NiAl－Fe金属间化合物合金的正电子寿命谱

测量了塑性金属间化合物合金Ｎｉ（５０）Ａｌ（３０）Ｆｅ（２０），Ｎｉ（５０）Ａｌ（２０）Ｆｅ（３０）和Ｎｉ（６０）Ａｌ（２０）Ｆｅ（２０）单晶和多晶的正电子寿命谱．基于正电子寿命谱的特征参数引入了正电子双区域捕获模型，并讨论了这些合金微观结构与力学性能之间的关系．     

Determination of the glass transition temperature of polymer/layered silicate nanocomposites from positron annihilation lifetime measurements

The glass transitions of acrylonitrile-butadiene rubber (NBR)/organoclay nanocomposites with various silicate contents were investigated using positron annihilation lifetime spectroscopy (PALS). The nanocomposites were prepared through melt intercalation of NBR with various concentrations of organoclay (OC30B) modified with the organic modifier, methyl tallow bis(2-hydroxyethyl) quaternary ammonium (MT2EtOH), i.e., Cloisite^® 30B. X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HR-TEM) measurements of the NBR/OC30B nanocomposites showed that the NBR chains were intercalated between the silicate layers, thereby increasing the gallery heights of the organosilicates. The glass transition temperature of NBR was determined using differential scanning calorimetry (DSC). However, it seemed to be very difficult to clearly resolve the very small differences in T_gs caused from various loading of nanosized silicate in NBR/OC30B nanocomposites. Hence, we performed positron annihilation lifetime spectroscopy (PALS) on NBR/OC30B nanocomposites containing various amounts of OC30B (1-10 wt%). Significant changes in the temperature dependencies of free volume parameters (i.e., lifetimes and intensities) were observed at the transition temperature, T_g,PALS, and the T_g,PALS values were found to increase with increasing organoclay content in the samples. These observations are consistent with PALS having a higher sensitivity in the detection of very small changes in free volume properties. The present findings thus highlight the usefulness of PALS for studying phase transition phenomena in polymeric materials with nanoscale structural variations.     

Ex vivo and in vivo Evaluation of [18F]PR04.MZ in Rodents: A Selective Dopamine Transporter Imaging Agent

N‐4‐Fluorobut‐2‐yn‐1‐yl‐2β‐carbomethoxy‐3β‐phenyltropane (PR04.MZ) has been developed as dopamine transporter (DAT) ligand for molecular imaging. It contains a terminally fluorinated, conformationally constrained nitrogen substituent that is well suited for the introduction of fluorine‐18. The present report describes the pharmacological characterisation of [¹⁸F]PR04.MZ. The ligand shows an IC₅₀ value of 2 nM against human DAT, whereas the IC₅₀ value against human serotonin transporter and human noradrenalin transporter are lower (110 nM and 22 nM , respectively). Furthermore, its ex vivo organ distribution, its binding profile in the rat brain and reversibility of binding were examined. A μPET study illuminates a fast kinetic profile and specific binding to rat DAT.     

Interaction of positronium atoms, with paramagnetic molecules, measured by perturbed angular distribution in 3γ annihilation decay

Positronium in the triplet spin state (S = 1) decays by 3γ annihilation having a life time of about 140 ns in vacuum. Positronium annihilation is affected by magnetic fields which mix the M = 0 state of ortho-positronium with the M = 0 state of para-positronium. The mixing fraction depends on the magnetic field intensity and causes quantum beats in the time distribution of γ annihilation decay. This effect was predicted by Barishevsky et al. [V.G. Barishevsky, O.N. Metelitsa, V.V. Tikhomirov, J. Phys. B Atom. Mol. Opt. Phys. 22 (1989) 2835]. The time differential perturbed angular correlation method (TDPAC), combined with long-lived positron life time spectroscopy (PLTS), has been used to observe these quantum beats. It is found that the characteristics of the annihilation time distribution are not influenced by the presence of diamagnetic species such as Ar, N₂ and H₂ but are affected by the presence of the paramagnetic O₂ molecule. Our results are encouraging in developing a new method for investigating magnetic fields on an atomic scale.     

