泡沫铝的动态压缩性能和吸能性研究

通过测量泡沫铝在动态和准静态压缩条件下的应力 -应变曲线 ,研究了泡沫铝的准静态和动态压缩行为以及不同应变条件下的吸能性 ,并对其应变率效应进行了分析。结果表明 ,在高应变速率和准静态压缩下 ,泡沫铝的σ -ε曲线均表现出弹性变形段、平缓段和密实段三阶段特征 ;泡沫铝的压缩性能具有明显的应变速率敏感性 ,随应变速率的提高 ,流动应力上升 ,吸能性升高     

镁合金表面喷铝防腐蚀层的微观组织分析

在AZ91D镁合金表面热喷铝，用以提高其表面的耐腐蚀性能。采用SEM，EPMA等方法对AZ91D表面喷铝扩散层的组织进行了仔细的观察与分析，发现在防腐蚀层上有大量的Mg17Al12相存在，且呈决状及非连续片状分布。经显微硬度测定，喷铝层硬度较镁合金基体高；腐蚀后这种相凸出于基体，比镁合金基体有较好的耐腐蚀性能。     

表面引发剂对熔融铝合金直接氧化生长的影响

为了控制熔融铝合金直接氧化法制备Al2O3/Al复合材料的氧化生长,采用ZnO,SiO2和MgO3种表面引发剂,研究它们对Al-Si-Zn合金氧化生长过程及Al2O3/Al复合材料组织形貌的影响.结果表明:与未使用引发剂时相比,使用SiO2,ZnO或MgO表面引发剂制备的粉末都能显著地缩短Al-Si-Zn合金的氧化生长孕育期,提高合金氧化生长速率,改善复合材料的胞状生长方式,提高复合材料的组织均匀度和致密度,为实际生产应用提供了依据.实验发现:ZnO表面引发剂的使用效果最为突出,其最佳添加量为12mg/cm2.     

蒸馏与减粘热联合装置的设备腐蚀及防护

介绍了锦西石化分公司南蒸馏与减粘热联合装置炼制辽河高酸值原油及带炼高硫进口油在 2 0 0～40 0℃范围内对设备、管线和阀门的腐蚀特点、腐蚀机理以及针对高温环烷酸腐蚀所采取的防护措施。通过试验和理论分析 ,提出了应用新材料和新工艺解决减粘后高温渣油系统的腐蚀及低温露点腐蚀的建议     

Oscillating Cup Viscosity Measurements of Aluminum Alloys: A201, A319 and A356

An oscillating cup viscometer was developed to measure the absolute viscosities of molten metals. Previous experiments established the capability of the apparatus to characterize the viscosities of molten nickel-based superalloys. However, modifications to the instrument and its theoretical analysis were required for reliable measurements on molten aluminum alloys, presumably due to their lower densities and lower viscosities. The theoretical literature for the fluid flow inside an oscillating cup is reviewed, and a working equation without any correction factor is developed for the improved viscometer. Some design parameters of the viscometer that directly affect the accuracy of viscosity estimation by using the working equation are discussed. A special vertical furnace was adopted to uniformly heat a longer cylindrical sample (10 mm inner diameter and 120 mm length) with a temperature difference of less than 2°C over the sample length. The measuring procedure was also improved to get more accurate motion parameters. It is estimated that the working equation and improved instrument provide an uncertainty of less than 4%. In addition, applications and experimental data are presented for pure aluminum and three aluminum alloys: A201, A319, and A356.     

Crack growth in aluminium alloy sheet material under flight-simulation loading

Crack propagation tests were carried out on 2024-T3 sheet specimens to study the effects of omitting low-amplitude cycles from the gust-dominated TWIST load sequence (MiniTWIST) and the removal of small load ranges from the manoeuvre-dominated FALSTAFF load sequence (short FALSTAFF). In other tests high-amplitude loads of TWIST and MiniTWIST were truncated at different levels. The results are compared with data from similar test programmes, including crack initiation. Attention is paid to unstationary crack growth retardation and a transient retardation during initial crack growth started by an artificial crack.     

铝合金薄板尖边缘缺口试样的机械加工方法及缺口敏感性测试

介绍高强度铝合金薄板的尖边缘缺口拉伸试样的机械加工方法，用该方法制备的仿美７０７５、美制７０７５、国产ＬＣ４、ＬＣ９、ＬＹ１２、ＬＢ７３３等６种铝合金１６种热处理状态下的ＥＮ试样，其内率半径Ｒ满足了ＡＳＴＭＥ３３８－６８标准方法中Ｒｍａｘ０．０１８毫米的要求，并且达到Ｒ＜０．０１０毫米的特高精度。同时，还对仿美７０７５、美制７０７５、国产ＬＣ４的６种热处理状态下的缺口敏感性和宏观断口、以及选择仿美７０７５、ＬＹ１２对扫描断口形态进行了研究。     

静态水热脱铝处理对HZSM-5分子筛的结构、酸性和催化性能的影响

开发了一种静态水热脱铝的方法。HZSM-5经此法处理后,正戊烷的裂解活性增加,脱氢和芳构化性能加强。可用改变处理温度的方法来控制脱铝的程度。用XRD和吡啶吸附红外技术进行了研究。HZSM-5分子筛催化剂性能的变化用非骨架铝产生的强L酸中心来解释。     

铝活塞余热淬火和自然时效的应用研究

图 1所示的活塞试件 ,在开型时间为 5 0s～ 5 5s时 ,其表面温度为 (4 90± 5 )℃ ,可满足淬火要求。自然时效时间为 2 4天时 ,其机械性能可达到国标技术要求。这种新工艺有明显的经济效益。     

关于彩涂压型钢板构件设计中的选材问题

近年来 ,在彩涂压型钢板构件设计应用中 ,由于不重视、不了解如何合理选材 ,在实际工程的材料订货中也都不提出对材料性能的技术要求 ,致使供货材质、材性不能满足使用要求 ,存在降低彩板构件承载力或减少其使用寿命的隐患 ,应引起设计人员的注意。同时对当前如何按使用条件及材料供应条件合理地选定彩板材料的性能技术要求 ,包括基板钢材的级别及力学性能、板厚及公差控制要求、镀锌层质量与彩涂层类别以及参照的技术标准等 ,提出了一些建议 ,供设计应用参考。最后还对板的强度、厚度以及镀铝锌板的选用问题进行了讨论