Microstructure and Mechanical Properties of Heat-treated GeSb_2Te_4 Thin Films

The effect of annealing on microstructure,adhesive and frictional properties of GeSb 2 Te 4 films were experimentally studied.The GeSb 2 Te 4 films were prepared by radio frequency(RF)magnetron sputtering,and annealed at 200℃and 340℃under vacuum circumstance,respectively.The adhesion and friction experiments were mainly conducted with a lateral force microscope(LFM)for the GeSb 2 Te 4 thin films before and after annealing.Their morphology and phase structure were analyzed by using atomic force microscopy(AFM)and X-ray Diffraction(XRD)techniques,and the nanoindention was employed to evaluate their hardness values.Moreover,an electric force microscope(EFM)was used to measure the surface potential. It is found that the deposited GeSb 2 Te 4 thin film undergoes an amorphous-to-fcc and fcc-to-hex structure transition;the adhesion has a weaker dependence on the surface roughness,but a certain correlation with the surface potential of GeSb 2 Te 4 thin films.And the friction behavior of GeSb 2 Te 4 thin films follows their adhesion behavior under a lower applied load.However,such a relation is replaced by the mechanical behavior when the load is relatively higher.Moreover,the GeSb 2 Te 4 thin film annealed at 340℃presents a lubricative property.     

热轧高强钢平整机辊径参数设计技术研究

基于高强钢平整机的生产工艺特点,结合板形与辊耗问题,将带材的出口前张力与辊间压力横向分布都均匀作为目标函数,把保证所有被平整高强钢产品的机械性能满足产品大纲要求作为约束条件,提出了一套针对热轧高强钢平整机的工作辊与支承辊辊径参数设计模型.其研究结果对指导宝钢分公司1880 mm热轧平整机的工艺参数的确定与技术谈判发挥了重要作用,并具有进一步的推广价值.     

孤后八气田机械堵水技术与应用

在多层合试合采工艺实施过程中，经常会遇到地层水的问题，通常采用的挤水泥或化学堵剂的办法不仅成本高且工艺复杂，而使用常规封隔器又达不到封堵效果。Y445(3)型封隔器 Y341(Ⅱ)型封隔器的悬挂式封隔组合管柱堵水工艺，满足了封堵水层、采气的要求。     

Linear Algebra Considerations for the Multi-Threaded Simulation of Mechanical Systems

A solution method suitable for the multi-threaded simulation ofmechanical systems represented in Cartesian coordinates isproposed and analyzed. In a state-space framework for thesolution of the Differential Algebraic Equations (DAE) ofMultibody Dynamics, the position/velocity stabilization and theacceleration computation are based on iterative solvers applied toequivalent reduced problems. The most in-depth computationalaspect analyzed is the preconditioning, i.e., the direct solutionof the reduced systems. Provided a topology index reduction is first applied to the model, the effort for the direct solution of the reduced systems is shown to be of order O(N _J ), where N _J is the number of joints in the model. The recurring theme of thepaper is the central role that the topology of the mechanicalsystem plays in the overall performance of the numericalsimulation. Based on the topology of the model, parallelcomputational threads can be established to start in the equationformulation and continue through the iterative numericalalgorithms employed for the numerical solution. Task schedulingthese parallel threads is expected to redeem real-time performancefor certain classes of complex applications.     

化学成分和固溶温度对1Cr17Mn9Ni4N不锈钢组织和性能的影响

为提高1Crl7Mn9Ni4N钢固溶处理后的力学性能(特别是钢的强度)，研究了化学成分及固溶处理温度对其组织和性能的影响。结果表明，1000—1125℃固溶处理后，该钢的组织为单相奥氏体。在标准成分范围内，随着镍、锰含量的增加，该钢的强度降低，塑性有所改善。氮明显提高该钢的强度。根据试验结果，每增加0．01％的氮钢的室温强度可提高大约5MPa，且塑性基本上不受影响。当合金成分(质量分数，％)控制在C0．08—0．12、Crl6．5—17．5、Ni3．5—4．2、Mn8．0—9．0、N0．22—0．28时，1Crl7Mn9Ni4N钢经1050—1100℃固溶处理后强度较高、塑性好，室温强度σ0．2和σb可分别达到400MPa和800MPa。     

VN合金在大规格角钢生产中的应用研究

大规格角钢主要用于铁塔制造和建筑结构中。唐钢过去用16Mn钢生产Q345级别角钢，因供轧化学成分范围较窄，供轧率偏低。通过加入V-Fe合金及VN合金进行微合金化，设计了16Mnv(N)钢种生产角钢，使角钢综合性能有显著提高。分析比较了16Mn、16MnV及16MnV(N)角钢的性能，认为在大规格高强度角钢生产中，用VN合金进行微合金化，其效果是最佳的。     

Hydriding and Dehydriding Characteristics of Mechanically Alloyed LaMg_(17) Ni Composite Material

Magnesiumandmagnesiumalloyshavebeenin vestigatedashydrogenstoragematerialsforseveralde cadesbecausefarmorehydrogenbyweightcanbestoredinthemthaninmostoftheothercurrentlyknownhydrogenstoragealloys .Moreover ,thehighnaturalabundanceofMg ,itslightmassandenviron mentalcompatibilitypotentiallymakemagnesiumoneofthemostprospectivecandidatesforfuturehydrogenstoragematerials .Unfortunately ,thepracticalappli cationofMganditsalloyshasbeenlimitedonlytocertainstoragedevicebecauseoftheirpoorhydriding dehydr…     

纤维体积分数对K3D/MCPA复合材料力学性能的影响

本文研究了纤维体积分数对三维编织芳纶纤维增强铸性尼龙(简称K3D／MCPA)复合材料力学性能的影响。研究表明，K3D／MCPA复合材料有优异的抗冲击性能，冲击强度比三维编织芳纶纤维增强铸性尼龙(简称C3D／MCPA)和纯基体均有大幅度的提高，且随着纤维体积的提高而升高。K3D／MCPA复合材料剪切强度随纤维体积比的增大而增大，其纵向剪切强度低于纯基体和C3D／MCPA复合材料，但其横向剪切强度高于它们。K3D／MCPA复合材料弯曲强度与弯曲模量随纤维体积比的提高而提高，但与相同体积比的C3D／MCPA相比，K3D／MCPA的弯曲强度与弯曲模量均较低。     

可焊性高强度钢筋的开发与生产

为进一步开发国际钢材市场，研制开发了符合加拿大可焊性高强度钢筋标准要求的高强度钢筋．制定了化学成分及力学性能内控标准，分析了生产工艺各环节对成分和性能的影响，依据试验结果，在全面统计分析的基础上，调整了冶炼成分，生产的531批钢筋全部合格．通过直方图及回归分析，说明了制定的产品生产工艺可行，也为今后的生产提供了理论依据。