腐蚀磨损过程中材料的环境脆性

从腐蚀磨损的交互作用、腐蚀磨损与应力腐蚀及氢脆的异同出发，论述了磨损加速腐蚀及腐蚀加速磨损的微观机制，指出材料的环境脆性与腐蚀对磨损的加速作用程度有关．从腐蚀对磨损的加速作用、比能耗、磨痕硬度等方面分析了不锈钢 Cl^-体系、Ni-P镀层 NaOH溶液、H4340钢与Ti6A14V合金 稀硫酸溶液体系、铜合金 NH4^ (NH3)或S^2-溶液中的环境脆化行为和规律，总结出材料环境脆性的力学判据，展望了今后腐蚀磨损的研究方向．     

Influence of Polyalkylmethacrylate VII on Boundary Film Formation,Friction,Wear and Efficiency of Lubricants

1 Influence of PAMAon Boundary Fil mFormation and Friction1.1 Experi mental methodsUltra-thin optical interferometry has been used tostudy thinlubricating fil ms for more than a decade and theexperi mental details of this technique have been reportedpreviously[1].The principle of the test setup is shown inFigure1.A polished steel ball is loaded and rolled againstthe flat surface of a glass disc that is coated with a thinsemi-reflecting chromiumlayer and a silica spacer of about500nmthickne…     

热作模具钢表面激光堆焊耐磨合金层的研究

本文主要通过在H13钢上用大功率CO_2激光束进行堆焊,阐述了激光堆焊工艺变化对堆焊组织和性能的影响,在本试验条件下,得到了高密度弥散金属化合物组织的激光堆焊层,平均硬度为HV800,与基体呈冶金结合,耐磨性比H13模具钢提高149%。     

新世纪我国压铸业与国际接轨的思考

针对中国压铸行业的现状和存在的问题 ,以及当前的机遇和面临的挑战 ,论述了中国压铸工业进入 2 1世纪所面临的新形势及应采取的对策     

激光熔覆Ni基SiC合金涂层组织与性能的研究

利用5kWCO2连续波激光器在16Mn钢基材表面对含20%(体积比)SiC陶瓷粉末的镍基自熔性合金粉末进行激光熔覆得到Ni基SiC合金涂层(NiSiC)。研究了合金涂层的组织形貌及相结构,并用单纯的镍基合金涂层(Ni60)进行了显微硬度及滑动磨损性能的对比试验。结果表明,NiSiC合金涂层由γ枝晶及其间的共晶组织组成,主要组成相为γ-Ni,γ-(Ni,Fe)固溶体和(Cr,Fe)7C3,Cr23C6及(Cr,Si)3Ni3Si等化合物。添加SiC的镍基合金涂层NiSiC比单纯的镍基合金涂层Ni60具有较高的硬度和耐磨性。     

浅谈冲压模具的维修要领及常见故障的排除

介绍冲压模具修理和检查各环节的主要工作内容及维修要领 ,列举了常见故障的排除方法 ,通过总结实际生产中的修模经验 ,对缩短修模周期 ,降低成本 ,延长模具寿命有一定的参考价值。。     

PVD涂层工艺在M3滚刀上的应用

对M3滚刀进行了物理气相沉积 (PVD)工艺试验。经高温耐磨试验和切削试验证明 ,M3滚刀经TiN涂层后 ,其耐磨性和使用寿命显著提高。     

Study of Friction and Wear Performance of Zinc Dialkyldithiophosphate in the Presence of Trace Ketone

This study reports the influence of methyl isopropyl ketone on the tribological performance of zinc dialkyldithiophosphate. The lubricity and friction and wear tests of 500 SN neutral base stock oil containing zinc dialkyldithiophosphate with methyl isopropyl ketone were carried out by MQ-800 four-ball and MM-200 block-on-ring tribometers respectively. The experimental results show that methyl isopropyl ketone decreases the wear resistance and the load-carrying capacity of zinc dialkyldithiophosphate. The friction reduction of zinc dialkyldithiophosphate was lowered as well because of the addition of ketone. The friction and wear mechanism of zinc dialkyldithiophosphate with trace ketone was studied by optical microscopy IR, SEM, XPS and ferrography. The variations of the tribological performance of zinc dialkyldithiophosphate with ketone could be partly attributed to the decreases of active species, such as phosphorus and zinc, which are responsible for the formation of anti-wear films, on the rubbing surface due to the existence of ketone.     

超大型材生产经验

对几种超大型材挤压生产的工艺技术、工模具设计、挤压参数控制等过程进行了分析，通过例子总结了挤压生产超大型材的经验及关键技术。     

邻苯二甲酸酯鼓泡生物降解

该课题测试了邻苯二甲酸酯类化合物的鼓泡生物降解行为。结果表明，邻苯二甲酸酯的降解速率常数（kb)与其烷基链长度之间存在良好的相关性，kb=0.0009x^2-0.019x 0.1123，相关系数r=0.9906；浓度超过500mg/L时，邻苯二甲酸二乙酯可抑制自身的生物降解；中间产物邻苯二甲酸浓度超过50mg/L时，也对邻苯二甲酸二乙酯的生物降解有明显的抑制作用。