EPS模陶瓷型精密铸造失模工艺研究

针对EPS陶瓷壳型精铸失模时容易裂壳的现象,对EPS消失模精密铸造工艺进行了研究。利用自制的膨胀率检测设备对不同密度的EPS模试样在不同加热温度下的最大膨胀率进行了测试,研究了壳型膨胀与失模温度之间的关系;对陶瓷壳型中EPS模失模时的温度场分布进行测量,发现EPS模试样的密度大小对失模时温度场有着很重要的影响。在试验和分析的基础上,对EPS模失模机制进行了探讨,提出了高温失模机制。高温失模有利于降低失模时对壳型的膨胀作用力,为获得洁净而健全的陶瓷型壳提供了可靠保证。     

Analysis of chill-cast NiAl intermetallic compound with copper additions

This study carried out a characterization of chill-cast NiAl alloys with copper additions, which were added to NiAl, such that the resulting alloy composition occurred in the β-field of the ternary NiAlCu phase diagram. The alloys were vacuum induction melted and casted in copper chill molds to produce ingots 0.002 m thick, 0.020 m wide, and 0.050 m long. X-ray diffractometry (XRD) and transmission electron microscopy (TEM) performed in chill-cast ingots identified mainly the presence of the β-(Ni,Cu)Al phase. As-cast ingots showed essentially no ductility at room temperature except for the Ni₅₀Al₄₀Cu₁₀ alloy, which showed 1.79% of elongation at room temperature. Ingots with this alloy composition were then heat treated under a high-purity argon atmosphere at 550 °C (24 h) and cooled either in the furnace or in air, until room temperature was reached. β-(Ni,Cu)Al and γ′(Ni,Cu)₃Al were present in specimens cooled in the furnace and β-(Ni,Cu)Al, γ′(Ni,Cu)₃Al plus martensite-(Ni,Cu)Al were present in specimens cooled in air. Thermogravimetric analysis indicated that martensite transformation was the result of a solid-state reaction with M _s ∼ 470 and M _f ∼ 430 °C. Tensile tests performed on bulk heat-treated ingots showed room-temperature ductility between 3 and 6%, depending on the cooling media.     

304不锈钢精铸件点缺陷的形成与控制

针对典型304不锈钢精密铸件内出现的黑色点缺陷,对其表面形貌、成分进行了分析,并在此基础上总结了缺陷的形成机制,确定了相应的防止措施。研究结果表明,铸件内的点缺陷可以划分为两类:一类具有不规则截面,为脱蜡过程中剩余腊料的燃烧残留物;另一类为熔炼过程中,由于脱氧剂和除渣剂的去除不彻底而引入的夹杂。通过优化脱蜡和熔炼工艺,使得铸件内的点缺陷得到了很好的控制。     

艺术铸件冷冻冰模制模方法的研究

艺术铸件是艺术创作和铸造技术的完美组合，铸造工艺是艺术思想的重要保证。从古至今，艺术家和铸造工作者进行了不懈的探索。本文通过试验，分析了冷冻铸造方法用于艺术铸造的一些优势，探讨了用硅橡胶模具制作冰模的工艺方法，并将用此工艺成功制作的一些冰模展示出来。     

Airslip结晶器内凝固壳形成特性分析

根据Airslip结晶器的传热特性,建立了凝固壳厚度和临界凝固壳厚度的数学模型.理论分析和实验结果表明,凝固壳厚度与铸造速度的乘积为常数,铸造速度增大,凝固壳厚度减小,铸锭表面质量提高;铸造速度的波动引起凝固壳厚度的波动,降低了铸锭的表面质量;铸锭直径和铸造速度的乘积也为常数,铸锭直径增大,铸造速度相应减小.     

铸造工艺远程设计系统的实现

探索一种基于Internet的铸造工艺远程设计系统的开发方法。采用大口出流理论和均衡凝固理论作为浇冒口设计理论;以ASP．NET作为系统的开发工具,使用Access作为后台数据源,并用ADO．NET技术连接数据库;介绍实现系统主要功能的关键技术。将铸造工艺设计系统从单机平台转向Internet,提高了系统的共享度及升级维护的方便性,避免了系统的孤立和老化,并能实现多用户同时对系统的不间断使用。     

Analysis of Intermetallic Phases Formed on Surface Vapor Oxidized H13 Hot Work Steels in Molten Aluminum

In this paper, the author dipped surface vapor oxidized H13 steel specimens into 700℃ molten aluminum liquid for a certain period of time. Analyze the intermetallic phases formed on the H13 samples surface with optical microscope and X-ray diffraction method. The observation of immersion test sample's cross-section shows that Fe3O4 film will protect die substrate from molten aluminum erosion. The identification of the intermetallic phases reveals that they consist of 2parts, which is named as the composite layer and the compact layer. Further investigations are made in order to know the phase constituents of the 2 layers, they are Al8Fe2Si (outer composite layer), (AlCuMg) and Al5Fe2 (compact layer),respectively. The experimental results show that on the same specimen, a convex surface with bigger radius of curvature is more likely to be molten and the melting loss speed is also faster than a flat and smooth surface. The thickness of compact layer on a smooth surface is much bigger than that of the convex surface. Therefore, the author supposes the compact layer is favorable in stabilizing the die surface material from further melting loss, as their formation on the die surface, the melting loss speed will decrease.     

铸钢件铸造工艺CAD软件的研制与应用

在收集、整理和总结多个版本和厂家的参考材料和手册以及作者多年工作经验的基础上 ,在国产CAXA电子图版的二次开发平台上 ,选用VisualC 语言研制了砂型铸钢件铸造工艺CAD软件。该软件具有图库管理、铸件重量和模数计算、铸造工艺方案和参数选择、冒口系统设计和浇注系统设计等项基本功能 ,对下环铸钢件铸造工艺的计算机辅助设计和生产实践结果表明 ,可以缩短工艺设计周期 ,提高工艺设计水平 ,生产优质铸件。     

逆向工程技术在复杂铸造模具制造中的应用

首先介绍了逆向工程技术与传统制造技术的区别,然后着重讨论利用逆向工程技术快速制造复杂铸造模具的过程及工艺路线,同时给出一些具体应用实例。最后得出与传统制造方法相比具有效率高、成本低、操作简单等优点的结论。     

用气冲气推成形触头造型机制造电机壳铸型的试验研究

扼要介绍了用气冲气推成形触头造型机制造电机壳铸型的成型过程及其实砂效果,试验结果表明,在工作气压为0,4￣0.45MPa的条件下,气冲气推成形触头造型机对电机壳类铸型的紧实,实砂效果十分理想,砂型紧实度高而且均匀。