Role of temperature gradient in liquid／solid phase solution-diffusion bonding

The liquid-film solution-diffusion bonding of ZCuBe2. 5 alloys was conducted using Cu-based alloy powders. The tensile strength of the joint is up to 318 MPa. With the increase of temperature gradient, the bonding time decreases and the interlace migration velocity increases remarkably. The appropriate temperature gradient is 5 -40 K/cm. Under fixed bonding time, the thickness of diffusion layer increases with the increase of temperature gradient, and this tendency becomes more remarkable with the prolonging of bonding time.     

太阳能电池自动封装系统的研究

为了保证太阳能电池在恶劣的太空环境下能可靠运行，在太阳能电池布贴前，必须进行抗辐照玻璃盖片的封装操作，以达到保护太阳能电池的目的。抗辐照特性是空间太阳能电池区别于地面应用的太阳能电池的重要特征之一。抗辐照玻璃盖片的封装操作是空间太阳能电池方阵制造过程的重要环节。本文通过机器人技术与滴胶技术的结合，设计出一套太阳能电池自动封装系统，实现太阳能电池片的高精度定量喷涂和抗辐照玻璃盖片的非真空环境下的精确封装。文章详细介绍了设计要求、设计思想、系统组成、工作原理和实现过程，并分析了系统的技术特点。     

Fe3Al合金与Q235钢扩散焊界面的析出相

采用扫描电镜(SEM)、能谱分析(EDS)、X射线衍射(XRD)和电子探针(EPMA)对Fe3Al/Q235扩散焊界面的析出相形貌进行观察和成分测定,研究微观析出相的形成以及工艺参数(T,t,p)的影响.结果表明,Fe3Al/Q235扩散焊界面靠近Fe3Al一侧形成FeAl(Cr)析出相,是引起扩散焊接头脆性断裂的关键.扩散焊温度T、保温时间t与析出相区宽度y符合抛物线规律y2=3.5(t-t0)exp[-5.6×104/(RT)].在降低加热温度和保温时间的条件下,增加焊接压力可促进Fe3Al/Q235界面原子的扩散,避免脆性析出相的形成,保证Fe3Al/Q235扩散焊接头的性能.     

加工TiNi形状记忆丝的新工艺

采用模拟试样研究了Ti/TiAl、Nb/TiAl和NbTi/TiAl 3种复合材料的界面特性。结果表明,爆炸试样的界面反应层厚度远小于热等静压试样的界面反应层厚度。在同一条件下热等静压成型的这3种复合材料,其界面差异明显:Ti/TiAl和NbTi/TiAl试样的界面反应层较厚,界面结合强度较高;Nb/TiAl试样的界面反应层较薄,界面结合强度较低。     

HA—微孔钛基涂层种植体的复合强度

研究了羟基磷灰石(HA)和中性玻璃(G)的混合涂料在TC4多孔钛基体上的界面复合强度。探讨了中性玻璃含量、基体表面状态以及烧结工艺对这种涂层复合种植体的复合强度的影响。指出:复合的实质是中性玻璃与基体的润湿结合,最合适的玻璃含量为50 wt%,提高复合强度的关键,在于基体表面的TiN蒸镀处理,当TiN厚度为2～3 μm时,复合强度可达7.2 MPa。最佳烧结工艺为:900～950℃/30 min。     

不同pH值和F-浓度人工唾液对钛/瓷结合的影响

研究了不同pH值和F-浓度人工唾液对钛/瓷结合性能的影响.将实验室制备的钛瓷粉分层烧结于钛片上,浸泡于37℃,pH2.7、pH7.0/F-100 μg·mL-1与pH2.7/F-100 μg·mL-1的人工唾液中,测量了浸泡7d和30d试件的三点弯曲结合强度,应用扫描电镜观察了瓷剥脱后钛表面的形貌,并进行了EDX分析.结果显示:pH2.7/F-100 μg·mL-1组试件的钛/瓷结合强度明显低于未浸泡组,其余各组与未浸泡组相比无显著差异.研究结果提示:酸性环境中,F-的存在可使钛/瓷结合强度降低,而酸性环境和低浓度的F-环境对钛/瓷结合强度则没有明显影响,口腔内有钛瓷修复体的患者应慎用含氟口腔产品.     

Effect of solid fraction on steel-mushy Cu-graphite pressing bonding

The pressing bonding of steel plate to QTi3.5-3.5graphite slurry was studied. The bonding conditions were 620℃ for preheating temperature of steel plate, 530℃ for preheating temperature of dies, 50 MPa for pressure and 2 min for pressing time. The relationship between the solid fraction of QTi3.5-3.5graphite slurry and the interracial mechanical property of bonding plate was obtained. The results show that when the solid fraction of QTi3.5-3.5graphite slurry is smaller than 45.8%, the interracial shear strength of bonding plate increases with the increasing of solid fraction. When the solid fraction is larger than 45.8%, the interracial shear strength decreases with the increasing of solid fraction. When the solid fraction is 45.8%, the largest interracial shear strength of bonding plate 127 MPa can be got, and the interface is made up of Fe-Cu solid solution.     

TiAl/Ti/V/Cu/40Cr钢扩散连接界面组织结构对接头强度的影响

研究了TiAl/Ti/V/Cu/40Cr钢的扩散连接，结果显示：在TiAl/Ti界面处形成了对接头强度有利的Ti3Al TiAl双相层及Ti固溶体层，而Ti/V/Cu/40Cr界面处未出现金属间化合物及其它脆性相，接头最高拉伸强度可达420MPa，接近TiAl母材。     

聚氧化乙烯改性水玻璃粘结剂的研究

确定了聚氧化乙烯改性水玻璃粘结剂的基本组分,测试了有机酯自硬和CO2气硬型砂的常温粘结强度和高温残留强度。研究发现,在水玻璃中加入聚氧化乙烯树脂能改善水玻璃的老化现象,充分发挥其粘结效率;粘结剂加入量相同时,型砂强度是普通水玻璃砂的1.5倍,800～1000℃时,型砂残留强度≤0.5MPa。结果表明,聚氧化乙烯改性水玻璃粘结剂加入量低,型砂工艺性能良好,浇注后出砂容易,有利于旧砂进一步干法回用。     

汽车拼板的激光焊接的研究

采用2kWNd：YAG激光器对不同厚度车身用板进行了搭接和对接两种接头形式的激光焊接研究。并对焊接接头进行了拉伸试验分析，确定了合适的焊接参数。