Composition Range of Amorphous Mg-Ni-Y Alloys

Based on the thermodynamic point of view, a method for predication of the composition range of amorphous ter-nary alloys was proposed. The composition range of amorphous ternary alloys is determined by the comparison of the excess free energy of the amorphous alloy and the free energy of competing crystalline states. The free energy is extrapolated from the data of three binary alloys by using Toop‘s model. The method was applied to predict the composition range of amor-phous Mg-Ni-Y alloys. The theoretical results are in good agreement with the available experimental results. It indicates that the present method can be used to predict the composition range for amorphous ternary alloys.     

Crystalline Behavior and Magnetic Properties of Nd60Fe30-x Al10Cox（x = 0,5,10） Bulk Amorphous Alloys

Crystalline behavior and magnetic properties of Nd60Fe30-xAl10Cox( x = 0, 5, 10) bulk amorphous alloys were investigated by differential scanning calorimeter (DSC), X-ray diffraction (XRD) and the vibrating sample magnetometer (VSM). Neither glass transition nor supercooled liquid region before crystallization was observed for the as-cast Nd60Fe30-xAl10Cox ( x = 0,5,10) bulk amorphous alloys. The glass forming ability can be improved significantly by the addition of Co. The as-cast Nd60Fe30-xAl10Cox (x = 0,5,10) alloys show hard magnetic behavior. With the addition of Co content, intrinsic coercivity (iHc) increases while the saturation magnetization(σs) and remanence (σr) decrease. The Curie temperature for the as-cast Nd60Fe30-xAl10Cox alloys increases from 451 K for x =0 to 468 K for x = 10. Some pre-cipitation of crystalline phases does not affect the hard magnetic properties of Nd60Fe30-xAl10Cox(x = 0,5,10) alloys, while the hard magnetic behavior disappears quickly after the alloys being completely crystallized.     

Effect of Substrate Bias on Microstructure and Properties of Tetrahedral Amorphous Carbon Films

The microstructure and properties of tetrahedral amorphous carbon (ta-C) films deposited by the filtered cathodic vacuum arc technology has been investigated by visible Raman spectroscopy, AFM and Nano-indentor. The Raman spectra have been fitted with a s     

Amorphous chromium silicide formation in hydrogenated amorphous silicon

The interaction between thin films of hydrogenated amorphous silicon and sputter-deposited chromium has been studied. Following deposition of the chromium films at room temperature, the films were annealed over a range of times and temperatures below 350°C. It was found that an amorphous silicide was formed only a few nanometers thick with the square of thickness proportional to the annealing time. The activation energy for the process was 0.55±0.05 eV. The formation process of the silicide was very reproducible with the value of density derived from the thickness and Cr surface density being close to the value for crystalline CrSi₂ for all films formed at temperatures ≤300°C. The specific resistivity of the amorphous CrSi₂ was ≈600 μΩ·cm and independent of annealing temperature.     

超声波对化学镀Ni－Cr－P非晶态薄膜的金刚石性能的影响

研究了超声波对化学镀Ｎｉ－Ｃｒ－Ｐ非晶态薄膜的金刚石性能的影响。结果表明，超声波可使金刚石表面非晶态薄膜更加均匀和致密，从而提高了抗压强度，氧化温度和晶化后的强度。随超声波频率的增加，金刚石性能有增加的趋势。     

非晶硅基薄膜的等离子体刻蚀光发射谱检测

本文研究了采用锁定放大相干检测技术的等离子体光发射谱检测系统。用该系统检测了仅用CF4作为刻蚀气体刻蚀非晶硅基薄膜的等离子体光发射谱。分析了检测结果和刻蚀机理。     

一种制备插层和无定形高岭土的新方法

利用甲醇钠强烈的夺氢作用 ,介绍了一种制备插层和无定形高岭土的方法。利用XRD为主要检测手段研究了甲醇钠的质量分数、反应温度等因素对反应的影响。结果表明 :在反应温度较低、质量分数较低的甲醇钠溶液中 ,高岭土容易被插层而膨胀 ,反之高岭土的层状结构被破坏而无定形化。红外光谱分析进一步证明了插层和无定形高岭土结构的变化     

Development of sealing compositions with nanostructure iron-based fillers

The possibility of utilizing nanopowders of iron and Fe-Co-Ni produced bu a thermochemical method in the fabrication of sealing composition materials is investigated. It is established that such hermetic sealing composition materials function reliably under extremal conditions and guarantee elevated strength of adhesion to the surface of the metal and high corrosion and temperature stability. __________ Translated from Poroshkaya Metallurgiya, Nos. 3–4(448), pp. 112–117, March–April, 2006.     

CVD金刚石膜生长过程的Raman分析

采用激光Raman散射分析法对CVD金刚石膜的生长过程进行研究 ,讨论在金刚石膜生长的不同阶段 ,膜内金刚石和非金刚石成分的相对含量及其残余应力的变化情况     

Thermally stimulated shrinkage forces in oriented polymers: 1. Temperature dependence

Temperature dependences of shrinkage forces appearing in oriented polymer samples when heated at constant length were recorded for polycarbonate, polyethylene terephthalate, polyethylene and polypropylene. The influence of various processing conditions on thermally stimulated shrinkage forces is demonstrated. A four-state model is proposed which qualitatively describes the temperature dependences of shrinkage forces in amorphous polymers.