低熔点合金填充聚合物材料断口形貌研究

研究了合金元素、加工温度、金属含量、第三组分对低熔点金属填充聚合物材料断口形貌的影响。实验结果表明:不同的合金对体系的影响很大,低分子量、低结晶性聚合物,高的成型加工温度可提高材料的相容性。     

Computation of concentrations of characteristic atoms of alloys in BCC structure

In this paper,taking Nb-Mo alloy system as an example,the equations of concentration of characteristic atoms of alloys in BCC structure were obtained on the basis of the idea of systematic science of alloys and the number of coordination atoms.The concentrations of characteristic atoms in B2-NbMo type ordered alloys were calculated as functions of ordering degree(s) and composition xMo.When s=smax,the concentrations of characteristic atoms of stoichiometric B2-NbMo intermetallic compound are equal to that o...     

铝合金中锌、铁的快速测定--原子吸收分光光度法

样品以盐酸溶解，加入过氧化氢助溶，蒸至近干．加入1 1盐酸提取，移入100mL容量瓶中，分取部分溶液于50mL容量瓶中，调整盐酸酸度为5％，用水稀至刻度，摇匀后，以空气-乙炔火焰水相直接测定锌和铁。为了消除大量基体元素的影响，在标准系列中加入相当量的铝。此方法快捷、简便，亦可用于锰、镁、铜、铅、镍的测定。     

钯－银合金膜分离氢气的研究

采用厚为５０μｍ的Ｐｄ／Ａｇ（２３）合金膜进行了氢气渗透系数的测定和Ｈ＿２／Ｎ＿２混和气分离的研究，得出温度、压力、膜厚、进料气流量、膜的预处理和再活化及膜表面中毒等因素对氢气渗透的影响。分离Ｈ＿２／Ｎ＿２混和气可获得高纯氢气。     

CJ91胶粘剂在螺旋振动光整机中的应用

螺旋振动光整机槽内壁的橡皮保护层由于老化及磨损等原因出现裂口甚至脱落现象，严重影响设备的使用寿命和闸把壳体的外观质量。通过分析和试验筛选出螺旋振动光整机的理想胶粘荆——CJ91胶粘剂并介绍了粘接修补工艺。     

Cu-Zn-Al形状记忆合金直接淬火和分级淬火后马氏体稳定性的研究SCIEI

用透射电镜,X射线衍射仪和电阻法研究了Cu-14.84wt-％Zn-7.75wt-％Al形状记忆合金在直接淬火和分级淬火后马氏体的稳定性。试验结果表明,直接淬火和分级淬火(150℃,2min)后于室温时效约3h的马氏体均为M18R结构,但刚直接淬火后马氏体并不稳定,其某些衍射峰位置和电阻率均随室温时效而变化;而分级淬火(150℃,2min)后马氏体是稳定的,其所有衍射峰位置和电阻率几乎不随室温时效而变化。上述结果可用“马氏体再有序化机制”解释。     

Large magnetic-field-induced strains in rare earth polycrystalline Ni-Mn-Ga

The magnetic-field-induced strains (MFIS) of polycrystalline Ni50Mn29Ga21 alloys containing Tb were studied. A large MFIS of-1.10% was obtained under compressive prestress conditions. The addition of Tb can fine the crystal grains, enhance the bending strength obviously, and make MFIS increase further, indicating that a moderate amount of Tb does not hinder twin boundary motion and it conversely makes the material more practical.     

镁合金废料的回收

在镁合金零部件生产过程中，特别是在压力铸造生产中，产生出来的废料以及使用后报废的镁合金零件逐渐增多。出于成本和环境因素的考虑，必须对这与日俱增的镁合金废料进行有效回收。本文以生产占90％的镁合金零部件压力铸造为主线，介绍镁合金废料回收的经济分析，镁合金废料的来源和分类、现行回收技术的现状及发展趋势。并介绍香港生产力促进局和重庆硕龙科技公司最近研究开发的一种新型镁合金废料现场精炼回收系统。