High cycle fatigue behaviour of Ti–6Al–4V alloy at elevated temperatures

High cycle fatigue behaviour of Ti–6Al–4V alloy was studied at 623 K and 723 K. Fatigue strength decreased at elevated temperatures compared with at ambient temperature. In the short life regime, fatigue strength was lower at 723 K than at 623 K, but in the long life regime it was nearly the same at both temperatures. At elevated temperatures, cracks were generated earlier at applied stresses below the fatigue limit at ambient temperature, indicating lowered crack initiation resistance. Small cracks grew faster at elevated temperatures than at ambient temperature, which became more noticeable with increasing temperature. After allowing for the elastic modulus, small cracks still grew faster at elevated temperatures.     

Processing study of a high temperature adhesive

An adhesive-bonding process cycle study was performed for a polyimidesulphone. The high molecular weight, linear aromatic system possesses properties which make it attractive as a processable, low-cost material for elevated temperature applications. The results of a study to better understand the parameters that affect the adhesive properties of the polymer for titanium alloy adherends are presented. These include the tape preparation, the use of a primer and press and simulated autoclave processing conditions. The polymer was characterized using Fourier transform infrared spectroscopy, glass transition temperature determination, flow measurements, and weight loss measurements. The lap shear strength of the adhesive was used to evaluate the effects of the bonding process variations.     

Structure and properties of polyimide‐bonded magnets processed from prepolymers based on diacetyl derivatives of aromatic diamines and dianhydrides

We report a novel method of polyimide (PI) synthesis from prepolymers based on dianhydrides and diacetyl derivatives of aromatic diamines that facilitate the preparation of a melt processable mixture at 300 ± 10°C of the prepolymer and magnetic Nd‐Fe‐B alloy to provide PI‐bonded magnets with enhanced properties. It is shown that chemical structure of the prepolymers strongly influences viscosity behavior via crystallization of the oligoimide in the melt, leading to formation of PI with rigid‐rod like structure. This structural ordering of the prepolymers based on diacetyl derivative of diamine used in this study, if not controlled, leads to exponential increase of melt viscosity with time, making it practically impossible to prepare melt processable mixture of the magnetic particles and the PI prepolymers at elevated temperatures. The results obtained demonstrate that appropriate dianhydrides and diacetyl derivatives of diamines that do not lead to crystallization of oligoimides in prepolymer mixture can be used under controlled processing conditions to prepare melt‐processable PI‐bonded magnets containing rigid‐rod like PI structure that significantly increases thermal stability of the magnets. The temperature dependencies of the magnetic properties of the PI‐bonded magnets under conditions that they are likely to encounter during their service life were found to be remarkably similar to that of commercial thermoplastic magnets such as injection‐molded nylon magnets. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 478–485, 2006     

非金属电镀用导电漆的研制

介绍了导电漆、作为导电填料的片状镀银铜粉的制备工艺流程。分别研究了漆膜表面单位电阻与镀银铜粉的含量及其粒径以及钛酸酯偶联剂的含量之间的关系。结果表明,当镀银铜粉的粒径为400目、质量分数在57%~65%之间,钛酸酯偶联剂的质量分数为10%时,所得涂膜的导电性能最佳。加入含C-18的油酸可以使导电漆长期贮存而电阻值不变。经检测,所得涂膜具有良好的性能:附着力1级,硬度1 H,柔韧性1 mm,冲击强度50 kg/cm2,膜厚10~15μm,漆膜表面每厘米电阻0.15Ω,每分米电阻0.47Ω。指出了导电漆应用过程中的注意事项。     

Reserve estimation of an open pit mine under price uncertainty by real option approach

Reserve estimation is a key to find the correct NPV in a mining project. The most important factor in reserve estimation is the metal price. Metal price fluctuations in recent years were exaggerated, and imposed a high degree of uncertainty to the re-serve estimation, and in consequence to the whole mine planning procedure. Real option approach is an efficient method of deci-sion making in the uncertain conditions. This approach has been used for evaluation of defined natural resources projects until now. This study considering the metal price uncertainty used real option approach to prepare a methodology for reserve estimation in open pit mines. This study was done on a copper cylindrical deposit, but the achieved methodology can be adjusted for all kinds of deposits. This methodology was comprehensively described through the examples in such a manner that can be used by the mine planners.     

Evolution of insoluble eutectic Si particles in anodic oxidation films during adipic-sulfuric acid anodizing processes of ZL114A aluminum alloys

The effects of insoluble eutectic Si particles on the growth of anodic oxide films on ZL114A aluminum alloy substrates were in-vestigated by optical microscopy (OM) and scanning electron microscopy (SE...     

铜离子印迹改性壳聚糖海绵的制备及应用研究

以醋酸铜为模板,甲醇、氯仿为溶剂,2-乙烯吡啶、丙烯酰胺为功能单体,乙二醇二甲基丙烯酸酯为交联剂,采用本体聚合法制备铜离子印迹聚合物;然后掺入到壳聚糖海绵的制备中,使壳聚糖海绵对铜离子的吸附率由27．1％提高到72．3％。制备的铜离子印迹改性壳聚糖海绵需要2d达到吸附平衡,吸附-解吸5次后,性能稳定。     

Thermophysical properties of a Ti–44%Al–8%Nb–1%B alloy in the solid and molten states

The families of titanium aluminide intermetallic alloys have attractive high temperature mechanical properties which make them potential candidate materials for a wide range of applications, particularly in the aeronautic and automobile sectors. The development of appropriate manufacturing techniques is an essential stage in the engineering exploitation of these materials, e.g., Induction Skull Melting is one of the techniques which needs to be optimised for the casting of titanium aluminides. Research is underway to develop a computer model of this process but data are required for the key thermophysical properties. Pulse-heating techniques have been used to measure properties for the Ti–44Al–8Nb–1B system. Rectangular samples have been prepared and are resistively heated as part of a fast capacitor discharge circuit. Time-resolved measurements with sub-μs resolution of currents through the specimen were made with a Pearson probe current monitor using the induction principle. Voltages across the specimen were determined with knife-edge contacts and voltage dividers, and radiance temperatures of the sample were measured with a pyrometer. These measurements allow the calculation of specific heat and dependencies between enthalpy, electrical resistivity and temperature of the alloy up into the liquid phase. Data for thermal diffusivity have been obtained by using the Wiedeman–Franz relation. The results are compared with those obtained using DSC and the four-probe method to measure the temperature dependence of the resistivity.