大剂量Si-Mn复合孕育剂在铸铁中的应用

从例证和机理两方面来说明通过大剂量Si Mn复合孕育在铸铁中的应用 ,使Mn的作用得到充分发挥 ;Mn13是提高铸铁组织中珠光体量和性能的理想元素 ;通过调节大剂量Si Mn复合孕育剂中Mn的比例来稳定和提高基体组织中的珠光体量 ,达到稳定和提高铸铁性能的目的 ,它的可操作性比通过控制化学成分来稳定和提高铸铁的性能更好更容易 ,冲天炉熔炼效果更明显。     

AGING BEHAVIOUR OF PARTICULATE REINFORCED ALUMINUM ALLOY MATRIX COMPOSITES

The process of aging precipitation in SiC_p/6061 and Al_2O_3/6061 composites were investigated. Hardness testing, differential scanning calorimetry(DSC) and transmission electron microscopy were employed. Results showed that the precipitation phase form directly along dislocation lines in the composites because the particles produce high densities of dislocations which makes vacancy densities in the composites decrease, and the main precipitation phase at peak hardness was β′ phase.     

Morphological evolution of primary TiC carbide in laser clad TiC reinforced FeAl intermetallic composite coating

1　INTRODUCTIONIronaluminumbasedonFeAlintermetallicalloywasexpectedtobeanimportantandpotentialhightemperaturematerial,becauseitsgoodresistancetooxidationandcorrosion ,lowdensityandhightem peraturemelting point[12 ] .However ,theintrinsicpropertiesofFeAlintermetallicalloy ,suchaslowductilityandlowfracturestrength ,limiteditsindus trialapplications .Howtoimprovemechanicalproper tiesofFeAlintermetallicalloyandexpanditsindus trialapplicationrealmwasanimportantresearchas pectformaterialworke…     

液态铝合金表面张力快速检测新方法与装置

表面张力是液态合金的重要物性参数之一,铝合金表面张力与其变质处理效果及充型能力等质量参数密切相关,研究铸造铝合金表面张力快速检测方法及装置,对于开发铝合金熔炼质量炉前实时评价系统具有非常重要的实际意义.介绍了一种液态铝合金表面张力快速测试的新方法和新装置,新方法以固定时间内吹入被测液体的气泡个数以及气泡在生长过程中内部压差变化为信息参数,通过回归公式求解表面张力.基于该方法研制的表面张力新型测试装置由单片机测控单元、探头及其锁紧和升降机构、供气单元等部分构成.采用新装置可在5 s内测得铝合金表面张力,且具有较高的测试精度.     

Influence of Reinforcement Content and Matrix Composition on the Oxidation Resistance of Aluminum-Matrix Composites (A3xx.x/SiCp)

A study was made on the influence of the SiCp proportion and the matrix concentration of four composites (A360/SiC/10p, A360/SiC/20p, A380/SiC/10p, A380/SiC/20p) on their oxidation behavior. Gravimetric tests were used in a kinetics study of the corrosion process at different temperatures (350, 400, 450, and 500°C). The influence of corrosion on mechanical properties was evaluated by hardness measurements. The nature of corrosion products and the influence of the microstructure on the morphology and growth of the oxidation layer were analyzed by SEM and low-angle XRD. The extent of the damage due to oxidation for Al/SiCp composites increases with the SiCp concentration due to the increase of nucleation sites. One of these nucleation sites is in the interface region between the matrix and the particles. Oxidation was influenced more by the percentage of alloy elements in the matrix than by the proportion of SiCp reinforcement. The presence of Cu and Ni in the matrix favors the oxidation process through the formation of different intermetallic compounds.     

Corrosion resistance of austenitic stainless steel separator for molten carbonate fuel cell

STS310S and SC-STS310S (simultaneously co-deposited chromium and aluminum onto 310S austenitic stainless steel substrate by pack-cementation process) were used as separator materials on the cathode side of a molten carbonate fuel cell. With the STS310S, corrosion proceeded via three steps; a formation step of unstable corrosion product, a protection step against corrosion until breakaway, and an advance step of corrosion after breakaway. The final corrosion product was LiFeO₂ and the loss of mass was 6.5 mg/cm² after a corrosion test of 480 hr at 650°C. The SC-STS310S showed more effective corrosion resistance, however, than did common STS310S. There was especially no corrosion loss on the SC-STS310S after the 480 hr corrosion test. It is anticipated that it will be very useful as an alternative separator on the cathode side off the MCFC in the future.     

铝—钢双金属复合轧制层厚比及轧制力的研究

用实验方法研究了铝－钢双金属复合轧制时层厚比的变化规律。给出了双金属复合时轧制力的计算式。