通过添加适量CuO和Bi2O3，将Ni-Zn铁氧体材料的烧结温度降至870—920℃，达到Ni-Zn铁氧体材料与Ag电极共烧匹配的目的。试制了片式抗电磁干扰滤波器，并对其插入损耗特性进行了计算机模拟，表明所研制的抗电磁干扰滤波器不仅适合高密度表面封装技术的要求，也可满足宽频域抗电磁干扰需要。     

Electromagnetic properties of ferroelectric-ferrite ceramic composites

The NiFe₂O₄ and Pb(Zr_0.52Ti_0.48)O₃ ceramic composites are prepared by conventional solid state reaction method. The microstructural and morphological properties of the composites are studied by X-ray diffraction analysis and scanning electron microscopy. Results indicate that the ferrite and piezoelectric phases can co-exist in the composites. The relationship between the dielectric constant and frequency (40 Hz–40 MHz) as well as temperature is also investigated. It is noted that the transition temperature of the composites is about 380 °C. A double electric hysteresis loop is observed in our composites. The magnetic properties are relatively weak according to the magnetic hysteresis loop. With increase in the content of the ferrite phase, the permeability increases. The electromagnetic properties of the as-prepared composites are tunable according to the content of the NiFe₂O₄ phase.     

锰锌铁氧体纳米粉体的液相制备及磁性能

以δ-FeOOH为前驱体,用氨水调节溶液的pH值,分别采用(1)90℃水浴加热动态转化、(2)沸腾回流动态转化,(3)90℃静态转化及(4)200℃水热法四种方法合成了锰锌铁氧体纳米粉体.采用X射线衍射仪(XRD),透射电子显微镜(TEM)、振动样品磁强计(VSM)和X射线荧光光谱仪(XRF)等方法对粉体进行了表征,对四种液相法制备的锰锌铁氧体纳米粉体的结构和性能等进行了对比和分析.结果表明,四种方法中沸腾回流相转化法得到的产物具有磁性能较好、形状较规则、粒径可控等优点.     

首钢“川气出川”工程用17.5mmX70管线钢的试制

介绍了首钢试制17.5mm规格高强度、高韧性X70管线钢的生产工艺（成分设计、炼钢和轧钢工艺）及产品的力学性能。在华油钢管厂完成制管（管径为1016mm）以及相应的检验后，所有性能指标全部达到“川气出川”管道工程的技术规范要求。     

共沉淀法制备锰锌软磁铁氧体前躯体共沉过程中钙、镁深度脱除的热力学分析

通过对Fe(Ⅱ)-Mn(Ⅱ)-Zn(Ⅱ)-Ca(Ⅱ)-Mg(Ⅱ)-NH3-NH4HCO3-H2O体系的热力学分析，得到各金属离子浓度与pH的关系，从而确定共沉法制备锰锌软磁铁氧体前躯体共沉过程中钙、镁深度脱除的共沉区域。热力学分析结果表明，溶液中钙、镁的含量随着体系pH的增大而降低，在相同条件下镁的溶解度大于钙的溶解度。为减少进入共沉粉中的钙、镁含量，需要保证在铁、锰、锌共沉完全的基础上降低体系的pH。当溶液中[C]T=0．1mol／L，[N]T=1．0mol／L时，pH控制在6．23～6．50之间可以大大降低进入共沉粉中的钙、镁含量。确定共沉过程钙，镁深度脱除的共沉区域，对于生产高纯锰锌软磁铁氧体前躯体具有重要的指导意义。     

Miniaturization and bandwidth enhancement of a cavity backed circular microstrip patch antenna

The resonant frequency of a circular patch antenna with and without circular cavity is measured. The patch miniaturization in the presence of the cavity is proved. Different methods of reducing resonant frequencies and broadening bandwidth without significantly reducing antenna gain are presented. Capacitively loaded patch and slits on the patch stimulate the patch at lower frequencies and multiple resonances, thus help miniaturization. Finally ferrite loading on the feed probe further increases the bandwidth without significantly reducing the antenna gain. The method is much more improved than that for a resistive loaded patch and a deformed patch. © 2007 Wiley Periodicals, Inc. Int J RF and Microwave CAE, 2007.     

