Effect of rolling temperature on microstructure and mechanical properties of 6063 Al alloy

Aluminium alloy (6063) was severely rolled upto 92% thickness reduction at liquid nitrogen temperature and room temperature to study the effect of rolling temperature on its mechanical properties and microstructural characteristics by using tensile tests and SEM/electron back scattered diffraction (EBSD), transmission electron microscope (TEM), DSC, X-ray diffraction (XRD) as compared to room temperature rolled (RTR) material with the same deformation strain. An improved strength (257 MPa) of cryorolled 6063 Al alloy was observed as compared to the room temperature rolled alloy (232 MPa). The improved strength of cryorolled alloy is due to the accumulation of higher dislocation density than the room temperature rolled material. The tensile properties of cryorolled alloy and the alloy subjected to different annealing treatments were measured. The cryorolled alloy subjected to annealing treatment at 300 °C for 5 min exhibits an ultrafine-grained (UFG) microstructure with improved tensile strength and ductility.     

唐河水电站堆石坝基础处理与堆石料填筑施工

唐河水电站的坝型是混凝土面板堆石坝，坝高26．9m，坝顶长度280．5m。文中叙述了坝基处理、坝体碾压试验及筑坝的方法。     

镍-钛爆炸复合板的轧制

本文叙述了镍-钛爆炸复合板热轧和冷轧的工艺、组织和性能。     

轧钢燃油加热炉燃烧技术的探讨与实践

以提高轧钢加热炉燃油燃烧技术为题，详细地阐述了提高重油燃烧前的质量与温度，改进与完善供油设备和燃烧设施在节能中的作用，着重介绍了新型重油加热系统在轧钢炉上的应用与效果。     

变质处理高碳高速钢导板的研究

导板是线材轧机的关键备件，要求有优良的耐磨性，抗断裂性，抗粘钢性和热冲击抗力，常用高镍镍钢导板和高铬铸铁导板满足不了上述要求，使用寿命短，更换频繁，降低了轧机作业率，增大了工人劳动强度，高速钢具有硬度高，红硬性好和耐磨性好等特点，但铸造高速钢脆性大，通过调整高速钢成分和采用RE－Mg-Ti复合变质处理，可改变共晶碳化物的形态和分布，使高速钢冲击韧性大幅度提高，变质处理高速钢导板使用中不粘钢，不断裂，耐磨性明显优于普通导板。     

基于改进谐波小波包分解的滚动轴承复合故障特征分离方法

为解决滚动轴承单通道振动信号中复合故障特征难以分离的问题,提出了基于改进谐波小波包分解的轴承复合故障特征分离方法。首先,改进了二进谐波小波包分解方法,提出了连续谐波小波包分解方法,克服了信号分解后子带个数和带宽范围受二进制划分的缺陷;然后,采用谐波窗分解提取信号中频率成分集中的频段,根据轴承各单点故障特征频率确定分解层数,进行连续谐波小波包分解,利用能量算子包络解调得到子带信号中各个单点故障的权重因子;最后,重构轴承各单点故障信号,实现复合故障的特征分离和提取。对仿真信号和实测轴承内、外圈复合故障信号分析的结果表明,该方法能将轴承单通道复合故障信号分解到不同的通道中,实现了复合故障特征的分离,具有一定的工程实用价值。     

Interfacial Microstructure and Mechanical Properties of Al5052/Mg-9.5Li-2Al Alloy Clad Plates

通过冷轧制备出了Al5052/Mg-9.5Li-2Al合金复合板,研究了复合板退火后的组织与力学性能。结果表明:退火后复合板的结合界面上没有出现类似裂纹或孔洞的缺陷。经623或623 K以上的温度退火后,合金复合的界面形成反应相。Mg-9.5Li-2Al板和Al5052板之间结合界面处的主要反应相依次为α-Mg+β-Li相、Mg17Al12相、Li-dissolved Al3Mg2相和α-Al。在一定温度范围内,随退火温度的升高,界面结合强度逐渐增加。当退火温度为623 K时,复合板的结合强度达到最大值17.83 MPa,而且具有良好的塑性,延伸率达到18.7%,另外,界面未出现剥离现象。当退火温度为673 K时,覆板的拉伸性能由于界面剥离而恶化。     

6061-T6铝合金纵-扭复合振动超声深滚加工试验研究

基于纵-扭复合振动超声加工和超声深滚加工提出了纵-扭复合振动超声深滚加工工艺。采用普通深滚与纵-扭复合振动超声深滚2种加工方法对供应态6061-T6铝合金轴件进行表面强化处理,研究深滚工艺参数对加工表面质量的影响。结果表明:引入纵-扭复合振动后,超声深滚工艺参数对表面质量的影响规律与普通深滚不同,且在相同的工艺参数下,超声深滚所获得的表面粗糙度Ra值要小于普通深滚,最高降低约50%,而表面显微硬度和硬化率则有大幅提高,硬化率最高约为普通深滚的3倍,经纵-扭复合振动超声深滚处理后的表面更光滑,从而证明了纵-扭复合振动超声深滚加工工艺能更有效地实现6061-T6铝合金的强化处理。     

Study on Deformation Structure and Texture of Pure Zirconium with Large Grain Size Rolled at Liquid Nitrogen Temperature

主要研究大晶粒退火态纯锆在液氮温度下均匀轧制时的形变组织特征及孪生机制。利用光学显微镜、扫描电镜、电子背散射衍衬（EBSD）、X射线衍射等对不同变形量样品的变形组织和织构进行了研究,重点结合软件对EBSD结果进行组织重构和机理分析。结果表明,液氮温度轧制时大晶粒纯锆中产生的孪晶类型为C1{112}<11>、T1{102}<10>和T2{111}<11>孪晶,其中C1{112}<11>孪晶最容易产生且为主要孪生类型。变形开始时,3种孪晶的数量迅速增多,而小角度晶界含量较少;变形量增大到30%时,小角度晶界含量占优势。变形初始阶段孪生优先于滑移进行, 且孪生变形是最主要的变形方式,当变形量为30%时,孪晶协调的位错滑移成为主要的变形方式。变形过程中织构类型未发生变化,保持基面双峰织构（偏离ND方向±30°左右）,但强度随着变形量的增大呈减小趋势     

堆焊层预压力滚压表面纳米化层的微观结构

利用场发射扫描电镜、高分辨透射电镜和表面三维形貌仪对经预压力滚压表面纳米化处理的堆焊层的表面微观结构进行研究。结果表明,用中锰焊丝在Cr-Ni合金钢表面制备堆焊层,经滚压加工后,零件表面粗糙度明显降低,零件表面层形成厚度约10μm的明显塑性变形层;在最表层形成了平均晶粒尺寸约10 nm的具有随机取向的等轴晶,纳米晶粒的尺寸随距表面距离增加而增大;在距表面为10~15μm处,存在平均晶粒尺寸约100 nm的等轴晶和具有相近尺寸的胞状结构。预压力滚压加工在提高表面光洁度同时,能够有效地将堆焊层的树枝状晶细化为纳米晶。