不连续增强镁基复合材料的界面行为

综述了近年来国内外关于Ａｌ２Ｏ３短纤维、ＳｉＣ晶须、ＳｉＣ颗粒、Ｂ４Ｃ颗粒增强镁基复合材料的界面结构及其对复合材料性能影响的研究进展，并对今后的研究提出了一些看法。     

高温合金材料在铝电解工业中的应用探讨

对高温合金在铝电解工业用作惰性金属阳极材料的选择进行阐述，并就实际应用过程中的抗氧化耐腐蚀性进行探讨；阐述适用于铝电解工业的惰性阳极合金所应具备的必要条件和必须解决的问题，并介绍目前有关的研究动态和研究方向。     

分离有机/有机混合物的PVA、CA系列膜及其渗透汽化性能研究(Ⅱ) 成膜条件对渗透汽化性能的影响

用溶剂完全蒸发法制备了PVA复合膜 .经对MTBE/MeOH混合物的分离实验得到了PVA复合膜的最佳成膜条件 ,即 :铸膜液中PVA、马来酸浓度分别为 7%、3% ,热处理温度130～ 15 0℃ .在 1%～ 2 %丙酮水溶液中浸泡处理 4～ 8h ,CTA中空纤维RO膜被改性成渗透汽化膜 .CTA中空纤维膜的分离性能优于其它醋酸纤维素系列膜 ,PVA/CA复合膜的性能优于PVA/PAN复合膜和CA/PAN复合膜     

溶胶－凝胶二氧化硅驻极体薄膜的物理化学改性

实验研究了由溶胶－凝胶法制备二氧化硅驻极体薄膜的工艺。用红外透射谱、扫描电子显微镜以及驻极体等温表面电位测量和热刺激放电等实验考察了热处理和化学表面修正两个关键工艺对溶胶－凝胶二氧化硅样品驻极体性能的影响。结果表明经过高温条件下一定时间的热处理和化学表面修正，可以制备出性能优良的驻极体薄膜     

如何辨别电影画原底片的优劣

本文提供一个简便实用的质量鉴定方法,用于在制作发行拷贝前,辨别电影画原底片的优劣。     

SiCf/O′-SiAlON composite: properties and oxidation retained properties

A composite of O′SiAlON (Si_2-xAl_xN_2-xO_1+x, with x 0.14) reinforced with 20 vol.% SiC monofilaments was fabricated by hot-pressing, at 1600°C, for 2 h under 34 MPa pressure. The mechanical and interfacial properties of the composites, as-fabricated as well as post-oxidized, were, investigated. The composite exhibited a significant improvement in ultimate flexure strength (640 MPa) and work of fracture (42 kJ m⁻²) compared with that (350 MPa and 1.8 kJ m⁻², respectively) of the monolithic material. These mechanical properties were slightly increased after the composite was heat treated for 24 h in air at 1200 and 1300°C. However, the composite exhibited a significant degradation in ultimate strength, while the work of fracture (WOF) remained unchanged after exposure in air at temperatures beyond 1400°C. The as-fabricated composite revealed a low interfacial shear strength (6.2 MPa) and a frictional sliding stress (3.2 MPa). After the composite was oxidized at elevated temperatures, the interfacial bonding and sliding stresses were reduced to noticeable extents, resulting from the degradation of the carbon coating layer of the SiC monofilaments.     

Lubricating behavior of iron rhenate and its relation to matching pairs

The iron rhenate was compounded by chemical method, which may be generated during wear process of Fe-Re alloys at elevated temperature. The friction coefficient of iron rhenate has been determined by a pin-on-disc device. The results show that iron rhenate plays role of lubricating at RT-600 °C. The lubricating behavior is related to the matching pairs. The hardness of the materials of matching pairs, compatibility of iron rhenate with materials of matching pairs and surface roughness of disc affect the lubricating behavior of iron rhenate mostly. The principle of matching pairs is proposed. Project supported by the National Natural Science Foundation of China Synopsis of the first author Xiong Dangsheng. associated professor, born in 1960. Current research fields include high-temperature self-lubricating alloys and tribological properties of material.     

铸轧5052合金冷隔缺陷产生的机理研究

阐述了5052合金铸轧坯料生产时冷隔缺陷产生的机理,结合超型FATA—HUNTERΦ1003×1850mm机多年的生产实践经验,提出了消除铸轧冷隔缺陷的措施。     

纤维表面处理对植物纤维增强水泥的物理力学性能影响

植物纤维增强水泥的力学性能具有湿敏感性，随湿度增加弯曲强度下降幅度较大。本文工作采用的几种浸渍处理纤维表面的方法，有效地改善了这种状况，其中一种经处理的纤维增强水泥较没有处理的对比试样在饱水状态下的弯曲强度提高了67％，气干状态提高了18％，缩小了二者间的差距。     

TFT有源矩阵α－Si∶H薄膜PECVD淀积工艺研究

分析了α－Ｓｉ∶Ｈ薄膜的质量和厚度对α－Ｓｉ∶ＨＴＦＴ关键性指标的影响，深入、详细地讨论了其ＰＥＣＶＤ淀积工艺，并在实验的基础上确定了最佳淀积工艺参数，从而获得了高性能的７５ｍｍ３７２×２７６像素α－Ｓｉ∶ＨＴＦＴ有源矩阵