碳含量对易切削非调质塑模钢组织及性能的影响

研究了碳含量与易切削非调质塑料模具钢性能间的关系。结果表明，随着碳含量的上升，钢的硬度随之而升高，韧性则先升后降，钢的切削性能渐趋恶化。     

Microstructures and mechanical properties of welded Fe-12Cr-20Mn austenitic stainless steel

The effects of welding on the tensile and fatigue properties of fully annealed and cold-worked Fe-12Cr-20Mn austenitic stainless steel were evaluated. Room temperature and 500 °C tensile tests and room temperature cantilever beam fatigue tests were accomplished on specimens that contained autogenous bead-on-plate welds. The tensile and fatigue properties of the fully annealed material were not significantly influenced by welding. The tensile properties of the welded cold-worked material were also not significantly affected by the presence of a weldment. However, welding caused a large reduction of the fatigue life of the cold-worked material. Fatigue cracks preferentially initiated at large Mn-Si inclusions that formed in the fusion zones of the weldments.     

Characterization of angular dependence of macroscopic magnetic properties in ASTM 36 steel using magnetic Barkhausen noise

Angular-dependent magnetic Barkhausen noise measurements were performed on ASTM 36 steel samples for various values of applied uniaxial stress. The maximum differential permeability and the coercive field are obtained from this Barkhausen signals. The angular dependence of these macroscopic magnetic properties is studied. The tension for which the magneto-elastic energy balances the anisotropic energy is estimated. The results are discussed based on the domain wall theory.     

Modelling of plastic flow, heat transfer and microstructural evolution during rolling of eutectoid steel rods

A study was undertaken in an attempt to quantitatively describe the rolling process of eutectoid steel rods. Finite element method was employed to model plastic flow and heat transfer in the deformed material, and heat transfer during cooling to ambient temperature. The numerical calculation gave an assessment of the strain, strain rate and temperature distributions in the work piece. This allowed the prediction of the austenite microstructure evolution during the process. Finally, the relationships describing the microstructure-mechanical properties were used to quantitatively characterize the influence of processing parameters on strength of rods after rolling.     

Environmental effects on the stress corrosion cracking susceptibility of 3.5NiCrMoV steels in high temperature water

Constant elongation rate tests (CERTs) were carried out to investigate the effects of environmental factors of dissolved oxygen and temperature on the stress corrosion cracking (SCC) susceptibility of 3.5NiCrMoV turbine steels. Tests were conducted in pure water of various dissolved oxygen concentrations at temperatures of 50 °C-200 °C in the range of strain rates from 5 × 10⁻⁸/s to 1 ×  10⁻⁶/s. Dissolved oxygen significantly affected the SCC susceptibility of turbine steels in water. The SCC susceptibility of the turbine steels increases as the dissolved oxygen concentration in water increases. The elongation of the turbine steels tested in aerated water at 150 °C at a strain rate of 1 × 10⁻⁷/s decreased to half of that of the steels tested in deaerated water in the same test condition. And the SCC susceptibility of the steels increased with decreasing strain rate, and with increasing temperature. The increase of the SCC susceptibility of the turbine steels in the higher dissolved oxygen environment is considered to be due to the higher content of dissolved oxygen enhancing the reduction reactions of oxygen on the metal surfaces (cathode) and accelerating the dissolution rate at the crack tips (anode) by galvanic attack of an aeration cell.     

Spheroidization of medium-carbon steels

Spheroidization experiments were made on a medium- carbon AISI 4037 steel, using both intercritical and subcritical annealing cycles. The results indicate that in the subcritical cycle the spheroidization occurred much more quickly than expected, so that shorter times were sufficient to achieve high formability. On the other hand, the hardness dropped faster in the intercritical cycle. Although more work needs to be done, these results suggest that using a subcritical spheroidization process instead of an intercritical process could achieve considerable savings in time, energy, and cost.     

High-temperature oxidation of aluminum electroplated Fe-Mn alloys

Austenitic Mn-Al alloys (20–32 W/O Mn, 7–10 Al, 2–3 Si, 1C) were found to have satisfactory oxidation resistance up to 950°C under isothermal conditions in air. Surface enrichment of aluminum is a necessary condition for obtaining an almost pure alumina scale for uses at higher temperatures. Four different Mn-steels were Al-coated by the Capuano electroplating process. In all the steels there was an increase in the hot-oxidation resistance. The best results were obtained with steels containing both Al and Si, and this for temperatures up to 1100°C. No spalling was noticed during rapid cooling of the test pieces. Silicon was found to act as a diffusion barrier to outward iron diffusion. It appears that there is formation of a pure, thin film of alumina from the matrix which interacts with the aluminum diffusing from the superimposed, coating for the formation of good bonds.     

开放水热法制备莫来石复相纳米晶体的影响因素

以天然高岭土为原料,经精细化处理煅烧制备莫来石.用常压、开放水热技术制备出莫来石复相纳米晶体材料.实验表明:常压、开放水热条件下制备莫来石复相纳米晶粉体的水热反应中,采用质量比为m(Na2O)/m(SiO2)=2.8,m(H2O)/m(Na2O)=35～30,0～80℃控温升温1 h,在80℃保温2 h,可制备出尺寸为80～100 nm莫来石复相纳米晶体.所制备的莫来石纳米晶体的水热溶液相变驱动力△μ为(3.609～4.672)×10-20 J/mol;水热体系溶解度控制在3.891×10-6 mol/L;熔解热△E为18.846 kJ/mol;晶体生长速率常数选择0.85～0.92,有利于快速成核和晶体生长,并且可以很好地控制晶体尺寸和分散度.