Sintering of the Mechanochemically Activated Powders of Hexagonal Boron Nitride

Pressureless sintering of hexagonal boron nitride (BN) was performed using a powder activated by mechano-chemical treatments. Physical properties of the sintered BN bodies depend on the type of starting powder and the conditions of the treatments. The BN body, which was obtained at 2000°C using an appropriate activated powder, was 99 wt% pure and was excellent in mechanical and physical properties, in spite of its low density (1.64 g/cm³).     

Exothermic effect in the process of electron‐beam curing of epoxy resins

Temperature measurements have been performed in the process of electron‐beam curing of EB‐I and EB‐II epoxy resin systems. The influence of initiator content, resin type, and dose rate on the temperature of the systems was studied. Transverse and longitudinal temperatures of samples in the glass vessel were also analyzed. The nature of temperature curves varied with the different epoxy resin systems in the steel mold, but did not change with different contents of the initiator. At the same time, the heat had no effect on the gel fraction of epoxy resin systems. The temperature curve was greatly affected by the dose rate, and its peak value, peak width, and plateau value also increased with it. The transverse temperature of EB‐II glass vessel samples increased as the radiation dose increased and, in the same sample, the temperature reduced as the distance between the radiation center and the test point increased. The longitudinal temperature of EB‐I and EB‐II resin systems in a glass vessel decreased as the radiation depth increased. As the radiation dose increased, the temperature of the EB‐I resin system increased simultaneously, while that of the EB‐II resin system initially increased and then kept constant when the dose reached a certain value. The temperatures of these two resin systems decreased rapidly when the radiation process stopped. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 2217–2222, 2004     

电子陶瓷和器件的低温共烧技术

较系统地介绍了电子器件用低温共烧陶瓷(low temperature cofired ceramics,LTCCs)材料,探讨了其工艺中的若干问题。电子器件用低温共烧陶瓷材料包括:玻璃/陶瓷复合材料、结晶化玻璃、晶化玻璃/陶瓷复合材料以及液相烧结陶瓷,其中典型的和最为常用的LTCCs为玻璃/陶瓷(特别是氧化铝)复合材料。正在研究的一些陶瓷介质材料中,Bi基介质材料引起了人们的关注。玻璃/陶瓷复合材料的制备工艺中,应当着重关注和加深了解玻璃的流动性和结晶性、玻璃的起泡、玻璃和陶瓷颗粒间的反应、共烧材料的匹配等问题,从优选材料配方和优化工艺着手,从而获得优质可靠的材质和器件。     

Lifetime assessment of epoxies by the kinetics of thermal degradation

The kinetics of thermal degradation of 4,4′‐diaminodiphenylsulfone (DDS)‐cured glycidylethers (DGBA) and glycidylamines (TGDDM) have been studied by isothermal annealing. Thermal degradation proceeds via first‐order kinetics with activation energies of 138 (DGBA/DDS) and 95 kJ/mol (TGDDM/DDS). From these data the temperature‐dependent lifetime can be calculated. Based on the heat distortion temperature and 20 years' service as criteria, the upper service temperature is found to be around 115–120°C. In spite of the different activation energies and bond stabilities, only marginal differences in the upper allowed service temperatures between these resins were found. Only slight improvements can be expected by optimizing the cure conditions. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 1881–1886, 2004     

安钢二炼焦加热集散控制系统

安钢二炼焦焦炉加热控制系统根据蓄热室温度，建立了可靠的数学模型，通过控制加热煤气的压力和烟道废气吸力实现加热的自动控制，并实现参数无纸记录，日报表的自动生成，设备巡检的记录等功能。     

不同玻璃料对PTC陶瓷性能的影响

研究了AST和ASL两种玻璃料对PTC陶瓷性能的影响,发现在1280℃～1340℃的烧成范围内,添加ASL的样品其室温电阻要比添加AST的样品大,而其电阻—温度特性要比添加AST的样品好,且两种样品的晶粒尺寸及晶粒均匀度有明显差别.研究结果表明,两种样品性能上的差异与它们显微结构上的差异有着密切关系.     

转炉用快速烧结镁r质投补料

根据转炉大面耐火材料的使用条件 ,研究了影响沥青结合及树脂结合镁质投补料使用性能的主要因素。结果表明 ,控制配入合适溶剂的沥青或树脂的加入量 ,掺加少量外加剂 ,可获得性能良好的修补料。二者相比 ,沥青结合镁质投补料的烧结时间较长 ,容易出现凹坑 ;树脂结合投补料与砖体间的粘结性比沥青的稍差 ,容易出现翘曲。     

Characterization and Sintering Behavior of Alkoxide-Derived Aluminosilicate Powders

Submicrometer SiO₂-Al₂O₃ powders with compositions of 46.5 to 76.6 wt% Al₂O₃ were prepared by hydrolysis of mixed alkoxides. Phase change, mullite composition, and particle size of powders with heating were analyzed by DTA, XRD, IR, BET, and TEM. As-produced amorphous powders partially transformed to mullite and Al-Si spinel at around 980°C. The compositions of mullite produced at 1400° and 1550°C were richer in Al₂O₃ than the compositions of stable mullite solid solutions predicted from the phase diagram of the SiO₂-Al₂O₃ system. Particle size decreased with increasing Al₂O₃ content. The sintered densities depended upon the amount of SiO₂-rich glassy phase formed during sintering and the green density expressed as a function of particle size.     

料温对RIM交联型聚氨酯脲结构与性能的影响

采用便携式微型反应注射成型机制备了一组料温分别为３０，４０，５０，６０℃的交联型聚氨酯脲。用ＤＳＣ和力学性能对试样进行表征的结果表明：料温提高有利于软、硬微相的混合，而硬链段微区的有序性变差。反映在宏观力学性能上则表现为：试样的拉伸强度提高，伸长率在５０℃料温时出现极大值，弯曲强度和弯曲模量则出现最小值。料温为３０℃时，物料混合不充分，随着料温升高，混合逐渐均匀，试样透明度提高。     

公共制造云服务平台架构及其支撑技术研究

为了能使量大面广的中小企业充分享受云制造的益处, 分析了公共制造云的运行原理, 搭建了一个面向中小企业的公共制造云服务平台架构, 并给出了其形式化描述。对平台所涉及的关键支撑技术如云制造资源管理、协同设计及QoS管理进行分析, 提出了基于多级递阶控制结构的云制造资源管理与监控模型, 以及在云制造基础设施之上构建了支持复杂产品设计、面向服务的虚拟协同设计环境。最后通过公共制造云服务平台运作模型说明了平台的应用性和示范性。