ST－4型节能全自动辊道双推板窑

ＳＴ－４型全自动辊道双推板窑是为永磁铁氧体规模生产而研制的一种节能型空气烧结窑。它根据永磁铁氧体烧结的工艺要求，设计了合理的温区，使规模生产烧结成品率达９５％以上；采用辊道推板相结合的窑床形式与复合保温结构，达到了永磁铁氧体能耗１．２ｋｗｈ／ｋｇ；采用优化设计，使设备性能先进，稳定可靠。     

连铸高铝氮积齿轮钢第三脆性区形成机制与控制

钢中的Al、N含量对连铸及其后续加工热塑性和奥氏体晶粒度控制有重要影响,这也是高温渗碳钢与各种Al脱氧钢广泛关注的问题。使用Gleeble 3800热/力学模拟试验机测定了一种轨道交通用高铝氮积齿轮钢(SCM420H)的高温热塑性,并结合差示扫描量热仪(DSC)分析、AlN析出热力学模型以及Schwerdtfeger热塑性特征值计算模型揭示了其第三脆性区的形成机制与调控途径。结果表明,高铝氮积齿轮钢第三脆性区低谷温度范围为750~850 ℃,这是由应力诱导先共析铁素体膜的产生与AlN粒子的大量析出共同导致的。Schwerdtfeger热塑性特征值计算模型可以较准确地预测高铝氮积齿轮钢第三脆性区的上限温度与最小面缩率,但由其预测的热塑性曲线下限温度偏高,应进一步考虑先共析铁素体膜析出的影响,并依据Ar3温度对其进行修正。高Al高N齿轮钢第三脆性区的下限温度取决于其先共析铁素体开始析出温度,主要与钢种成分和铸坯冷却速率相关,连铸生产中可控性有限;但其上限温度则与铸坯应变速率、冷却速率以及钢中的Al、N含量和AlN析出行为均有关联,调控空间较大,应该是连铸生产中合理控制铸坯热塑性与表面裂纹倾向的正确途径。     

控轧控冷工艺对高强度锚杆钢组织和性能的影响

随着矿井深度的增加,对锚杆支护强韧性的要求越来越高,为了应对这一情况,需要研发出更高强度的锚杆钢。利用锚杆钢研究了轧制工艺、冷却工艺与珠光体、铁素体相比例,析出相析出行为及力学性能的关系。研究结果表明,在中轧后、精轧前采用适当水冷+回复段处理的复合工艺可使晶粒更细小、组织更均匀。对超高强度锚杆钢进行热压缩变形试验,由热模拟试验结果确定相转变温度为A_c1=737 ℃、A_c3=886 ℃。最终筛选出入精轧温度为810 ℃、回复段温度为800 ℃时,可获得的晶粒尺寸达4 μm,珠光体体积分数为66.8%,铁素体体积分数为33.2%,珠光体片层间距达200 nm;另外调整V、Cr、N等析出以提高锚杆钢的强韧性,较低的回复温度有利于细小、弥散、V(C/N)析出相的析出,V(C/N)的析出可进一步改善锚杆钢的力学性能。由该控轧控冷工艺轧制的锚杆钢屈服强度为780 MPa、抗拉强度为930 MPa、硬度为291HV、伸长率为20%。     

X80管线钢埋弧焊匹配焊丝试验

通过分析高强度低合金钢焊缝熔敷金属常见显微组织对其力学性能的影响,确定X80管线钢用埋弧焊丝熔敷金属组织应以大量针状铁素体(AF)和少量粒状贝氏体(GB)的复合组织.从相变动力学原理出发,结合针状铁素体(AF)非自发形核机制和微合金组织韧化理论,选择Mn-Ni-Mo-Ti-B合金系进行X80管线钢匹配焊丝的试制.结果表明,合理选择和控制合金元素,可以获得理想的焊缝熔敷金属组织和强韧性以及低温韧性要求,试制的1号焊丝能够满足X80管线钢的使用要求.