Finite elements in the analysis of pressure vessels and piping-a bibliography (1976–1996)

The paper gives a bibliographical review of the finite element methods (FEMs) applied for the analysis of pressure vessel structures/components and piping from the theoretical as well as practical points of view. The range of applications of FEMs in this area is wide and cannot be presented in a single paper; therefore the aim of this review is to give the reader an encyclopaedic view of the differnt possibilities that exist today for the finite element analysis in the fields of pressure vessels and piping. The bibliography at the end of the paper contains approximately 1900 references to papers, conference proceedings and theses/dissertations on the subject that were published in 1976–1996. These are classified in the following categories: linear and non-linear, static and dynamic, stress and deflection analysis; stability problems; thermal problems; fracture mechanics problems; contact problems; fluid-structure interaction problems; manufacturing of pipes and tubes; welded pipes and pressure vessel components; development of special finite elements for pressure vessels and pipes; finite element software; and other topics. Also finite element software, general purpose and special purpose codes, used for the analysis of pressure vessels and pipes are briefly discussed and presented.     

An investigation of pore cracking in titanium welds

Two welded Ti-6A1-4V pressure vessels leaked prematurely in service. The leaks were caused by cracks emanating from weld porosity. The cracks originated during fabrication, with subsequent growth in service leading to the formation of the leak paths. Pore cracking is thought to be caused by a mechanism that involves both sustained-load and cyclic contributions, with the former being the more prominent. It is shown that the tendency for cracking is influenced by pore position and that pore size is not a deciding factor in that regard. The factors that govern pore cracking are discussed, and the possible role of interstitial embrittlement is assessed.     

含钇奥氏体基堆焊焊条堆焊层研究

针对高温、磨损、热疲劳工况下服役零件的失效，研制了一种含稀土元素钇的奥氏体基沉淀强化型堆焊焊条，并对堆焊层组织与性能进行了较系统的研究。     

自动化加工过程的在线质量监测及管理平台的研究

以机器人焊接生产线质量的自动监测及管理为对象，探讨了流水线加工过程通用性质量监控平台的构建方法，采用基于网络的车间级前沿机及服务器，分别实现了现场单个质量监控点的微观质量监测及整个流水线的宏观质量管理；最后探讨了数据集市和数据挖掘技术系统在该系统的应用。     

不锈钢绕带容器环板与绕带端头的焊接

本文通过焊接试验对奥氏体不锈钢绕带容器环板与绕带焊接工艺进行了研究分析,并得出了合理的焊接方法和工艺参数。     

自动焊技术在涩宁兰输气管道X70钢试验段上的应用

通过涩宁兰输气管道X70钢试验段的施工,进一步探索和完善自动焊接技术在高强钢管道焊接中的应用。文章介绍了该试验段施工的焊接设备、焊材和焊接工艺,可为同类焊接工程提供借鉴。     

CO2气体保护焊在高炉炉壳焊接中的应用

通过对CO2气体保护焊在高炉炉壳组装与焊接工艺的使用，有效地控制了焊接变形及防止焊缝裂纹，阐明提高焊接质量要从多元角度出发，有机整体地考虑问题，在结论中进一步从成本，焊接质量及培训等方面分析证明推广CO2气体保护焊的必要性。     

Recovery retardation in equal channel angular pressed Al–Zr alloy during friction stir welding

The effect of Zr on reduction of hardness and microstructure in an FS weld of equal channel angular-pressed Al alloy was investigated. Zr addition to Al suppressed dynamic recovery in the thermomechanically affected zone and enabled retention of the high hardness of the ECA-pressed material throughout the weld.     

Metallurgical failure analysis of cold cracking in a structural steel weldment: Revisiting a classic failure mechanism

Cold cracking of structural steel weldments is a well-characterized, well-documented, and well-understood failure mechanism. Extensive effort has been put forth to recognize the welding and materials selection parameters that are conducive to cold cracking; however, these engineering efforts have not fully eliminated the occurrence of such failures. This article describes cold cracking failure specifically related to the construction industry. This particular failure was successfully identified prior to final erection of the structural member, and the weld was successfully reworked. These actions potentially prevented a serious catastrophic event that could have occurred have occurred either later in the construction process or possibly during the use of the building. Individual welding parameters, such as electrode/wire selection, joint design, and pre/postheating, played a role in the failure, and a number of human factors relating to the actual fabrication practices also contributed to the failure process.     

钢骨架塑料(PE)复合管的安装技术

钢骨架塑料复合管既有钢管的耐压又有塑料管的耐腐蚀性，且易于敷设，使用寿命长，本文结合实际施工中的应用。介绍其要点。