铝活塞余热淬火和自然时效的应用研究

图 1所示的活塞试件 ,在开型时间为 5 0s～ 5 5s时 ,其表面温度为 (4 90± 5 )℃ ,可满足淬火要求。自然时效时间为 2 4天时 ,其机械性能可达到国标技术要求。这种新工艺有明显的经济效益。     

非晶Sm5Fe74.3Nb1.5Si11.7B4.5C2.5Cu0.5合金经预退火后的晶化动力学的DTA研究

研究了非晶Sm5Fe74.3Nb1.5Si11.7B4.5C2.5Cu0.5合金经400℃，保温10min预退火后的晶化动力学。结果表明；该合金的晶化相为α-Fe固溶体和Sm2Fe17Cx金属间化合物，两相的晶化表观激活能分别为557KJ/mol和514KJ/mol，当晶化体积分数为60%时，α-Fe相的晶化激活能达极大值；Sm2Fe17Cx相晶化激活能则随其晶化体积分数的增加而逐渐减小。     

压力对Fe－29wt％Ni合金超细微粒特性的影响

利用蒸发冷凝法，制备了不同平均粒径的Ｆｅ－２９ｗｔ％Ｎｉ合金超细微粒。在不同压强下，将超细微粒压制成片。随压强增大，马氏体体积分数和比饱和磁化强度σｓ明显增大，而矫顽力Ｈｃ呈线性下降。压力效应与平均粒径ｄ大小密切相关     

Direct electroless Ni-P deposition on AM50 magnesium alloy from sulfate bath

A bright electroless Ni-P deposition on AM50 magnesium alloy in a sulfate plating bath was proposed by using direct plating process with non-chromate pretreatment. The electroless Ni-P plating on AM50 magnesium alloy has an admirable appearance and good adhesion. The results indicate that the electroless Ni-P deposition with non-chromate pretreatment has better adhesion than that of zinc immersion coating. Anodic polarization curves indicate that the electroless Ni-P deposition obtained from the sulfate bath has similar corrosion-resistance to that obtained from basic nickel carbonate bath. The deposition process generates less pollutant by a non-chromate plating bath and is suitable for the magnesium alloys manufacture because of its low cost. The hardness of the electroless Ni-P plated AM50 is about HV 720.6 and HV 969.7 after heat treatments at 180℃ for 2 h. The wear resistance of Ni-P plated magnesium alloy specimens is about 5 to 9 times as high as that of bare magnesium alloys.     

热强钛合金BT25组织与性能

介绍了前苏联航空发动机用热强钛合金（或高温钛合金）BT25的发展概况，并对BT25合金的成分特点、热处理强化优点等做了进一步阐述，给出了退火状态下的物理性能，在说明热强钛合金微观组织与力学性能关系的基础上给出了BT25合金的各种力学性能。     

铜基催化剂孔隙率对气体有效扩散系数的影响

研究了18种具有不同孔结构参数的粒状铜基甲醇合成催化剂孔隙率对有效扩散系数的影响。结果发现，催化剂微孔孔隙率增大，曲节因子亦增大，扩散阻力增加。将孔隙率与催化剂曲节因子关联，得到了半经验方程，用它可估算催化剂的曲节因子。     

Catalyst instabilities during the liquid phase partial oxidation of methane

A promising catalytic system for the low temperature oxidation of methane to a methanol derivative has been investigated under both batch and semi-continuous operation in two different reactor types. The system comprises of a bimetallic palladium and copper(II) chloride catalyst contained in a trifluoroacetic acid (TFA) and an aqueous phase. Methane, oxygen and a co-reductant carbon monoxide constitute the gas phase. Typical operating conditions were a temperature of 85 °C and a pressure of 83 bar.

The yields of the methyl trifluoroacetate product observed in this present work were less than those obtained in other batch autoclave works, which employed only 4 ml of liquid phase, compared with 50 ml in this study. Furthermore, an encouraging initial product formation rate of ca. 40 mol/m³ h, quickly decreased after the first hour, and came to an apparent end after only 2 h. This observation had not been reported previously.

Work performed in a semi-continuous porous tube reactor (300 ml of re-circulating liquid phase) also showed the same reaction characteristics as in the batch reactor. Thus, the deteriorating product formation rate cannot be attributed to gaseous reactant depletion (batch operation). The results suggest problems associated with catalyst instabilities, e.g. with the previously elucidated Wacker chemistry.     

电解铜箔产业发展趋势

随着技术的进步,电解铜箔在厚度上迅速向薄、超薄方向发展,THE、RCC、CAC等特殊性能铜箔需求比例快速 增加,以锂离子电池为代表的新应用领域正在形成。     

纯铜双层辉光离子渗钛组织形成机理及性能分析

采用双层辉光离子渗金属技术对纯铜进行了渗钛处理。用配有能谱仪(EDS)的扫描电子显微镜(SEM)、X射线衍射仪和透射电子显微镜对合金层的显微组织形貌、钛含量分布、相组成及相结构类型进行了观察与测定，对合金层的形成机理进行了探讨，并对其性能进行了对比测定。结果表明：渗钛层由合金层和扩散层组成，合金层主要由TiCu (Cu)固溶体 TiCu4构成，TiCu4为Dla型有序相，TiCu为B2型有序相，扩散层为(Cu)固溶体。渗钛处理后纯铜的表面得到显著强化。     

Homogeneous Plastic Flow of Fully Amorphous and Partially Crystallized Zr_(41.2)Ti_(13.8)Cu_(12.5)Ni_(10)Be_(22.5) Bulk Metallic Glass

The homogeneous plastic flow of fully amorphous and partially crystallized Zr(41.2)Ti(13.8)Cu(12.5)Ni(10)Be(22.5) bulk metallic glass (Vitl) has been investigated by compression tests at high temperatures in supercooled liquid region. Experimental results show that at sufficiently low strain rates, the supercooled liquid of the fully amorphous alloy reveals Newtonian flow with a linear relationship between the flow stress and strain rate. As the strain rate is increased, a transition from linear Newtonian to nonlinear flow is detected, which can be explained by the transition state theory. Over the entire strain rate interval investigated, however, only nonlinear flow is present in the partially crystallized alloy, and the flow stress for each strain rate is much higher. It is found that the strain rate-stress relationship for the partially crystaltized alloy at the given temperature of 646 K also obeys the sinh law derived from the transition state theory, similar to that of the initial homogeneous amo