直流法测量钯氢化物电极电阻时的阻值偏移

讨论了直流法在线测量钯氢化物电极电阻时的电化学效应，计算了电解液的共导、测量电流与电解电流引起的浓差电池效应以及电极作为集流体引起的电阻贡献。结果表明：当电极具有高的长度与半径比值、粗糙的表面、高的溶液电导以及大的电解电流时容易引起显著的附加电阻。     

稀土改善09CuPTiRE耐候钢耐蚀性的作用机理

应用扫描电镜(SEM)、离子探针(IMA)、X射线光电子能谱(XPS)和交流阻抗法研究含不同稀土耐候钢稀土提高耐大气腐蚀作用机理。结果表明,合适的稀土含量可显著提高钢的耐腐蚀性,稀土能促进Si、Cu和P在内锈层中以Si~(4+)、Cu~+和P~(5+)形态富集,并观察到锈层中的稀土。钢中加入稀土形成了致密连续厚而粘附性好的含硅铜稀土的复合铁锈层,从而提高了抗大气腐蚀性能。     

The Effect of Structural Defects on the Thermal Conductivity of ZnS, ZnSe, and CdTe Polycrystals

ZnS, ZnSe, and CdTe polycrystals are experimentally investigated. Mechanisms are treated which restrict the thermal conductivity in samples prepared by recrystallization pressing and by deposition from the vapor phase and subjected to additional strain. Anomalies are observed on the temperature dependences of the thermal resistance of investigated samples, which are due to the special features of their phonon spectra and to the variation of the contribution made by longitudinal and transverse phonon branches to the heat transfer in the Debye temperature region and higher.     

Fracture Resistance of Ceramics upon Edge Chipping

Modern methods of determining fracture resistance are analyzed. The necessity of developing a crucially new method based on edge chipping of a brittle material is shown. The results of experimental studies are presented. The applicability of the method to the comparative fracture resistance evaluation of ceramics is substantiated.     

Nonlinear electrical transport in K-TCNQ at low temperatures

A remarkable nonlinearity has been observed for electric transport in K-TCNQ (potassium tetracyanoquinodimethane) quasi-one-dimensional conductor. The negative differential resistance region appears afterV _m (turn over voltage), beyond which voltage goes down with increase of current. A possible mechanism is discussed in terms of dynamics of charged solitons and domain walls in one-dimensional molecular stacks of these types of crystals.     

TiAl基合金表面改性对高温抗氧化性的影响

研究了渗碳处理ＴｉＡｌ基合金试样的高温氧化行为，发现渗碳处理可以在ＴｉＡｌ基合金试样表层形成致密的多层结构的渗碳层，并发生表层Ａｌ、Ｔｉ重新分配。致密的渗碳层具有良好的高温抗氧化性和高温热稳定性，同时，Ｔｉ、Ａｌ重新分配形成的富Ａｌ最外层也能进一步提高合金的抗氧化性。     

弹性杆与水下壳体接触冲击的冲击力计算研究

对弹性杆与水下壳体接触冲击问题进行了研究，用有限元法模拟壳体，边界无法模拟无限域流体，通过温面上的耦合条件进行联立求解，文中给出了典型算例，并进行了有关讨论。     

离子注入对Cr12MoV钢表面组织结构和力学性能的影响

研究了Ｃｒ１２ＭｏＶ钢离子注入层的显微组织特征及其对表面性能的影响。结果表明，离子注入使Ｃｒ１２ＭｏＶ钢的表面硬度和耐磨性能得到显著改善，且存在着一个最佳的注入剂量，约为３×１０＾１＾７Ｎ＾＋／ｃｍ＾２左右。离了注入在Ｃｒ１２ＭｏＶ钢表面层中形成了大量细小弥散的第二相粒子，并使α－Ｆｅ晶格发生严重畸变，从而引起材料表面强化。     

Strength of Metals at High Strain Rates

Results of metal testing in impact tension–compression and indentation are analyzed. As the analysis of these data demonstrates, the strength of metals increases greatly with strain rates and at moderate indentation rates. At high indentation rates, a decrease in the specific energy (per unit volume of a displaced material) necessary for the formation of a conical cavity was observed. The account of the effects of viscosity, temperature increase upon plastic deformation and its localization can be used to explain the above phenomena.