碳纳米管及稀土元素钇(Y)对高Ni含量Ti(C,N)基金属陶瓷组织与性能的影响

研究了不同含量的碳纳米管及0.8%稀土Y对高Ni含量Ti(C,N)基金属陶瓷组织性能的影响.将不同成分的试样分别于1400℃、1410 ℃、1420℃真空烧结,测试抗弯强度、洛氏硬度,观察背散射电子形貌、断口形貌并做能谱分析.结果表明,加入质量分数(下同)为0.8%Y及0.3%～1.0%的碳纳米管时,碳纳米管含量为0.5%的组织较均匀,芯壳结构明显,抗弯强度及硬度均较高.     

Strengthening technology and mechanism for semi-solid die casting of aluminum alloy

Combined with theoretical evaluation,an optimized strengthening process for the semi-solid die castings of A356 aluminum alloy was obtained by studying the mechanical properties of castings solution treated and aged under different conditions in detail,then,the semi-solid die castings and liquid die castings were heat treated with the optimized process.The results show that the mechanical properties of semi-solid die castings of aluminum alloy are superior to those of the liquid die castings,especially the strengthening degree of heat treated semi-solid die castingsis much greater than that of liquid die castings with the tensile strength more than 330 MPa and the elongation more than 10％,and this is mainly contributed to the non-dendritic and more compact microstructure of semi-solid die castings.The strengthening mechanism of heat treatment for the semi-solid die castings of A356 aluminum alloy is due to the dispersive precipitation of the second phase(Mg2 Si) and formation of GP Zone.     

Assessing the predictive capability of two‐phase models for the mechanical behavior of alumina/epoxy nanocomposites

A review of analytical modeling of particulate reinforcement is made as a prelude to the problem of microstructural inhomogeneity in nanocomposite materials. Noting the inevitability of dispersion nonuniformity, and variations in agglomerate morphology and filler‐matrix interaction, the need to question the application of such models to novel materials arises. Employing the mechanical properties of alumina/epoxy nanocomposites, with known dispersion characteristics, an evaluation of the predictive capability of various models for Young's modulus, strength, and failure strain is made. Comparison between models is accompanied by a discussion of the parameters used in the fitting of macroscopic behavior to microstructural features. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 869–879, 2005     

锆莫来石材料的反应烧结机制和显微结构特征

研究了用锆英石和工业氧化铝合成锆莫来石材料的反应烧结过程和显微结构。结果表明，添加适量ＭｇＣｌ２·６Ｈ２Ｏ可以促进反应烧结进程。锆英石大颗粒完全分解以后形成ＺｒＯ２聚集体，结构中出现封闭气孔可能与ＺｒＯ２聚集体有密切关系。加入ＭｇＣｌ２·６Ｈ２Ｏ后锆莫来石材料显微结构的主要特征：ＺｒＯ２有聚集体和均匀分布两种赋存形式；封闭气孔一般与ＺｒＯ２聚集体相邻。     

Solid state interfacial reactions in electrodeposited Ni/Sn couples

Ni/Sn couples,prepared by sequentially electroplating Ni layers and Sn layers on metallized Si wafers,were employed to study the mierostructures and growth kinetics of Ni-Sn intermediate phases,when the Ni/Sn couples were aged at room temperature or annealed at temperatures from 150 to 225℃for various times.The results show that the NiSn phase and Ni_3Sn_4 phase are formed,respectively,in the aged couples and annealed couples.The Ni_3Sn_4 layer is continuously distributed between the Ni and Sn sides in t...     

Research on the friction and wear mechanism of Poly(vinyl alcohol)/hydroxylapatite composite hydrogel

Poly(vinyl alcohol)/Hydroxylapatite (PVA/HA) composite hydrogel was prepared with poly(vinyl alcohol) and hydroxylapatite as raw materials, using the method of repeated freezing and thawing. The morphologies of PVA/HA composite hydrogel were observed by means of high-accuracy 3D profiler and scanning electron microscope (SEM). The compressive elastic modulus and the stress relaxation characteristics of PVA/HA composite hydrogel were measured using the flat-head cylinder indenter. The friction and wear tests between PVA/HA composite hydrogel and bovine knee articular cartilage were performed on the micro-tribometer. The worn morphologies of PVA/HA composite hydrogel were observed with environmental scanning electron microscope (ESEM). The results showed that PVA/HA composite hydrogel has the cross-link network microstructure which is similar to that of the natural bovine knee articular cartilages. With the increase of freezing-thawing cycles and the HA content, the degree of cross-link and the crystallization of PVA/HA composite hydrogel both increase, the elastic modulus increases evidently, the rate of stress relaxation is improved and the value of balance stress decreases. The friction coefficient decreases with the increase of the freezing-thawing cycles and the HA content. The more the freezing-thawing cycles are, the earlier the friction coefficient reaches the stable balance value. The friction deformation depth between PVA/HA composite hydrogel and bovine knee articular cartilage is inversely proportional to freezing-thawing cycles and the HA content. The main wear mechanisms of PVA/HA composite hydrogel are plastic flowing and adhesive flaking. The wear severity degree decreases with the increase of freezing-thawing cycles and the HA content. Supported by Key Program of the National Natural Science Foundation of China (Grant No. 50535050), Program for New Century Excellent Talents in University (Grant No. NCET-06-0479) and Natural Science Foundation of Jiangsu Province (Grant No. BK2005403)     

Interfacial Microstructure and Mechanical Properties of Al/Mg Butt Joints Made by MIG Welding Process with Zn-Cd Alloy as Interlayer

Butt joints between Mg alloy AZ31 B and pure Al 1 060 sheets were produced via metal inert gas welding process with Zn-Cd alloy foil. Crack-free Al/Mg butt joints between AZ31 B Mg alloy and pure Al 1060 sheets were obtained. Intermetallic compound layer 1 and layer 2 had formed in fusion zone/Mg alloy and the average thickness of the layer 1 was about 50 μm. The intermetallic compound layer 1 consisted of Al12Mg17 and Mg2Si phases while layer 2 consisted of Al12Mg17, Mg2Si and Mg Zn2 phases. The crack started from the IMC layer at the bottom of the joint and propagated along the brittle IMC layer, then expanded into weld metal during the SEM in situ tensile test. The highest tensile strength of the dissimilar metal butt joints could reach 46.8 MPa and the effect ofinterfacial IMC layer on mechanical property of the joint was discussed in detail in the present study.