热处理前后丙烯腈／溴乙烯共聚纤维的热性能和阻燃性能研究

分析了热处理前后丙烯腈／溴乙烯共聚纤维的热性能与溴乙烯含量、升温速率或热处理时间的关系，并对纤维的阻燃性与溴含量或热处理时间关系进行了研究。结果表明，溴含量的增加或热处理时间的延长对热稳定性和阻燃性的提高有较大影响，而且经热处理后纤维的阻燃性与溴无关。     

丙烯酸接枝线形低密度聚乙烯的热学行为及结晶形态

利用差示扫描量热仪研究了丙烯酸接枝线形低密度聚乙烯（PE-LLD-g-AA）的热学行为，结果表明，与纯线形低密度聚乙烯（PE—LLD）相比，PE-LLD-g-AA的熔融温度（Tm）略有增加，结晶温度（Tc）增加大约4℃，熔融焓（AHm）随AA含量的增加而降低。还利用差示扫描量热仪研究了PE—LLD和PE—LLD-g—AA的等温结晶动力学，用扫描电子显微镜观察了PE—LLD-g—AA等温结晶形态。结果表明，PE-LLD-g-AA的结晶速率大于纯PE—LLD的，随着接枝率的增加，PE-LLD的球晶半径减小，接枝到PE—LLD分子链上的AA分子起到了成核剂的作用。     

清洁镀铬用紫色硫酸铬

紫色硫酸铬是一种新型清洁镀铬（Cr^3 镀铬）的原料，在镀铬中显示了优良的性能，特别是镀液无需预电解处理亦能得到满意镀层这一实验结论，使清洁镀铬工艺实现工业生产又向前迈进了一步，介绍了它的制法，技术要求，物相分析及使用效果。     

A vapor collection and thermal desorption method to measure semiochemical release rates from controlled release formulations

Chemicals (bp 270–490 °C/1 atm) evaporated from a controlled-release formulation dispenser were carried by an airflow to a collector packed with a polymeric adsorbent. After a set time, the chemicals were recovered by thermally desorbing them onto a gas-liquid chromatograpic column. They were then separated and quantified. The apparatus is described, and the requirements for its successful use are discussed. The soundness of the thermal desorption technique was confirmed by comparison with another technique: solvent elution from the collector. The advantages of the former technique are discussed.Mention of a commercial or proprietary product in this paper does not constitute an endorsement of that product by the USDA.     

Composites based on eucalyptus tar pitch/castor oil polyurethane and short sisal fibers

Polymeric materials are being developed with renewable resources to promote industrial progress with environmentally friendly technologies. For this reason, polyurethane samples were prepared with 4,4′‐diphenylmethane diisocyanate (NCO/OH = 1), eucalyptus tar pitch (biopitch), castor oil as a polyol, and dibutyltin dilaurate as a catalyst. These materials were reinforced with different contents of short sisal fibers (0, 2.5, 5.0, 7.5, and 10.0%) and were prepared by resin‐transfer molding. The composites were characterized by IR absorption spectroscopy, thermal analysis (thermogravimetry and differential scanning calorimetry), impact resistance, scanning electron microscopy, and water absorption resistance. These materials showed hydrophobic characteristics, despite the addition of sisal fibers. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 3797–3802, 2003     

Chemical Reaction Engineering and Research and development of gas solid systems

A general procedure is proposed for innovative research and development of gas-solid reactor systems, with a brief explanation of the significance of each step in the procedureBased upon the contacting mode between gas and solid phases, as well as the ways of supplying thermal energy to the reacting regions, various types of gas-solid reactor systems are classified by using tables of so called “matrix” form, for thermal cracking and gasification of heavy oils, gasification of coal, gasification of solid waste, calcination of limestone, clinkering of cement and reduction of iron ore.The importance of fundamental concepts is emphasized for successful research and development by presenting several examples; namely, calcination of limestone, thermal cracking of heavy oils and gasification of solid waste materials.In connection with the direction in which fundamental research should be oriented, four primary ways of thinking are proposed, which can be applied to obtain innovative ideas for further research and development in this field.One example of the author's practical experience was selected to show the role of the fundamental research in the course of large scale development. Finally the author outlines the role of chemical reaction engineering to innovate the novel gas-solid reactor systems which may be inevitable for simultaneous solution of the three big E's; namely, Energy, Environment and Economy.     

On the thermal stability of xanthan gum

The thermal stability of xanthan gum in dilute aqueous solutions at 90°C is considered. The relative viscosity as a function of ageing time is discussed, and it has been found to depend on the polymer concentration and conformation as well as on the salt content. The effectiveness of a quencher demonstrates the existence of a free-radical process in the degradation. During ageing, the molecular weight first decreases by rapid random hydrolysis of the main chain and loss of the pyruvate and acetate substituents. Later, oligomers are formed corresponding to a breakdown of both the side chain and the main chain. The identification of cellodextrins in the oligomer pool demonstrates the second effect.     

Thermal and crystallization characteristics of poly(ethylene terephthalate) with poly(oxybenzoate‐p‐trimethylene terephthalate) copolymer

Poly(ethylene terephthalate) (PET) was blended with two different poly(oxybenzoate‐p‐trimethylene terephthalate) copolymers, designated T28 and T64, with the level of copolymer varying from 1 to 15 wt %. All samples were prepared by solution blending in a 60/40 (by weight) phenol/tetrachloroethane solvent at 50°C. The crystallization behavior of the samples was studied by DSC. The results indicate that both T28 and T64 accelerated the crystallization rate of PET in a manner similar to that of a nucleating agent. The acceleration of PET crystallization rate was most pronounced in the PET/T64 blends with a maximum level at 5 wt % of T64. The melting temperatures for the blends are comparable to that of pure PET. The observed changes in crystallization behavior are explained by the effect of the physical state of the copolyester during PET crystallization as well as the amount of copolymer in the blends. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 1599–1606, 2002     

Polysulphone and poly(phenylene sulphide) blends: 1. Thermal characterization and phase morphology

The phase behaviour and morphology of injection moulded specimens of polysulphone (PSF) and poly(phenylene sulphide) (PPS) blends were studied by differential scanning calorimetry (d.s.c.), dynamical mechanical thermal analysis (d.m.t.a.) and transmission electron microscopy (TEM). The blends are phase separated regardless of the blend composition as revealed by d.s.c., d.m.t.a. and TEM. Upon annealing at 160°C for 2 h, d.m.t.a. results indicate that the PPS phase remains in the amorphous state at compositions <10%. At compositions between 20 and 35%, the PPS appears to be dispersed in a mixed mode of amorphous and crystalline domains. Above 35% the PPS phase appears to become fully crystallized upon annealing of the blends. At 10% PPS, TEM results showed 35–200 nm size dispersion both in the as-moulded and in the annealed specimens. At 20% the PPS phase varied widely in size, from 35 nm to tens of micrometres but remained as an included phase. TEM also revealed a compound morphology of the included phase at a composition of 50 wt% of each component.