RE modification in combination with heat treatment. The optimal thermal fatigue property can be obtained when treated with 0.2% RE modification as well as normalization at 950℃ for 3h.     

Contact interaction of double titanium and chromium diboride with Fe-Cr alloys

The kinetics of wetting double titanium and chromium diboride by iron-based alloys with different chromium content is studied. It is shown that contact angles are formed in such systems over the range 0–10°. The energy parameters of wetting are calculated. It is established that chromium as a surface-active element promotes Fe-Cr alloy spreading on the diboride surface. The microstructure of the interaction area is studied. It is shown that terminal solid solutions and eutectics are formed in the TiCrB₂-(Fe-Cr) system. The optimum compositions of the metallic binder are determined for TiCrB₂-based composite materials. __________ Translated from Poroshkovaya Metallurgiya, Vol. 46, No. 1–2(453), pp. 109–115, 2007     

摩擦诱发高铬铸铁相变的透射电镜研究

利用透射电子显微镜研究了高铬铸铁在摩擦过程中的显微组织变化。结果表明：奥氏体基体在摩擦应力的作用下发生相变。摩擦表面形成α‘Ｍ。次表层形成γ与α’Ｍ共存区；γ与．ε共存区；γ位错丛聚区。     

Analysis of the effect of polypyrrole synthesis conditions on its capacity to reduce hexavalent chromium

This paper reports the capacity of polypyrrole to reduce toxic hexavalent chromium (Cr(VI)). The influence of using different electrolytes during the polymer's synthesis has been studied. To improve the reduction of Cr(VI), the parameters considered were the polypyrrole morphology and the amount of conducting polymer. Polypyrrole obtained by cyclic voltammetry at a low sweep rate using KBr as supporting electrolyte showed better performance for Cr(VI) reduction compared to coatings obtained by constant potential or cyclic voltammetry at high sweep rates.     

FTIR investigation of ethylene coordination and polymerization on reduced Cr/SiO2 catalyst

FTIR spectroscopy was applied to study the initial steps of ethylene polymerization on reduced chromia-silica (0.5 wt% Cr/SiO₂). To decrease the speed of the reaction small doses of gas were introduced to the catalyst in each run and C₂D₄ was used to confirm band assignments. At the initial steps of the reaction only ethylene molecules coordinated to probably Cr _A ²⁺ cations were observed. The concentration of such complexes was estimated to be about 50% of the total amount of Cr atoms in the sample. The FTIR spectrum of the polymer formed at the initial doses of C₂H₄ (when [C₂H₄] [Cr]) was found to be slightly different from that formed after excess ethylene was introduced onto the catalyst ([C₂H₄] > [Cr]).     

石英砂的相变与换向器套筒铸件的变形

用呋喃树脂石英砂工艺生产牵引电机换向器套筒出现变形、裂纹等铸造缺陷,是由石英砂相变膨胀引起,后用高铬刚玉砂代替石英砂得到解决.     

碳化物在高铬铸铁高应力磨料磨损中的影响

对不同载荷作用下的高铬铸铁在耐磨实验机上进行了磨料磨损试验;对在不同的碳化物对基体的保护作用与碳化物的剥离进行了相关的分析.结果表明载荷在一定值以下磨损较为缓慢,当载荷超过一定值时,磨损急剧加剧,随着载荷的增加"尺寸较小"的碳化物首先剥离基体,当载荷继续增大时,"尺寸较大"的碳化物也剥离基体并有碎裂现象.这要求高铬铸铁中的碳化物不仅要分布均匀,碳化物的尺寸也要合适.     

关于“冲天炉熔制高铬磨球的探讨”一文的商榷

讨论了用冲天炉熔炼高铬铸铁的可能性。分析在明，冲天炉条件下铬铁合金熔化的热力学条件是不合适的，它将导致大量铬元素的烧损，增加铁液夹杂物数量。其次，高铬铸铁的熔体，有强烈的从焦大中渗碳的趋势，故含碳量难以控制。认为用冲天炉熔炼高铬铸铁是不合适的。     

化学气相沉积法制备碳化铬薄膜的研究

以三（2,2,6,6-四甲基-3,5-庚二酮）化铬为前驱体,采用化学气相沉积（CVD）法在氧化铝（Al₂O₃）陶瓷基板上制备碳化铬（Cr₃C₂）薄膜,其中沉积温度为723 K至923 K,沉积时间为1 200 s。研究了不同沉积温度对Cr₃C₂薄膜的相组成、择优取向、宏观表面、微观结构及电学性能的影响。结果表明,在723 K至923 K下制备得到具有高度（130）择优取向的Cr₃C₂薄膜。随着沉积温度的升高,Cr₃C₂薄膜表面先由光滑变粗糙,后逐渐变光滑;薄膜晶粒呈椭球型生长;薄膜的厚度先增加后减小,从而导致电阻先减小后增大。在798 K时制备得到厚度最大且电阻最小的（130）择优取向的最佳Cr₃C₂薄膜。同时,在实验条件下Cr₃C₂薄膜表面存在少量的碳和Cr₂O₃。