高铬铸铁筛板研究

对高铬铸铁合金化和热处理工艺的研究结果表明，选用Ｃｒ／Ｃ比为７左右的Ｃｒ２０型高铬铸铁，在添加适量的Ｍｏ、Ｃｕ、Ｍｎ，并经合适的热处理后，可获得在马氏体基体上分布着较为均匀的Ｍ７Ｃ３型碳化物，使材料达到良好的强韧性配合，耐磨性明显提高，使用寿命明显高于原用筛板，达到与进口筛板相当的寿命，具有明显的经济效益。     

Influence of Tempering Temperature on Cyclic Viscoplastic Behaviour of 55NiCrMoV7 Steel

Low cycle fatigue behaviour of a steel 55NiCrMoV7 under tour tempered conditions is reported. One special type of total swain controlled isothermal cyclic deformation tests were performed in the temperature range 20℃ to 600℃ for the steel tempered 2h at 350℃, 460℃, 560℃ and 600℃. The influence of temperature on cyclic behaviour was investigated. Generally, the cyclic stress response shows an initial exponential softening for the first few cycles, followed by a gradual softening without cyclic softening saturatioo. At 10^-2 strain rate, σmax.Δσ／2 decrease with the test tumperature for all hardness levels. They decrease linearly with tempering temperature when testing temperature is lower than that of tempering, but rest nearly constant when test temperature is equal to or exceed tempering temperature of steel. Cyclic softening intensity increases with testing temperature from 300℃ to 600℃, but the maximal softening intensity occurs at room tumpemture. The strain rate influences notably the cyclic behavioor when T≥50℃, The time dependence of cyclic behaviour is closely related to test temperature and the tempering history of the steel.     

螺杆钻具中定子和转子的中频感应热处理生产线

介绍了石油、天然气钻井用螺杆钻具中的定子、转子和类似工件的中频感应调质热处理生产线的工艺要求、设计思路和生产线结构。与传统的调质工艺相比，采用感应调质生产线提高了工件的综合力学性能，减少了热处理畸变，提高了经济效益。     

铌和热处理对高铬铸铁组织性能的影响

在无钼高铬铸铁中加入适量铌和锰,研究了热处理工艺对其组织和性能的影响。结果表明:加铌并配合高温淬火-亚临界回火工艺,可改善共晶碳化物的形态和分布,并产生明显的二次硬化。试验合金的宏观硬度与Cr15Mo1Cu1高铬铸铁相当,而抗磨性优于后者。     

回火温度对Cr-Mo-V系高强度钢力学性能的影响

回火温度对Cr-Mo-V系高强度钢力学性能的影响并非单调变化，在低于500℃时，随着回火温度的升高，实验钢的硬度，强度和应变硬化指数降低，塑性和韧性提高，在500-630℃的温度范围内，由于二次硬化效应，实验钢的硬度，强度和韧性变化不大，对单轴拉伸实验过程的能量分析表明，在450℃附近回火时有一能量低谷，而在585℃附近回火时有一能量高峰。在单轴拉伸状态下，断裂受裂纹扩展控制。     

Experimental Study of Microstructure Evolution during Tempering of Quenched Steel and Its Application

LARGE-SIZED FORGINGS are usually intensivelyquenched to obtain the desired microstructuredistribution,high strength and hardness.Becauseresidual stresses are high in quenched large-sizedforgings,tempering processes follow quenchingprocesses to reduce the residual stress and obtain goodmechanical properties.Several differentmicrostructures are generated in quenched steelforgings,such as martensite,bainite and retainedaustenite.Modeling of microstructure evolution inquenched steel during …     

DA471球铁凸轮轴热处理工艺研究

采用覆砂铁型生产了DA471型QT700—2球铁凸轮轴，其铸态显微组织由50％～85％的珠光体和球状石墨组成，球化率大于85％。论述了正火（雾冷和强风冷却）和回火温度对凸轮轴中显微组织和力学性能的影响。结果表明，正火加回火后凸轮轴的珠光体含量大于95％，抗拉强度和伸长率分别大于700MPa和3％。该凸轮轴已经大量使用。     

1200铝合金熔铸工艺研究

从熔铸方面总结了1200铝合金的一些特性，论证了该合金作为空调箔用料优于1100铝合金的一些方面。并从细化晶粒方式着手，讨论了不同细化剂对1200铝合金组织、性能等方面的影响。     

回火工艺对新型贝氏体铸钢组织和性能的影响

研究了回火工艺对新型贝氏体铸钢组织和性能的影响。结果表明,ZG30CrMn2Si2Mo正火低温回火后的组织是由贝氏体铁素体和残余奥氏体组成的新型贝氏体组织,随回火温度的升高和保温时间的延长,组织由新型贝氏体组织逐渐转变为典型贝氏体组织;250℃×1h回火后,材料具有较好的强韧性配合,在450￣550℃回火出现回火脆性,其原因与回火过程中残余奥氏体和贝氏体铁素体的分解、碳化物析出有关。     

多元合金铁基堆焊层的回火稳定性

对多元合金铁基堆焊层的焊态试样进行不同条件下的回火后处理，研究了该堆焊层的回火稳定性。结果表明，多元合金铁基堆焊层经560℃保温4h回火后，堆焊层硬度达HRC57；经700℃←→17℃急冷急热重复循环150次后，堆焊层硬度达HRC43，具有较高的回火稳定性及“二次硬化”现象。