光隔离器及其相关的磁光材料

本文简要介绍了磁光隔离器的理论、结构和分类 ,并提出了该器件今后发展的几个问题 ,最后介绍了几种磁光材料     

非化学计量LaNi5型储氢合金的性能

采用富La混合稀土与Ni、Co、Mg等元素组合，获得了一种非化学计量LaNi5型储氢合金、用金相、XRD和SEM-EDX等方法分析了该合金的组织结构，研究了合金的气相储氢特性以及电化学性能，结果表明：在1.6MPa氢压和温度29℃下，该合金的储氢量达到1.58%（质量分数），该合金的放电容量为380mAh/g。经300次循环后容量保持率为55%，该合金的基体是CaCu5型结构的LaNi5相，但有第二相（LaMg)Ni3析出，这种第二相的形成是导致该合金大容量的关键。     

Continuous formation of slurry ice by cooling water–oil emulsion in a tube

Water-silicone oil emulsion with an additive, (C₂H₅O)₃SiC₃H₆NH₂, was examined as a heat storage material. A spiral tube used as a heat exchanger was immersed in a low temperature bath and the emulsion was circulated in the tube to make ice continuously. Ice was separated from the ice–liquid suspension in an outlet tank. The amount of formed ice, the temperatures of the inlet and the outlet of the heat exchanger, and the temperatures in the tube wall were measured and the overall heat transfer coefficient and the heat flux through the tube were calculated. Experiments were carried out, varying the flow rate, the temperature of cooling brine, and the thickness of tube wall. The condition under which slurry ice was formed continuously without adhesion of ice to the cooling wall was clarified. Though decrease in the thermal resistance of the tube increased the rate of ice formation or raised the brine temperature, it narrowed the range of the flow rate and of the brine temperature in which slurry ice was formed continuously.     

车用乙醇汽油调合及储运问题的探讨

简要介绍了车用乙醇汽油的组成、性质 ,阐述了车用乙醇汽油调合及储运设施的工艺设计思想 ,以及车用乙醇汽油储运设施设计中应注意的问题。     

固液相变蓄能的数学模型和自然对流换热系数的实验研究

引入自然对流换热系数 ,将固液蓄能数学模型简化为仅用能量方程加以描述。并通过实验测得相变过程的实际温度场 ,证明了自然对流固液相变换热的影响不可忽略 ,验证了固液相变界面移动速率随自然对流换热系数的增大而增大的定性关系     

Efficient Management of Persistent Knowledge

Although computer speed has steadily increased and memory is getting cheaper, the need for storage managers to deal efficiently with applications that cannot be held into main memory is vital. Dealing with large quantities of clauses implies the use of persistent knowledge and thus, indexing methods are essential to access efficiently the subset of clauses relevant to answering a query. We introduce PerKMan, a storage manager that uses G-trees, and aims at efficient manipulation of large amounts of persistent knowledge. PerKMan may be connected to Prolog systems that offer an external C language interface. As well as the fact that the storage manager allows different arguments of a predicate to share a common index dimension in a novel manner, it indexes rules and facts in the same manner. PerKMan handles compound terms efficiently and its data structures adapt their shape to large dynamic volumes of clauses, no matter what the distribution. The storage manager achieves fast clause retrieval and reasonable use of disk space.     

Metallurgical failure analysis of cold cracking in a structural steel weldment: Revisiting a classic failure mechanism

Cold cracking of structural steel weldments is a well-characterized, well-documented, and well-understood failure mechanism. Extensive effort has been put forth to recognize the welding and materials selection parameters that are conducive to cold cracking; however, these engineering efforts have not fully eliminated the occurrence of such failures. This article describes cold cracking failure specifically related to the construction industry. This particular failure was successfully identified prior to final erection of the structural member, and the weld was successfully reworked. These actions potentially prevented a serious catastrophic event that could have occurred have occurred either later in the construction process or possibly during the use of the building. Individual welding parameters, such as electrode/wire selection, joint design, and pre/postheating, played a role in the failure, and a number of human factors relating to the actual fabrication practices also contributed to the failure process.     

大型钢制焊接双层低温储罐设计建造

介绍了大型钢制焊接双层低温储罐的结构形式、选材、建造、检验及保冷要求 ,结合所设计的低温液氨储罐 ,对设计建造这类储罐必须考虑的一些问题作了分析     

Ti基MnO_x型DSA析氧电极材料的性能

本文报导了新型 Ti/SnO_2+MnO_x+RuO_2/MnO_x(DSA)电极材料的各种性能,其中包括电极的导电性、表面粗糙度、电化学活性表面积、析氧阳极特性等,并用 X 射线衍射法进行了物相分析、用 SEM观察了表面形貌。确认该电极性能良好,加之成本较低,可作为酸性介质中的析氧电极材料。     

Baseline assessment of metals and hydrocarbons in the sediments of Lake Mulwala, Australia

An assessment of hydrocarbon and metal/metalloids (arsenic, cadmium, copper, lead, mercury, selenium, zinc) contamination in sediments from Lake Mulwala, Australia, was undertaken. The objectives of the study were: (i) to determine the extent of contamination in the lake sediments, compared to Australian and international sediment quality guidelines, and (ii) to attempt to identify the contaminant sources to the lake. With the exception of a few samples containing elevated levels of arsenic and/or mercury, the levels of all contaminants in the sediment samples taken from the lake were below the ‘lower trigger’ of the Australian Sediment Quality Guidelines that would warrant further investigation. High molecular weight hydrocarbons (up to 700 mg kg⁻¹) were found in most sediment samples. Non‐metric statistical analysis indicated that the contaminant distribution was different in different parts of the lake, with the lowest concentrations generally found at the influent to the lake. No definitive source(s) of contamination could be identified for either metalloids or hydrocarbons.