湮没算符k次幂本征态的Wigner函数及其非经典特性

利用Fock态表象下的Wigner函数表达式，重构了湮没算符k次幂本征态的Wigner函数，并依据Wigner函数在相空间的分布规律，讨论了湮没算符k次幂本征态的非经典特性．数值结果表明：湮没算符k次幂本征态的Wigner函数的分布与复参数α的取值有关；湮没算符1次幂的本征态(即相干态)为准经典态(其Wigner函数值总是非负的)，而湮没算符大于或等于2次幂的本征态则都具有明显的非经典特性(它们的Wigner函数均出现了负值).     

Spatially resolved positron annihilation spectroscopy on friction stir weld induced defects

A friction stir welded (FSW) Al alloy sample was investigated by Doppler broadening spectroscopy (DBS) of the positron annihilation line. The spatially resolved defect distribution showed that the material in the joint zone becomes completely annealed during the welding process at the shoulder of the FSW tool, whereas at the tip, annealing is prevailed by the deterioration of the material due to the tool movement. This might be responsible for the increased probability of cracking in the heat affected zone of friction stir welds. Examination of a material pairing of steel S235 and the Al alloy Silafont36 by coincident Doppler broadening spectroscopy (CDBS) indicates the formation of annealed steel clusters in the Al alloy component of the sample. The clear visibility of Fe in the CDB spectra is explained by the very efficient trapping at the interface between steel cluster and bulk.     

Vacancy defects induced in the track region of 132 MeV C irradiated SiC

Positron annihilation lifetime spectroscopy (PALS) and electron paramagnetic resonance (EPR) have been used in this work to investigate vacancy defects induced in the track region of 132 MeV ¹²C irradiated silicon carbide. Irradiations have been performed at room temperature at a fluence of 2.5 × 10¹⁴ cm⁻² in N-low doped 6H–SiC and 3C–SiC monocrystals. Silicon monovacancies have been detected in both polytypes using EPR. Their charge state and concentration have been determined in the track and cascade region of the C⁺ ions. PALS measurements performed as a function of temperature have shown the presence of V_Si–C divacancies in the track region for both polytypes.     

聚合物模量与其自由体积的关系研究

选用密度树脂制备高模量基体，采用正电子湮没技术（PLAS），测试了自由体积的尺寸及浓度，研究了基体密度与拉伸模具，压缩模量，自由体积尺寸及浓度之间的关系，结果表明，高密度树脂由于自由体积小，使固化体系具有高模量。     

Irradiation embrittlement monitoring of WWER-440/213 TYPE RPVs

In the paper the main goals and progress of the surveillance specimen programme for the RPVs WWER-440/213 in Jaslovské Bohunice V-2 and Mochovce NPPs are presented. At Jaslovské Bohunice V-2, the standard surveillance specimen programme (SSSP) was finished and so-called ‘Extended Surveillance Specimen Programme’ (ESSP) was prepared on the base of its critical analysis. For first two units of the Mochovce NPP completely new programmes of irradiation embrittlement monitoring called ‘Modern Surveillance Specimen Programme’ is prepared. It is based on the experience with SSSP and ESSP as well as the recommendations of IAEA experts. This programme will serve for Mochovce NPP during all planned service life. The experience of ESSP application on the 3rd and 4th units in Jaslovské Bohunice V-2 NPP are presented in the paper too.     

STUDY OF POSITRON ANNIHILATION ONE DIMENSION ANGULAR-CORRELATION RADIATION ON POLYCRYSTAL Na~+ CONDUCTOR Na_5Y_(1-x)Cr_xSi_4O_(12)

With positron annihilation radiation onedimension angular-correlation device,it ismeasured that positron annihilation radiationone dimension angular-correlation curves ofpolycrystal sodium ion conductor Na_5Y_(1-x)Cr_xSi_4O_(12)(NYCS)system.After electronmomentum distribution curves arenormalized,linear parameters arecalculated.The parameters H,W and Sshow the change of Na~+ ion vacancyconcentration in NYCS series samples.Theresults show that parameters H,W and S ofone dimension angular-correlation curves ofthose samples vary greatly with Cr_2O_3contents.With Cr_2O_3 content increasing,Hand S parameters increase,but W decreases,and reaches extremes at x=0.05;then withCr_20_3 adding continually,parameters H andS decrease gradually,parameter W increasesgradually.This shows that,in addtion toCr_2O_3,the conductivity has close relation