钴酸锂的再生及其电化学性能

采用提取的含少量Co3O4的LiCoO2为原料,在不同温度下合成正极材料LiCoO2,烧结时间为12 h,并采用XRD和SEM技术研究合成的LiCoO2的晶相结构与微观形貌。结果发现:烧结温度对LiCoO2的晶体结构影响较大,烧结温度越高,LiCoO2的层状结构发育越完整。循环伏安曲线很好地反映了再生LiCoO2的脱/嵌锂行为。将LiCoO2样品做成电池进行电化学检测,结果发现,烧结温度为850℃的样品首次放电容量为151mA.h/g,30次循环之后,放电容量仍有141mA.h/g,表现出良好的电化学性能。     

气体雾化贮氢电极合金Ml（Ni,Co,Mn,Ti）5的活化性能

研究了感应熔炼后随炉冷却和经不同处理的气体雾化贮氢电极合金Ｍｌ（Ｎｉ，Ｃｏ，Ｍｎ，Ｔｉ）５的电化学活化特性。结果表明，氢化前后合金内能的变化是影响活化性能的原因，因表面覆盖氧化膜或任何其它原因所引起的附加内能越大，或氢化时氢原子进入四面体或八面体间隙位置所引起应变能越大，活化越困难。     

Exploring thermal spray gray alumina coating pore network architecture by combining stereological protocols and impedance electrochemical spectroscopy

Complex multiscale pore network architecture characterized by multimodal pore size distribution and connectivity develops during the manufacture of ceramic thermal spray coatings from intra- and interlamellar cracks generated when each lamella spreads and solidifies to globular pores resulting from lamella stacking defects. This network significantly affects the coating properties and their in-service behaviors. De Hoff stereological analysis permits quantification of the three-dimensional (3D) distribution of spheroids (i.e., pores) from the determination of their two-dimensional (2D) distribution estimated by image analysis when analyzing the coating structure from a polished plane. Electrochemical impedance spectroscopy electrochemically examines a material surface by frequency variable current and potential and analyzes the complex impedance. When a coating covers the material surface, the electrolyte percolates through the more or less connected pore network to locally passivate the substrate. The resistive and capacitive characteristics of the equivalent electrical circuit will depend upon the connected pore network architecture. Both protocols were implemented to quantify thermal spray coating structures. Al₂O₃-13TiO₂ coatings were atmospherically plasma sprayed using several sets of power parameters, are current intensity, plasma gas total flow rate, and plasma gas composition in order to determine their effects on pore network architecture. Particle characteristics upon impact, especially their related dimensionless numbers, such as Reynolds, Weber, and Sommerfeld criteria, were also determined. Analyses permitted identification of (a) the major effects of power parameters upon pore architecture and (b) the related formation mechanisms. This article was originally published inBuilding on 100 Years of Success, Proceedings of the 2006 International Thermal Spray Conference (Seattle, WA), May 15–18, 2006, B.R. Marple, M.M. Hyland, Y.-Ch. Lau, R.S. Lima, and J. Voyer, Ed., ASM International, Materials Park, OH, 2006.     

Electrochemical properties of AB5 type hydrogen storage alloy as anode electrocatalyst of PEMFC

1　INTRODUCTIONIn recent years, the application of the roomtemperature type ( < 100 ℃) polymer electrolytemembrane fuel cells(PEMFCs) as a primary powersource in electric vehicles and portable equipmentsetc has received increasing attention[1 4]. Usuallyin a PEMFC system, platinum is chosen as the e lectrode electrocatalyst, however, it results in ahigh cost PEMFC system for commercialization be cause Pt is a high cost, source limit metal. So,looking fo…     

一种计算氢扩散系数的新方法

利用电化学氢渗透曲线来计算室温附近氢在金属中的扩散系数是一种广为应用的方法。从理论上讲,在氢渗透曲线上的任何一点上都可以计算出氢在金属晶格中的扩散系数。但是从实际获得的氢渗透曲线各点算得的氢扩散系数并不一致。这是因为在金属中,一般都不可避免地存在一些氢的陷阱,如位错、晶界、杂质原子等,它们会不同程度地阻碍氢在金属晶格中的扩散过程。而理论推导本身并没有考虑到氢陷阱存在的影响,因此实际得     

铝阳极氧化膜在NaCl溶液中的电化学性能

采用交流阻抗法研究了工业纯铝L3阳极氧化膜在中性NaCl溶液中交流阻抗谱的变化规律, 比较了未封闭处理与沸水封闭处理后氧化膜的交流阻抗谱的差异, 并结合等效电路分析了氧化膜多孔层与阻挡层电化学参数的变化.结果表明, 未封闭的阳极氧化膜在NaCl溶液中浸泡初期存在一个自封闭过程, 封闭处理明显提高氧化膜多孔层的初始Rp值并降低初始CPEp值; 溶液中侵蚀性离子浓度越高, 封闭处理提高铝阳极氧化膜的耐蚀性能作用越明显.     

脉冲电化学光整加工的流场及间隙特性

通过系统的试验研究，分析了工作液流场分布、流量、加工间隙等工艺参数对加工质量的影响。研究结果表明：合理控制加工间隙和工作液流场分布，对保证加工表面的质量极为重要；在优选的工艺参数下，可快速获得优质表面。     

Preparation and electrocatalytic properties of tungsten carbide electrocatalysts

1　ＩＮＴＲＯＤＵＣＴＩＯＮ ｉｎ 1 5 0℃ .Ｍａａｓ[1 0 ] ａｌｓｏｍａｎｕｆａｃｔｕｒｅｄｔｈｅＨ2 Ｏ2 ｆｕｅｌｃｅｌｌｓｔａｃｋｓｗｉｔｈｔｈｅｏｕｔｐｕｔｐｏｗｅｒｕｐｔｏ 1ｋＷ ,ａｎｄｔｈｅｐｒｏｐｅｒｔｉｅｓｏｆｔｈｅａｓ ｐｒｅｐａｒｅｄｆｕｅｌ     

铸态Mm(NiCoMnAl)5.1Bx贮氢合金电化学性能研究

本文研究了B含量对铸态非化学计量比贮氢使合金Mm(NiCoMnAl)5.1Bx的相结构及其电化学性能的影响。结果表明，加B合金中除了CaCu5相以外还含有一定量的第二相MmCo4B，且随着B元素含量的增加而增加；B的加入有利于提高合金的活化性能和高倍率放电性能，合金的循环寿命亦有所提高，但不利于合金的放电容量和放电电压性能。     

碳钢在流动3%氯化钠溶液中的腐蚀机理的探讨

本文利用自行设计的模拟流动状态的装置,研究了碳钢在流动3%NaCl溶液中的腐蚀规律及施加阴极电流后对腐蚀的影响。结果表明:随着相对流速的增大,碳钢的腐蚀随之加剧,并发现存在一个临界相对流速值。当相对流速小于此值时,腐蚀主要受电化学因素影响。而相对流速大于此值时,流体力学因素开始明显起主导作用,并与电化学因素间的协同效应增强,导致腐蚀速度急剧上升。施加阴极电流后,不仅抑制了电化学因素引起的腐蚀,而且大幅度地削弱了电化学因素与流体力学因素间的协同效应,从而使腐蚀速度大大降低。