TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

纳米ZrO2等离子涂层的结构,性能和工艺特点

采用大气等离子喷涂技术(APS)，制备了常规氧化锆和纳米结构氧化锆两种涂层．利用扫描电镜(SEM)对涂层的显微结构进行了观察．对两种涂层的沉积效率、表面粗糙度和显微硬度作了对比研究．结果表明，粉末原料的显微结构、粒度、形态、喷涂工艺参数(喷涂功率和距离)对涂层的显微结构有较大的影响．等离子喷涂造粒纳米氧化锆粉制备的涂层沉积效率高而稳定，其显微结构与喷涂功率和距离密切相关．与常规氧化锆涂层相比，纳米结构氧化锆涂层具有较高的显微硬度和较低的表面粗糙度．     

Computational analysis of thin coating layer failure using a cohesive model and gradient plasticity

Thermal barrier coatings (TBC) are widely used to prevent transient high temperature attack and allow components high durability. Due to strong inhomogeneous material properties the TBC failure often initiates near the interface between the brittle oxide layer and the ductile substrate. A reliable prediction of the TBC failure requires detailed information about the crack tip field and the consequent fracture criteria. In the present paper both cohesive model and gradient plasticity are used to simulate the failure process and to study interdependence of the interface stress distribution with the specific fracture energies. Computations confirm that combination of the two models is able to simulate different failure mechanisms in the TBC system. The computational model has the potential to give a realistic prediction of the crack propagation process.     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

真空铸造高强度C/Mg复合材料

本文介绍用真空铸造法制造抗拉强度超过1000MPa的高强度C/Mg复合材料。将T300纤维经C-Si-O梯度涂层处理后单向排布于型腔内,在真空下注入ZM-5合金液,凝固后即得C/Mg复合材料零件或试样。试样的抗拉强度在纤维体积分数为0.35时达1050MPa。本文讨论C-Si-O梯度涂层对获得高强度复合材料的作用。     

T8钢－聚有机硅氧烷仿生减粘降阻复合涂层的特性

研究了Ｔ８钢－聚有机硅氧烷仿生减粘降阻复合涂层的表面润湿性、磨料磨损特性及对土壤的减粘降阻性能与金属材料相比，仿生复合涂层的表面憎水性显著提高，水在其表面上的接触角达９２°；与４５钢相比，其磨料磨损的体积相对耐磨系数为６３％，降阻率达１５．２２％～２２．２７％     

Improving Wear Resistance of the Ni-base Thermal Spray-Welding Coating Using Rare Earths

ＩｍｐｒｏｖｉｎｇＷｅａｒＲｅｓｉｓｔａｎｃｅｏｆｔｈｅＮｉｂａｓｅＴｈｅｒｍａｌＳｐｒａｙＷｅｌｄｉｎｇＣｏａｔｉｎｇＵｓｉｎｇＲａｒｅＥａｒｔｈｓＺｈａｉＧｕａｎｇｊｉｅ（翟光杰）（ＩｎｓｔｉｔｕｔｅｏｆＰｈｙｓｉｃｓ，ＡｃａｄｅｍｉｃａＳｉ...     

埋地管道涂层检测技术现状

文章对各种埋地管道涂层检测技术进行了综述,并指出了各种技术的优缺点及应用前景.     

SiC（w）／TZP＋mullite陶瓷复合材料界面和组成设计与力学性能

本文从理论上分析了ＳｉＣ（ｗ）ＴＺＰ＋ｍｕｌｌｉｔｅ（ｐ）复合材料界面残余热应力及其在基质内的分布规律。提出在ＳｉＣ（ｗ）表面涂复Ａｌ２Ｏ３和在ＰＺＴ中加入ｍｕｌｌｉｔｅ（ｐ）联合作用来降低晶须／基质界面残余热应力的界面设计方案，导出ＳｉＣ（ｗ）和ｍｕｌｌｉｔｅ（ｐ）协同补强ＰＺＴ的匹配条件。制备了ＳｉＣ（ｗ）／ＴＺＰ＋ｍｕｌｌｉｔｅ（ｐ）复合材料并了ＳｉＣ（ｗ）表面涂层Ａｌ２Ｏ３厚度和ＳｉＣ（ｗ     

水溶性丙烯酸涂料的环氧树脂改性

本实验论述了水溶性丙烯酸钢铁底漆涂料制备、性能以及用环氧树脂对其进行改性。原水溶性丙烯酸钢铁底漆涂料在进行耐盐雾测定试验时仅为 72h ,未通过国家规定标准。本实验的目的在于 ,以丙烯酸树脂为主要成膜物质 ,加入其他的辅助成膜物质 ,如环氧树脂来改善其抗盐雾、抗腐蚀、耐候等性能。结果表明 ,一定温度下在水溶性丙烯酸钢铁底漆涂料中加入 1/ 7的环氧树脂后 ,经测定其耐盐雾性可达 10 6h ,达到了国家的规定标准